Experimental investigation of the laser-plume interaction during high power fiber laser welding
(2011)
The effect of the well-known plasma absorption and refraction in CO2-laser metal welding plumes is in case of high power solid state laser welding negligibly small. By contrast, the diffraction effects of shorter wavelength laser radiation are considerable. According
to the results of preliminary studies, the fine condensed metal particles in the welding plume can lead to essential worsening of the laser beam quality.
This work is devoted to the investigation of the lasermatter interaction during up to 20 kW ytterbium fiber laser welding of thick mild steel plates. The plume attenuation of a probe 1.3 µm wavelength diode laser beam as well as of continuous radiation in 250-600 nm
wavelength range was measured during welding with and without Ar shielding gas supply. The measured results allow it to calculate average size and concentration of fine condensed metal particles in
different plume areas using the multi-wavelength method and the Mie scattering theory. The plume temperature, which determines the condensation conditions, was measured by means of Fe I atom
spectral line emission registration.
The obtained results can be also of interest for remote metal treatment with high-power fiber or disc lasers.
A three-dimensional laminar steady
state numerical model was used to investigate
the influence of an alternating current (ac)
magnetic field during high power laser beam
keyhole welding of 20 mm thick nonferromagnetic
aluminum. COMSOL
Multiphysics was used to calculate the threedimensional
heat transfer, fluid dynamics and
electromagnetic field equations. Most
important physical effects of the process were
taken into account: Thermo-capillary
(Marangoni) convection at the upper and lower
weld pool boundaries, natural convection due
to gravity and latent heat of solid-liquid phase
transition. It is shown that the gravity drop-out
associated with welding of thick plates due to
the hydrostatic pressure can be prevented by
the application of an ac magnetic field. The
application of an oscillating magnetic field of
70 mT was investigated to allow for singlepass
laser beam welding of thick aluminum
plates. The flow pattern in the molten zone and
the temperature distributions are significantly
changed.