The in situ analysis of the damage evolution in a metal Matrix composite (MMC) using synchrotron X-ray refraction radiography (SXRR) is presented. The investigated material is an Al alloy (6061)/10 vol% Al2O3 MMC after T6 heat treatment.
In an interrupted tensile test the gauge section of dog bone-shaped specimens is imaged in different states of tensile loading. On the basis of the SXRR images, the relative change of the specific surface (proportional to the amount of damage) in the course of tensile loading was analyzed. It could be shown that the damage can be detected by SXRR already at a stage of tensile loading, in which no Observation of damage is possible with radiographic absorption-based imaging methods.
Moreover, the quantitative analysis of the SXRR images reveals that the amount of damage increases homogeneously by an average of 25% with respect to the Initial state. To corroborate the experimental findings, the damage distribution was imaged in 3D after the final tensile loading by synchrotron X-ray refraction computed tomography (SXRCT) and absorption-based synchrotron X-ray computed tomography (SXCT). It could be evidenced that defects and damages cause pronounced indications in the SXRCT images.
In various kinds of radiography, deficient transmission imaging may occur due to backlighting inside the detector itself arising from light or radiation scattering. The related intensity mismatches barely disturb the high resolution contrast, but its long range nature results in reduced attenuation levels which are often disregarded. Based on X-ray observations and an empirical formalism, a procedure is developed for a first order correction of detector backlighting. A backlighting factor is modeled as a function of the relative detector coverage by the sample projection. Different cases of sample transmission are regarded at different backlight factors and detector coverage. The additional intensity of backlighting may strongly affect the values of materials’ attenuation up to a few 10%. The presented scenario provides a comfortable procedure for corrections of X-ray or neutron transmission imaging data.
While X-ray based darkfield imaging with grating interferometers is already widely used, darkfield imaging with neutrons has still a relatively small user community focused mostly on magnetic materials. Here, we demonstrate the application of neutron darkfield imaging byTalbot-Lau type grating interferometry to fiber reinforced plastics. Common carbon and glass fiber composites have been investigated including characteristic damage structures. The darkfield images show a strong signal response caused by fiber delamination, suitable fiber direction, particles, pores and cracks. The basic principles of neutron darkfield imaging applied to fiber composites are highlighted.