While the possibilities of improving corrosion resistance (especially galvanic corrosion) by alloying are limited, surface finishing of magnesium alloys is the alternative for improving corrosion resistance. Due to the low corrosion potential of Mg and the danger of galvanic corrosion in the case of a coating defect, the choice of coatings is limited. This chapter will summarize the corrosion behavior of magnesium alloys and the metallurgical possibilities to improve the corrosion resistance of the alloys and reviewing critically the most commonly used surface treatments and coatings for magnesium.
An important possibility to improve the corrosion behaviour of magnesium alloys is the application of protective coatings. The quality of such coatings depends mainly on the pretreatment and the exposure conditions after pretreatment. Since magnesium surfaces change much faster under atmospheric conditions than those of almost any other technical material, it is necessary to pay special attention to this particular feature. The activity of acid-pickled surfaces of the magnesium alloys AZ31 and AZ91 in dependence on the exposure time and the humidity conditions was investigated with electrochemical noise (EN) measurements. In addition to pickling, plasma chemical vapour deposition processes open new possibilities for an economical, as well as ecologically quite safe, pretreatment. The results of EN investigations after acid pickling as well as specific plasma oxidation treatments of the two magnesium alloys after exposure to air with different humidities are presented.
Development of anti-corrosive pigments for diverse coating systems is both time-consuming and costly, due to the necessary climatic testing, such as testing under salt spray exposure. To accelerate work on a new zinc-free pígment with improved protection, modern, electrochemical investigation methods have been used successfully and verified using traditional tests.
The development of anti-corrosive pigments for the most diverse coating Systems is extremely time consuming and expensive, owing to the necessary climatic testing, such as testing under salt spray exposure. To accelerate work on a new zinc-free pigment with improved protection, modern, electrochemical investigation methods have been used successfully and verified using traditional tests.
The degradation behaviour of an Mg-1Ca alloy is investigated in vitro to figure out the possibilities of influencing the degradation behaviour of such an alloy by applying heat treatment as well as the use of a coating system based on plasma-chemical oxidation. It is shown that an optimised solution annealing (T4-heat treatment) can reduce the degradation rate while an additional ageing between 240 and 300 °C (T6-heat treatment) increases it. A coating generated by plasma-chemical oxidation reduces the degradation rate in the immersion test. Its effect is depending on the former heat treatment of the Mg-1Ca alloy as well as on the parameter during plasma-chemical oxidation.