The solgel process was applied to enhance properties of pine sapwood. For this purpose wood prisms were soaked in nanoscaled precursor solutions prepared from titanium(IV) n-butoxide and titanium(IV) iso-propoxide, respectively, using vacuum impregnation technique. The wet composites were cured by special program with final heat treatment at 103 °C. Weight percent gains (WPG) of the wood specimen in the range of 19-25% were obtained due to these procedures. SEM investigations show that precursor solutions penetrate into the whole wood body and the titania formed after heat treatment in the composites is deposited in the pores (lumen) and partly in the cell walls of the wooden matrix. The moisture sorption was investigated in long term tests for a period of some months by storage at 20-23 °C in humid air (relative humidity of 99%) and ambient atmosphere (relative humidity 40-60%), respectively. For untreated reference samples the moisture sorption results in increasing of mass and volume according to saturation values of 24 and 13%, respectively, after about 15 days. The incorporation of titania reduces the saturation values of the moisture sorption by up to 12% in mass and by up to 5% in volume at a relative humidity of 99%. Thus, an enhancement of the dimensional stability of about 60% is obtained at best. The results demonstrate that modification of wood with sol-gel derived precursors can enhance its dimensional stability, which prevents the formation of cracks. Because of that reduced moisture sorption biological attacks should be delimited. Additionally, thermal analyses show a retarded combustion of the wood matrix due to titania infiltration.
The metabolism of moulds results in the formation of various microbial volatile organic compounds (MVOCs). These substances can be used as an indicator for the presence of moulds in the indoor environment. Three different mould strains were cultivated on culture media and IMS spectra of gaseous mould metabolites were recorded using a portable mini system with a tritium source and a 5 cm drift cell. The headspace spectra are characteristic for mould species and their age. Typical gaseous components of the metabolites were identified and compared with results obtained from gas chromatography using a mass spectrometer detector. It was observed that the MVOCs formation depends on mould species and their growing stage with a maximum of MVOCs emission occurring during the first 10 days. These preliminary results show that IMS can be applied to detect MVOCs in indoor environment and indicate hidden mould growth.
A market survey has been performed of commercially available hydrogen safety sensors, resulting in a total sample size of 53 sensors from 21 manufacturers. The technical specifications, as provided by the manufacturer, have been collated and are displayed herein as a function of sensor working principle. These specifications comprise measuring range, response and recovery times, ambient temperature, pressure and relative humidity, power consumption and lifetime. These are then compared against known performance targets for both automotive and stationary applications in order to establish in how far current technology satisfies current requirements of sensor end users. Gaps in the performance of hydrogen sensing technologies are thus identified and areas recommended for future research and development.