Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (32) (entfernen)
Schlagworte
- Durability (4)
- Acoustic emission analysis (3)
- Cracks (3)
- Nano-silica (3)
- Carbonation (2)
- Concrete (2)
- Crack formation (2)
- Digital image correlation (2)
- Grout (2)
- Grouted connection (2)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (16)
- 7.4 Baustofftechnologie (15)
- 7.2 Ingenieurbau (7)
- 7.1 Baustoffe (4)
- 8 Zerstörungsfreie Prüfung (4)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (3)
- 2 Prozess- und Anlagensicherheit (1)
- 2.4 Prüfung und Bewertung von Explosivstoffen/Pyrotechnik (1)
- 2.5 Konformitätsbewertung Explosivstoffe/Pyrotechnik (1)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (1)
Reinforced concrete buildings are frequently damaged by cracks, spalling and corroded
reinforcement bars. The present article focuses on the damage analysis of one of the first
buildings in Berlin that was constructed using reinforced lightweight concrete, which makes it
historically important. The compressive strength, carbonation depth, location and diameter of
reinforcement bars as well as moisture and salt profiles were determined. The carbonationinduced corrosion of the reinforcement bars represented the main damage of the building.
Certified repair mortars with lightweight aggregates (LWA) do not exist on the German
market. Therefore, an appropriate repair mortar was developed in accordance with DIN EN
1504 and the German guideline for the repair and protection of concrete structures (RL-SIB).
On the one hand, historic preservation requirements, such as: colour of the mortar,
possibilities of surface patterning, maximum preservation of the original substance and
reversibility of any Intervention must be met. On the other hand, technical requirements of the
relevant Standards must be achieved. The developed mix was designed to resist the identified
causes of deterioration. Thermal strains within the repair mortar and between the repair
mortar and the Substrate influence the crack formation and thus the durability. Therefore,
special attention was paid to the bonding and shrinking behaviour of the concrete repair
System. By using polymers, both hardened mortar properties and durability were influenced
positively.
The interaction mechanism of ultrasonic waves with surface-breaking cracks in reinforced concrete has been studied. For this, a detailed numerical analysis of the medium was first conducted using the spectral finite element method. Subsequently, measurements were conducted on a reinforced beam sample before and after mechanical-load-induced cracking. It was concluded that for the considered configuration, waves passing through the cracks dominated the tip-diffracted ones. In addition, substantial changes in the travel time and amplitude of the signals were observed when cracks were present.
Der durch Kräfte senkrecht zur Stabachse belastete Balken ist eines der Haupttragelemente des Stahlbetonbaus. Biegebalken finden unter anderem Anwendung in Form von Brückenträgern oder Unterzügen. Die bei maximaler Beanspruchung auftretenden Versagensformen unterteilen sich dabei in Biege- und Querkraftversagen (Schubversagen). Ein Versagen des Balkens kann je nach Versagensmechanismus mit oder ohne Vorankündigung erfolgen. Gebräuchliche Bemessungskonzepte der Baupraxis zur Dimensionierung entsprechender Tragelemente zielen auf ein Versagen mit ausreichender Vorankündigung (große Verformungen oder breite Risse) ab, wie es z.B. beim sekundären Biegedruckversagen entsteht. Für die Zustandsüberwachung von Bauwerken (z.B. Brücken) mittels zerstörungsfreier Prüftechniken sind fundierte Kenntnisse zu den bei Biegebeanspruchung auftretenden Schadensmechanismen erforderlich. Im Rahmen eines BAM-internen Projektes sollen durch praxisnahe Untersuchungen an einer brückenähnlichen Referenzstruktur unterschiedliche auf das Tragwerk einwirkende thermische und mechanische Belastungen untersucht werden und in die Entwicklung eines Monitoringsystems einfließen. Anhand der aus Biegeversuchen vorliegenden Ergebnisse wird der Einsatz unterschiedlicher Methoden der zerstörungsfreien Materialprüfung gezeigt und deren Anwendbarkeit für die Analyse des Verformungsverhaltens von Stahlbetonbalken diskutiert. Hierzu wurde das Verformungsverhalten eines Stahlbetonbalkens (L = 2,75 m) in einem Vierpunkt-Biegeversuch im Labormaßstab untersucht. Das Hauptaugenmerk liegt dabei auf der Charakterisierung der ausschlaggebenden Versagensmodi durch die einzelnen zerstörungsfreien Prüfverfahren und der Vergleich zu klassischen Messmethoden (z.B. Verformungsmessung mittels induktiver Wegaufnehmer (IWA)). Die Biegeversuche wurden dazu durch Schallemissionsanalyse (SEA) und optische Verformungsanalyse mittels Stereo-Fotogrammetrie (SF) und Bildkorrelationsverfahren (BKV) begleitet.
Current trend suggests that global energy consumption will increase in the future. This growing energy demand and advancement of technology lead to explore all potential offshore fossil and non-fossil energy sources, necessitating erection of exploration and production structures, rigs, platforms and towers, which are susceptible to adverse environmental conditions along with their maintenances. Cylindrical grouted joints provide suitable connections between steel substructure and foundation in these offshore platforms and wind structures especially monopiles for ease of installation. However, these are composite connections with exterior sleeve, interior pile and infill grout. The capacity of these connections is affected by number of factors. The literature over last four decades by numerous researchers has shown the development of these connections with increasingly higher capacities and influences on these capacities due to various factors. This paper provides a comprehensive review on the factors affecting the connection capacity along with technical challenges for the future. Critical aspects and shortcomings of the current connection systems and potential solutions may be sought after for these issues are also discussed.
The determination of the blast protection level of civil engineering buildings components
against explosive effects represents a topic of crucial importance, in current practice. However, some key aspects of blast resistant structures design have been only marginally considered in the last decade, and currently still require appropriate regulations. This is especially true in the case of windows and facades, where the intrinsic material brittleness is the major influencing parameter for blast-resistant assemblies. While blast assessment of buildings and systems is usually achieved by means of experimental investigations, as well as numerical simulations, general regulations and guidelines are currently missing.
In this regard, the European Reference Network for Critical Infrastructure Protection (ERNCIP) Thematic Group “Resistance of Structures to Explosion Effects” attempts to develop guidelines and recommendations aimed to harmonise test procedures in experimental testing of glass windows under blast, as well as standardized approaches for their vulnerability assessment via numerical modelling. In this paper, major Thematic Group outcomes and next challenges are briefly summarized.
The tensile behavior of strain-hardening cement-based composites (SHCC) is usually investigated on macroscopic scale by means of direct tension tests or bending tests. Additionally, the micromechanical properties of the composites are often described based on single fiber tension and pull-out tests. Such investigations, performed both on macroscopic and microscopic scales, are based on ‘classical’ force and displacement measuring techniques. Advanced test methods such as digital image correlation (DIC) and acoustic emission analysis (AE) may facilitate the identification and the analysis of the failure mechanisms in SHCC, which is important for both monitoring loaded SHCC elements and further material development and optimization. In this study, these two techniques are combined to characterize the failure mechanisms of three different types of SHCC in direct tension tests. The results are related to data of stress and strain measurements. It is shown that DIC provides detailed spatially resolved and stress related strain measurements. Furthermore, it is demonstrated that AE allows for the localization of active cracks, quantification of the damage accumulation under increasing stresses, and characterization of the dominant crack bridging mechanisms and failure modes observed in the different types of SHCC.
Alkali-activated slag materials are known for their high Chloride penetration resistance. This makes them potentially applicable as repair systems for damaged steel-reinforced concrete structures, which are exposed to chloride attack. For this purpose, the influence of the activator composition, i.e. the SiO2 and Na2O concentration of the alkaline solution on a) the compressive strength, b) shrinkage and mass change and c) the resistance against chloride penetration of four alkali-activated slag mortars (AASM) were studied. An ordinary Portland cement-based mortar was used as the reference sample. Increasing SiO2 and Na2O concentrations increased the strength, shrinkage and mass loss of the AASMs. The resistance of the mortars against chloride penetration was evaluated using the non-steady-state migration coefficient Dnssm obtained from NT BUILD 492. The results indicate that the Dnssm is related to differences in the pore solution of the AASMs rather than to differences in their microstructure. An upcoming study of the authors is going to evaluate this hypothesis by the accelerated chloride penetration (diffusion) test.
Remediation of Cracks Formed in Grouted Connections of Offshore Energy Structures under Static Loads
(2018)
The future energy demand necessitates the exploration of all potential energy sources both onshore and offshore. Global trend has shifted towards offshore energy, which can be obtained from either carbon intensive or renewable options, hence requiring structures such as rigs, platforms, and monopiles. Most of these structures adopt easily installable construction techniques, where lower foundation need to be connected with the super structure by mean of grouted composite joints. Generally, these composite connections have exterior sleeve, interior pile and infill grout. Being located in remote offshore conditions, connections can experience considerable adverse loading during their lifetimes. Degradations were reported inside similar connections, which were installed in last three decades. Besides, grouting in the offshore sites may often be proven difficult, which eventually leads to reduced capacity of connections in the long run. Thus, repair and rehabilitation of such connections should be planned ahead to minimize operational delays and costs in the future. This study aims at characterizing the nature of crack generation in grouted connections and thereby identifying the potential of repair using suitable repair material. Scaled grouted joints were manufactured using a novel mold, and connections were loaded under static load to visualize the main failure pattern. The failure mechanism and loading capacity are found compatible to previous results from earlier literature. Grouted connection was then repaired using cementitious injectable grout. The effectiveness of the repair system is also discussed.
Effects of amorphous nano-silica additions on mechanical and durability performance of SCC mixtures
(2012)
In the recent years the application of nanotechnology in building materials has increased
exponentially. One of the most referred and used nano-materials is amorphous silica with
particles size in the nano-range, even though its application and effect in concrete has not been
fully understood yet. It has been reported that nano-silica (nS) addition increases the
compressive strength and reduces the overall permeability of hardened concrete due to the
pozzolanic properties which are resulting in finer hydrated phases (C-S-H gel) and densified
microstructure (nano-filler and anti leaching effects). These effects enhance the durability of
concrete structures such as bridges, quays or off-shore oil facilities in marine environments.
In this study two different types of nano-silica were applied in self-compacting concrete (SCC),
both having similar particle size distributions (PSD) but produced in two different processes
(fumed powder silica and precipitated silica in colloidal suspension). The influence of nanosilica
on SCC was investigated with respect to the properties of concrete in the fresh state
(workability) and hardened state (mechanical properties and durability). Additionally, the
densification of microstructure of the hardened concrete was verified by SEM and EDS analyses.
The obtained results demonstrate that an efficient use of nano-silica in SCC can improve its
mechanical properties and durability. Considering the reactivity of the two nano-silica studied,
colloidal type shown more reactivity at early age, which influenced all the final SCC properties.
Für die rechnerische Dimensionierung der Betondecken im Oberbau von Verkehrsflächen für den Neubau sowie die Erneuerung nach RDO Beton 09 ist die statische Spaltzugfestigkeit an der unteren bzw. unteren und oberen Scheibe des Betonzylinders bzw. Bohrkerns entsprechend der Vorgaben der AL Sp-Beton zu bestimmen. Aufgrund der unzureichenden Kenntnis der Präzision dieses Prüfverfahrens wurden mit einem breit aufgestellten Ringversuch die statistischen Kennwerte an Labor- und Bestandsbetonen unter Vergleich- und Wiederholbedingungen auf der Grundlage des „Merkblatts über die statistische Auswertung von Prüfergebnissen" ermittelt. Für eine möglichst gute statistische Absicherung nahmen an dem Ringversuch 13 erfahrene Prüfstellen teil. Zur Abdeckung des vielschichtigen Einsatzes des Prüfverfahrens erfolgte der Ringversuch an acht Prüflosen. Dabei berücksichtigen einerseits die Prüf lose 1 und 2 mit den im Transportbetonwerk hergestellten Betonzylindern die Erst-/Eignungsprüfung und das darauf aufbauende Prüflos 3 mit Bohrkernen aus einer im Feldversuch hergestellten Fahrbahnplatte mit gleicher Betonrezeptur die Übereinstimmungskontrolle bei Neubaumaßnahmen. Andererseits findet der Einsatz des Prüfverfahrens bei der Restsubstanzbewertung von Betonfahrbahnplatten bei den Prüflosen 4 bis 7 mit den Bohrkernen aus vier in Waschbetonbauweise ausgeführten Fahrbahnplatten Berücksichtigung. Das zusätzlich aufgenommene Prüflos 8 mit einem Labormörtel dient der Herausarbeitung des Materialeinflusses auf die Präzision der Spaltzugfestigkeitsprüfung. Zusammenfassend kann festgestellt werden, dass die Präzision der in der AL SP-Beton beschriebenen Spaltzugfestigkeitsprüfung mit einem Variationskoeffizienten von weniger als 10 % unter Wiederhol- und Vergleichbedingungen hinreichend genau ist. Der geringe Unterschied zwischen den Variationskoeffizienten unter Wiederhol- und Vergleichbedingungen lässt zusätzlich den Schluss zu, dass der Einfluss des unterschiedlichen Personals und der verschiedenartigen Prüftechniken bei den einzelnen Prüfstellen relativ gering ist. Die im Rahmen des Ringversuchs gewonnenen Erkenntnisse haben bereits partiell Eingang in die Normung gefunden.