The motivation of this work is to produce thin films perovskite solar cells with constant high light conversion efficiency over time. Loss of efficiency may be caused by structural and/or chemical alterations of the complex layered system. As these changes might take place either in the bulk and/or on the surface of the stratified material, analytical tools addressing both key issues are selected and combined. SEM/EDS combined with XPS were chosen as appropriate methodical approach to characterise perovskite laboratory cells in depth and complementary on top, before and after light exposure. The layered perovskite system investigated here is based on glass covered with fluorine doped tin oxide (FTO), followed by three porous thin films of TiO2, ZrO2 and a thick monolithic carbon. The TiO2 film is subdivided into a dense layer covered by a porous one constituted of nanoparticles with a truncated bipyramidal shape. This layered system serves as the matrix for the perovskite. After infiltration of perovskite solution and annealing, EDS
spectral maps on cross-sections of the specimen have been measured. The distribution of relevant
elements – Si, Sn, Ti, Zr and C – correlates conclusively with layers visible in the acquired SEM images. Lead and iodine are distributed throughout the porous layers C, ZrO2 and TiO2. Specimens were exposed to ambient daylight for 7 weeks. In a SEM micrograph taken of the cross-section of a sample after illumination, the glass substrate and all layers FTO, TiO2, ZrO2 as well as C are clearly identified. EDS data have been acquired under the same measurement conditions as before the illumination. It was found that several weeks of ambient daylight did not change significantly the qualitative elemental composition of lead and iodine throughout the solar cell system. It was confirmed with EDS that nanoparticles identified in high-resolution SEM micrographs contain mainly Pb and I, indicating these to be the perovskite
crystals. However, a time-dependent compositional and chemical altering was observed with XPS for the near-surface region of the outermost ~10 nm after 2 months of illumination.
Manufacturing of new perovskite layered solar cells with constant high light conversion efficiency over time may be hampered by the loss of efficiency caused by structural and/or chemical alterations of the complex layered system. SEM/EDX combined with XPS were chosen as an appropriate methodical approach to characterize perovskite laboratory cells in depth and at surface, before and after light exposure. The layered perovskite system investigated here is based on glass covered with fluorine doped tin oxide (FTO), followed by thin films of TiO2, ZrO2 and a thick monolithic carbon. TiO2 film is subdivided into a dense layer covered by porous one constituted of nanoparticles (NPs) of truncated bipyramidal shape. This layered system serves as the matrix for the perovskite. EDX spectral maps on cross-sections of specimen have shown that Pb and I are distributed homogeneously throughout the porous layers C, ZrO2 and TiO2. SEM/EDX data show that 20 weeks of ambient daylight did not change significantly the indepth distribution of the elemental composition of Pb and I throughout the entire solar cell system. It was confirmed with EDX that NPs identified in high-resolution SEM micrographs contain mainly Pb and I, indicating these to be the perovskite crystals. However, a compositional and chemical altering began in the near-surface region of the outermost ~10 nm after 2 months of illumination which was observed with XPS.
Self-assembly of TiO2 nanoparticles in multiple layers by layer-by-layer deposition has been selected of different deposition procedures usually applied for fabrication of TiO2 thin films with defined and homogeneous thickness on supports of interest for the large-scale applications. The substrates tested were: conductive (FTO) glass, silica glass and titanium alloy. The selected film fabrication technique consists of the deposition of alternating layers of oppositely charged, i.e. functionalized, TiO2 nanoparticle layers with wash steps in between. The controlled assembly of TiO2 nanoparticles on the supports surface requires both a proper functionalization of the supports to promote the adhesion of the TiO2 film to the substrates and proper functionalization of TiO2 nanoparticles to allow attachment to substrate and subsequent reaction between different NP layers. The current study focusses on the analytical control of the functionalization of the substrates with 3-Aminopropyltriethoxysilane (APTS) and glutaraldehyde (GA) by means of surface sensitive methods, XPS, Auger Electron Spectroscopy (AES) and ToF-SIMS. Chemical composition of surface of functionalized substrates shows differences in the degree and type of modification in dependence on substrate.