Mixtures of hexamethyldisiloxane (HMDSO) and oxygen have been used for deposition of SiO2-like layers by plasma polymerization under low-pressure conditions onto polyethylene and polystyrene used as basecoat. Water glass was cast onto these 0.5 µm plasma thick siloxane-like layers with a thickness of 5 to 40 µm. The adhesion of these bilayer systems and their flame resistance were tested.
The effect of different plasma parameters such as monomer/gas ratio, pressure and power input into the discharge on the deposition rate and the composition of the formed layers was studied. Characterization and chemical composition of the formed films were performed using infrared, X-ray photoelectron and solid state nuclear magnetic resonance spectroscopy.
Peel strengths of composites were measured and the locus of peel front propagation was detected. Thermal properties of composites were analyzed by thermo-gravimetric analysis. Finally, the fire-retardant properties of thick coated polymers were determined by exposure to flames and the behavior of coatings on the polymers during flaming was observed visually.
1Brominated carbon nanotubes as effective catalysts for petroleum hydrocarbons aerobic oxidation
(2012)
Brominated single-walled carbon nanotubes [(Br)n-SWCNT) produced by the plasma-chemical technique were involved in the liquid-phase process of hydrocarbons aerobic oxidation. The significant catalytic effect of the (Br)n-SWCNT was revealed at first by the cumene initiated model oxidation and then in experiments on profound aerobic oxidation of petroleum naphthenic fraction derived from the commercial Azerbaijan (Baku) oils blend diesel cut. The ability of (Br)n-SWCNT to accelerate the aerobic oxidation of the hydrocarbons was found out for the first time. Obviously this phenomenon originates from the peculiarities of electronic configuration of the (Br)n-CNT patterns. The plausible mechanism of (Br)n-SWCNT catalytic action is inclined to the formation of reactive oxygen species. The catalytic activity of (Br)n-SWCNT markedly exceeds the activity of the industrial catalysts, manganese salt of indigenous petroleum acids, used for the liquid phase petroleum hydrocarbons oxidation process.
Die hochselektive und ausbeutereiche plasmachemische Bromierung von Polyolefinoberflächen wurde auf graphitische Materialien übertragen. Oberflächen von graphenartigem Highly Oriented Pyrolytic Graphite (HOPG), natürlichem Graphit, mehrwandige Kohlenstoffnanoröhren (MWCNT) sowie Kohlenstoff-Fasern wurden im Bromdampfplasma behandelt. Während die Bromierung von Polyolefinoberflächen als radikalische Wasserstoffabstraktion mit nachfolgender Addition (Rekombination) oder durch nucleophile Substitution an sp³-hybridisierten C-Atomen abläuft, können graphitische Strukturen sowohl an sp³-hybridisierten Strukturdefekten als auch durch elektrophile Addition an vollständig C-substituierte aromatische Doppelbindungen bromiert werden. Dabei werden die planaren (graphitischen) sp²-C-Atome in die tetraedrische sp³-Hybridisierung umgewandelt und zu elektrisch nichtleitenden Strukturen gefaltet.
Die maximalen Bromausbeuten bei Verwendung von Brom als Plasmamedium lagen je nach Substrat zwischen 1050% Br/C, mit Bromoform deutlich darüber, was durch Kombinationen von Bromoform mit Brom oder Allylbromid mit Bromoform durch Schichtbildung auf über 70% Br/C gesteigert werden konnte.
An die C-Br-Gruppen wurden nasschemisch verschiedene Amine nucleophil gepfropft. Die Pfropfausbeuten von 110 Moleküle je 100 C lagen deutlich niedriger als die erreichten Pfropfgrade von etwa 122 Moleküle je 100 C-Atome an Polyolefinoberflächen. Da nach der chemischen Pfropfung nahezu alle nichtgepfropften Br-Gruppen verschwunden waren, muss auf eine bevorzugte Rekonstruktion der planaren sp²-Graphitschicht geschlossen werden.
In contrast to other plasma modification processes of polymer surfaces, the bromination is very selective and shows a high yield in C—Br groups. The most convenient bromination process was found using bromoform, which was thus preferred to elemental bromine, allyl bromide, vinyl bromide or tert-butylbromide. The bromoform process give yields in C—Br up to 40 C—Br or more, with only 2-3% co-introduction of O-functionalities whereas allyl bromide results in yields of about 20 C—Br and more, but in more than 10% oxygen-containing by-products. C—Br groups serve as anchoring points for grafting of molecules, oligomers and pre-polymers of diole or diamine character.
The initial attachment and subsequent biofilm formation of electroactive bac-teriaShewanella putrefaciensCN32 was investigated to clarify the influence oforganic conditioning layers. A selection of macromolecules and self-assembledmonolayers (SAMs) of different chain lengths and functional groups were pre-pared and characterized by means of infrared spectroscopy in terms of theirchemistry. Surface energy and Zeta (ζ-) potential of the conditioning layers wasdetermined with contact angle and streaming current measurements. Amongthe studied surface parameters, a high polar component and a high ratio ofpolar-to-disperse components of the surface energy has emerged as a successfulindicator for the inhibition of the initial settlement ofS. putrefacienson stainlesssteel AISI 304 surfaces. Considering the negative surface charge of planktonicS. putrefacienscells, and the strong inhibition of cell attachment by positivelycharged polyethylenimine (PEI) conditioning layers, our results indicate thatelectrostatic interactions do play a subordinate role in controlling the attach-ment of this microorganism on stainless steel AISI 304 surfaces. For the biofilmformation, the organization of the SAMs affected the local distribution of thebiofilms. The formation of three-dimensional and patchy biofilm networks waspromoted with increasing disorder of the SAMs.
Multiple-sample approach: reliable ranking and validated statistics of bonding and adhesive strength
(2014)
Bonding strength of adhesive-bonded joints and adhesive strength of coatings have been exclusively determined in
single-sample tests using a tensile testing machine. Necessarily, the single-sample approach was also applied to the
corresponding bonding procedure. As a consequence, reliability and reproducibility of results were restricted. By
applying the newly introduced centrifuge technology, the multiple-sample approach was realized for simultaneous
tensile testing of up to eight samples under identical conditions without any disturbing shear-force effects. In order to
introduce the multiple-sample approach into the bonding procedure, a hydraulic bonding set-up was developed which
enables identical bonding pressure also for slightly different heights of sample assemblies. Both sample approaches
were compared for various application examples: ranking of different classes of adhesives, validated statistics of
adhesive-bonded joints using one particular adhesive and effects of cleaning and plasma-treatment on the adhesive
strength of coatings. The investigated systems included glass, metals and polymer substrates, different adhesives,
metallic and dielectric coatings on polymers.
Plasma-chemical bromination applied to graphitic materials, in particular to highly ordered pyrolytic graphite is reviewed. The resulting bromination efficiency of the plasma-chemical treatment was subject of systematic process optimization. The plasma of elemental bromine vapour produced bromine concentrations on graphene surfaces of more than 30 % Br/C using either inductively or capacitively coupled low-pressure radio-frequency plasmas. Plasma brominated graphite surfaces have been studied by Near Edge X-ray Absorption Fine Structure, X-ray Photoelectron Spectroscopy, Atomic Force Microscopy and Scanning Electron Microscopy. The introduction of bromine into graphene-like graphite layers and its binding situation were investigated. To study the physical effect of the plasma bromination process, Kr plasma was also used because of its chemical inertness but similar atomic mass. Covering the samples with a Faraday cage or with a LiF window should help to differentiate between physical, chemical and radiation effects of the plasma. Bromination was assigned to radical or electrophilic addition of bromine onto fully substituted aromatic double bonds (sp² C) with exothermal reaction enthalpy. Low bromination shows a strong decay of aromatic double bonds, higher bromination percentage let disappear all aromatic rings. The formed C–Br bonds were well suited for efficient grafting of organic molecules by post-plasma wet-chemical nucleophilic substitution. This grafting onto the graphene surface was demonstrated using aminosilane and different diamines. The bromination of double bonds changes the hybridization of carbon atoms from plane sp² to tetrahedral sp³ hybridization. Thus, the plane topography of graphene is destroyed and the conductivity is lost.
Since more than 40 years ammonia plasma exposure of polyolefins is used for introduction of primary amino groups. The selectivity of this reaction and the yield in primary amino groups was found to be low. Here, a prominent side-reactions of this process was investigated, the hydrogenation by NH3 plasma. For identification of hydrogenation ammonia (NH3) and deuterated ammonia (ND3) were exposed to Polyethylene (h-PE) and fully deuterated polyethylene (d-PE) as well as hexatriacontane (h-HTC) and fully deuterated hexatriacontane (d-HTC) as low-molecular weight model for PE. HD exchange was assumed and detected by Time-of-Flight Secondary Ion Mass Spectrometry (ToFSIMS), X-ray Photoelectron Spectroscopy (XPS), Attenuated Total Reflectance (ATR-FTIR) and 1H and 2H Nuclear magnetic Resonance. Results show a significant HD exchange within the sampling depth of ATR (2.5 µm). However, N- and NH2 introduction was limited to the topmost surface as shown by SIMS and XPS (a few nanometers).
Thin coatings of poly(acrylic acid) (PAA) and poly(hydroxyethylmethacrylate) (PHEMA) were deposited onto carbon fibers by means of the electrospray ionization (ESI) technique in ambient air. These high-molecular weight polymer layers were used as adhesion promoters in carbon fiberepoxy resin composites. Within the ESI process, the carbon fibers were completely enwrapped with polymer in the upper 10 plies of a carbon fiber roving. As identified with scanning electron microscopy also shadowed fibers in a bundle as well as backsides of fiber rovings were pinhole-free coated with polymers (electrophoretic effect'). Under the conditions used, the layers have a granular structure. Residual solvent was absent in the deposit. PAA and PHEMA films did not show any changes in composition and structure in comparison with the original polymers as analyzed by X-ray photo-electron spectroscopy and matrix-assisted laser desorption/ionization time-of-flight mass spectrometry. Single-fiber pullout tests of coated fibers embedded in epoxy resin showed significantly increased interfacial shear strength. It is assumed that chemical bonds between carbon fiber poly(acrylic acid) and epoxy resin contribute significantly to the improved interactions.