Cathodic protection (CP) is a common method for rehabilitation of reinforced concrete structures suffering from Chloride induced corrosion. A sufficient protection of the corroding rebar can be ensured by use of several protection criteria. The use of these assessment criteria, in particular the so called 100 mV-criterion, can lead to erroneous resuits for certain unconventional arrangements of rebar and cp anode.
Therefore a joint research project of the Institute for Building Materials Research, RWTH-Aachen University, Germany, (ibac) and the Federal Institute for Materials Research and Testing, Berlin, Germany, (BAM) has been set up to determine the applicability of CP under arbitrary geometrical conditions. A special focus was set on the applicability of surface applied anode Systems for protection of the reinforcement of structures opposite to the accessible side (e.g. outer side of tunnel Shell, Bridge deck protected from inside a box girder) In this paper, the impact of the time dependent changes of the Polarisation behaviour of the rebar on the current and potential distribution is shown by means of parametric studies using the FEM method.
Corrosion of steel reinforcement in concrete exposed to chloride containing
environments is a serious problem in civil engineering practice. Electrochemical
methods, e.g. potential mapping, provide information whether the steel reinforcement
is still passive or depassivation has been initiated. By applying such techniques no
information on the type of corrosion, its extent and distribution of corrosion products
is available. Particular the corrosion progress is a significant problem. Especially in
the case of element corrosion in reinforced concrete structures, the development at
the anode can not be separated into corrosion damage causing by element corrosion
or self-corrosion. Until now also in laboratory tests it is impossible to collect such
information without destroying specimens after electrochemical testing was
performed place. To overcome this problem it was tried to study the steel surface
within the mortar specimens by X-ray tomography (CT). Within the scope of these
investigations it could be shown, that X-ray tomography is suitable to make corrosion
pits visible which are embedded in a mortar with a cover thickness of about 35 mm.
In this publication the corrosion damage of reinforced steel is documented timedependent
by X-ray tomography.