Within the presented research project, experimental and numerical investigations were performed to develop a thin-shelled, modular, mobile element system made of a micro-reinforced ultra-high-performance ductile concrete (DUCON®). Material parameters were experimentally determined to adapt the material model within the numerical analysis applying the Drucker-Prager relationship. Afterwards, for validation of the numerical models, quasi-static and high-velocity impact tests were performed on plate-like structures. Finally, a suitable geometry of transportable barrier elements will be designed, which provides a maximum of resistance against impact by a minimum of weight and a maximum of mobility.
The presented development of a damping model is a research component of an experimental feasibility study about moisture in building materials measured with Bluetooth® Low Energy (BLE) signals. This study may be part of a structural health- and long-term monitoring aiming at early damage detection in the built infrastructure and is increasingly focusing on wireless sensor network technology. It is investigated, how the Received Signal Strength Indicator (RSSI) of a BLE signal, transmitted from the BLE-module embedded in building materials with changing moisture content is damped. The aim of the modelling is the derivation of a damping equation for the formal model to determine the moisture damping exponent to finding a correlation.
A new method for periodically monitoring reinforcement corrosion in concrete with Ground-Penetrating Radar (GPR) is proposed and a ten-year long-term corrosion periodic monitoring experiment is reported. GPR historical data was taken in different years, under different conditions. In order to align and normalize the obtained images properly prior to effectively performing any automatic defect detection, image registration techniques based on mutual-information are employed, and a new signal processing scheme is proposed for normalizing the intensity of GPR images. Then, the processed image results can be used to compare and find out the change of GPR detection due to corrosion.
Structural health monitoring contributes to early damage detection in the built infrastructure. During the last two decades, sensor networks transferred from wired to wireless sensor networks. Several methods exist to measure moisture in building materials. Most of the introduced commercial moisture measurement methods provide information about the local or near surface moisture. A feasibility study is presented to demonstrate, how the Received Signal Strength Indicator (RSSI) of a Bluetooth Low Energy (BLE) signal, transmitted from the BLE-module embedded in building materials, correlate with changing moisture content. The feasibility of this influence was investigated in the presented study. The maximum and minimum RSSI were systematically recorded and analysed.
Die Langzeitüberwachung von Bauteilen (Structural Health Monitoring, SHM) ging in den letzten Jahren zunehmend von verkabelten Sensoren zu kabellosen Sensornetzwerken (WSN) über. Frühwarnsysteme sollen rechtzeitige Signale senden, wenn Schädigungsprozesse einsetzen, wenn ein Bauteil z. B. zu feucht wird (Deiche, Staumauern), oder wenn Feuchteprozesse in Bauteilen auftreten, die den Transport von schädlichen Stoffen ermöglichen. Mittels handelsüblicher multifunktionaler Sensoren wie einem Bluetooth Low Energy (BLE) wurden erste Machbarkeitsuntersuchungen zur Massenfeuchtemessung durchgeführt. Die untersuchten Parameter sind der sogenannte Received Signal Strength Indicator (RSSI) eines Bluetooth-Low-Energy(BLE)-Signals und die abgestrahlte Sendeleistung eines eingebetteten BLE-Moduls. Das BLE-Modul kommuniziert mit einem mobilen smarten Empfänger wie einem Tablet oder einem Smartphone als SmartHub. Die Veränderung des RSS-Indikators ist ein Maß für die Veränderung der Feuchte im Bauteil, während die ausgesandte Signalstärke konstant bleibt. Wenn das BLE-Signal einen feuchten Bereich im Baumaterial durchläuft, verändert sich der RSS-Indikator. Nach erfolgreicher Machbarkeitsstudie wurde nun ein aus dem Netzwerk MI4G (Modern Industry for Germany) zwischen der Bundesanstalt für Materialprüfung und dem Klein- und mittelständigen Unternehmen LinTech GmbH heraus beantragtes ZIM-Projekt bewilligt. Der Bericht zeigt erste Ergebnisse von Voruntersuchungen und gibt einen Ausblick auf weitere Forschungsaktivitäten.
Brücken zählen einerseits zu den ältesten Zeugnissen der Verkehrsgeschichte und sind andererseits ein wichtiger Bestandteil der Verkehrsinfrastruktur für unsere heutige Gesellschaft. Sie erfüllen eine wichtige Funktion bei Transport von Personen und Gütern und prägen das Stadtbild. Die Berliner Hoch- und Untergrundbahn, eröffnet im Februar 1902 nach 5 1/2 –jähriger Bauzeit, ist in der heutigen Berliner Denkmalliste als Denkmalbereich (Gesamtanlage) geschützt. Bereits seit 1980 waren die historischen Bahnhöfe entlang der Stammstrecke als Baudenkmale gelistet.
An der Stahlkonstruktion der Hochbahnviadukte zwischen Halleschem Tor und Prinzenstraße wurden während regulärer Inspektionen in den 1990ziger Jahren Risse dokumentiert. Die Berliner Verkehrsbetriebe (BVG) bezogen die Bundesanstalt für Materialforschung und –prüfung (BAM) sowie Ingenieurbüros in eine Diskussion über die optimale Lösung zur Sanie-rung und zum Erhalt der Hochbahnviadukte ein. Zahlreiche Versuche im Labor und Messungen vor Ort dienten der Optimierung der bevorzugten Sanierungsvariante. Die BVG für eine Lösung mit relativ geringem Eingriff in die Konstruktion. Das äußere Erscheinungsbild der Hochbahnviadukte im Berliner Stadtbild konnte durch die Sanierungsvariante der BVG erhalten werden.
In this article, we present a laboratory experiment to monitor the accelerated corrosion in concrete using ground-penetrating radar (GPR). Four concrete test specimens were cast with rebars of different size and placed at different depths. The lifetime decades of reinforcement corrosion process were accelerated into 18 days by using the impress current technique. The electrochemical corrosion process was periodically monitored with GPR. Two control specimens were also prepared to investigate the influence of chloride contamination on GPR signal. The measured data were analysed both in time and frequency domains. In time domain, the peak-to-peak amplitude of a wave reflected by a rebar was calculated to investigate the relationship between an increase in signal amplitude and the degree of corrosion. In frequency domain, the time–frequency representations of the signal were computed by using S-transform. The results show that reinforce corrosion increased the amplitude of reflected signal in time domain but did not change the peak frequency in frequency domain while chloride contamination attenuates the signal to smaller amplitude and lower peak frequency. Based on the results, a novel process is finally proposed for GPR-based corrosion detection.
For almost 15 years, carbon fibre-reinforced polymer (CFRP) plates and sheets have been used for strengthening and repair of civil engineering structures. CFRP plates were applied to upgrade structures for change in use or increasing traffic load. CFRP laminates have also been used to repair deteriorated structures such as multi-storey parking or bridges. The execution quality and condition of the strengthening measure in terms of bond integrity were neither monitored nor tested systematically. Inspectors eventually applied simple hammer knocking during regular main inspection for subjective noise distinction as a measure for eventual insufficient bond. This paper presents the feasibility and the limitations of low-frequency transversal ultrasonic waves with dry-coupling point-contact sensors for inspection and defect detection between CFRP laminate and concrete surfaces. The German Centre of Competence in Civil Engineering (DIBt) has initiated a national research project [Helmerich et al. (2012). Condition analysis of bonded CFRP-applications on concrete structures by means of non-destructive testing [in German: Zustandsuntersuchung von CFK-Klebeverstärkungen an Betonbauteilen mittels zerstörungsfreier Prüfung (ZfP)]. Final, internal project report], carried out at the Federal Institute for Materials Research and Testing (BAM), Germany. The aim of the project was to present a potential non-destructive testing method for bond defect detection as a measure for the durability of the strengthening system more than 10 years after application.
Cracks perpendicular to the surface may be initial indicators for a deterioration process of concrete structures. Moisture penetrates inside the structure and transports adverse chemicals. The paper presents an investigation about the reliability of available commercial non-destructive evaluation techniques to reliably estimate the depth of surface-breaking cracks in reinforced concrete structures. Aim of the study was the investigation of surface-braking cracks under laboratory conditions. Commercial acoustic devices as impact echo equipment, single ultrasonic transducers and arrays were applied even if they have not been developed for this purpose. The commercial software and descriptions for application was followed strictly to compare the function, precision and repeatability of the measurements. Both, perpendicular notches and cracks have been considered. The study was completed with a discussion about reference specimens. The study was the basis for formulation of gaps in research. The Electric Power Research Institute (EPRI) has initiated and funded a Project.
The Berlin Congress Hall was a gift of the United States of America to Germany for the Berlin World Exhibition in 1957. The elegantly double-curved roof was made from an advanced prestressed concrete construction. The construction followed the design by the American architect Hugh Stubbins with special structural modifications to comply with German construction rules. No early indications for failure initiation were detected before a sudden partial collapse. On May 21st, 1980, the Southern external roof overhang collapsed. In December 1980, Jörg Schlaich and his co-authors published a summarizing expert opinion about structural causes of failure. The present paper mainly introduces results of cause analysis made at the Federal Institute for Materials Research and Testing (BAM), mandated by the Public Prosecutor at the Berlin District Court to specify the causes of the sudden failure. This paper refers to BAM-publications about analyses that were performed under this mandate and published – most of them in German language – within the first years after failure. The expert's opinions comprise structural considerations materials investigations, metallographic analyses and corrosion. Nowadays experts have learnt from the failure and built a slightly modified roof in the original shape at the 750th birthday of the city of Berlin and re-opened the former Berlin Congress Hall to the public on May 9th, 1987. The Hall is now serving as the House of the Cultures of the World, following the initial intention of the hall.