An unusual feature known as the negative difference effect (NDE) can be observed in magnesium when recording corrosion current density–potential curves. More hydrogen is evolved at a more positive potential which does not occur in conventional metals. Several models have been proposed in the literature in order to explain the phenomenon of NDE. They succeed in explaining some effects, and fail to deal with others. A new model, which explains the NDE by two electron consuming processes, is presented in this paper. By potentiostatic investigations of magnesium in a chloride electrolyte, measurements of hydrogen evolution and chemical analysis of the electrolyte the new model was experimentally verified.
An important possibility to improve the corrosion behaviour of magnesium alloys is the application of protective coatings. The quality of such coatings depends mainly on the pretreatment and the exposure conditions after pretreatment. Since magnesium surfaces change much faster under atmospheric conditions than those of almost any other technical material, it is necessary to pay special attention to this particular feature. The activity of acid-pickled surfaces of the magnesium alloys AZ31 and AZ91 in dependence on the exposure time and the humidity conditions was investigated with electrochemical noise (EN) measurements. In addition to pickling, plasma chemical vapour deposition processes open new possibilities for an economical, as well as ecologically quite safe, pretreatment. The results of EN investigations after acid pickling as well as specific plasma oxidation treatments of the two magnesium alloys after exposure to air with different humidities are presented.
Development of anti-corrosive pigments for diverse coating systems is both time-consuming and costly, due to the necessary climatic testing, such as testing under salt spray exposure. To accelerate work on a new zinc-free pígment with improved protection, modern, electrochemical investigation methods have been used successfully and verified using traditional tests.
The development of anti-corrosive pigments for the most diverse coating Systems is extremely time consuming and expensive, owing to the necessary climatic testing, such as testing under salt spray exposure. To accelerate work on a new zinc-free pigment with improved protection, modern, electrochemical investigation methods have been used successfully and verified using traditional tests.
As bio-absorbable implant material the magnesium alloy Mg-1Ca is able to degrade in-vivo. The mechanical properties of this alloy are similar to those of human bone; both Mg and Ca are essential elements in human body. The main problem is the high corrosion rate of this alloy. Two coating systems based on plasma-chemical oxidation and an organic dip coating are applied onto MgCa1.0 magnesium alloy in order to slow down the corrosion rate. The corrosion behaviour of the coated alloys was investigated with electrochemical noise measurements. The influence of hydrogen evolution and increasing pH-value on the cytotoxicity was examined. The results of these investigations suggest that a combination of both coating systems leads to promising degradation properties.
The degradation behaviour of an Mg-1Ca alloy is investigated in vitro to figure out the possibilities of influencing the degradation behaviour of such an alloy by applying heat treatment as well as the use of a coating system based on plasma-chemical oxidation. It is shown that an optimised solution annealing (T4-heat treatment) can reduce the degradation rate while an additional ageing between 240 and 300 °C (T6-heat treatment) increases it. A coating generated by plasma-chemical oxidation reduces the degradation rate in the immersion test. Its effect is depending on the former heat treatment of the Mg-1Ca alloy as well as on the parameter during plasma-chemical oxidation.