Organic thin films with defined chemical structures and physical properties are required for various applications. Plasma polymerization is of technological interest, since the deposition of plasma polymers is possible on any material of any shape in the desired thickness. We report on the TOF-SIMS (TOF: time-of-flight) and XPS investigations of pulse plasma poly(acetylene) and alkali metal doped pulse plasma poly(acetylene) films. The combination of TOF-SIMS and XPS supplies detailed information on the surface chemistry of these films. Application of both methods provides the possibility for cross-checking certain results. Moreover the different sensitivities of the methods can be utilized. According to the TOF-SIMS and XPS data it can be concluded that the interaction of alkali metals with plasma poly(acetylene) results in electrovalent bonds of the type Me?+C?- between carbon and metal. Furthermore carbonoxygenmetal interactions were observed. These interactions are of the type C=O?-cdots, three dots, centeredMe?+ and/or CO?-Me?+.
Overlayers of SiO2 (nominally 4, 6 and 8 nm thick) on silicon, prepared by thermal oxidation, were investigated using x-ray photoelectron spectroscopy (XPS). The thickness of these overlayers was obtained from a measurement of the photoelectron intensities originating from the substrate and the oxide overlayer by applying an appropriate quantitative model. The uncertainty budget of that thickness measurement method is given. The relative combined standard uncertainty of the method was found to be 15%. The effective attenuation lengths or the corresponding electron inelastic mean free paths are of considerable importance for both the estimated values of overlayer thickness and combined standard uncertainties. The XPS results were compared with ellipsometry data.
Results of an interlaboratory comparison of XPS data obtained with stainless steel are presented. Only one photoelectron spectrometer model was used. The stainless-steel sample surfaces were analysed in different states by XPS: as received, after sputtering to I(C 1s)/I(Fe 2p3/2) 0.025 and after removing a chromium-enriched oxide layer following a certain protocol. The Fe, Cr and Ni elemental concentrations were evaluated from the respective XPS data submitted by the participants of the interlaboratory test experiment. Total means, repeat standard deviations (sr) and reproducibility standard deviations (sR) are presented. The best reproducibility standard deviations were obtained for the XPS analysis after removal of a chromium-enriched oxide layer and quantification of the XPS intensities without taking the contamination elements of carbon and oxygen into account. The absolute reproducibility standard deviation of the elemental concentrations in that case is as small as 1.1-1.5 at.%. This gives 2%, 6% and 16% for the relative reproducibility standard deviation of the concentrations of iron, chromium and nickel, respectively. The total means of the iron, chromium and nickel concentrations finally obtained agree within 2sR with bulk values determined by wavelength-dispersive x-ray fluorescence spectroscopy. Comparison to an earlier interlaboratory test experiment shows that using only one model of photoelectron spectrometer reduces the reproducibility standard deviations efficiently. Copyright © 2002 John Wiley & Sons, Ltd.
Results are reported from a pilot study under the Consultative Committee for Amount of Substance (CCQM) to compare measurements of and resolve any relevant measurement issues in, the amount of thermal SiO2 oxide on (100) and (111) orientation Si wafer substrates in the thickness range 1.5 - 8 nm. As a result of the invitation to participate in this activity, 45 sets of measurements have been made in different laboratories using 10 analytical methods: medium-energy ion scattering spectrometry (MEIS), nuclear reaction analysis (NRA), RBS, elastic backscattering spectrometry (EBS), XPS, SIMS, ellipsometry, grazing-incidence x-ray reflectrometry (GIXRR), neutron reflectometry and transmission electron microscopy (TEM). The measurements are made on separate sets of 10 carefully prepared samples, all of which have been characterised by a combination of ellipsometry and XPS using carefully established reference conditions and reference parameters.
The results have been assessed against the National Physical Laboratory (NPL) data and all show excellent linearity. The remaining data sets correlate with the NPL data with average root-mean-square scatters of 0.15 nm, half being better than 0.1 nm and a few at or better than 0.05 nm. Each set of data allows a relative scaling constant and a zero thickness offset to be determined. Each method has an inherent zero thickness offset between 0 nm and 1 nm and it is these offsets, measured here for the first time, that have caused many problems in the past. There are three basic classes of offset: water and carbonadeous contamination equivalent to ~1 nm as seen by ellipsometry; adsorbed oxygen mainly from water at an equivalent thickness of 0.5 nm as seen by MEIS, NRA, RBS and possibly GIXRR; and no offset as seen by XPS using the Si 2p peaks. Each technique has a different uncertainty for the scaling constant and consistent results have been achieved. X-Ray photoelectron spectroscopy has large uncertainties for the scaling constant but a high precision and, critically, if used correctly, has zero offset. Thus, a combination of XPS and the other methods allows the XPS scaling constant to be determined with low uncertainty, traceable via the other methods. XPS laboratories returning results early were invited to test a new reference procedure. All showed very significant improvements. The reference attenuation lengths thus need scaling by 0.986 ± 0.009 (at an expansion factor of 2) deduced from the data for the other methods. Several other methods have small offsets and, to the extent that these can be shown to be constant or measurable, then these methods will also show low uncertainty. Recommendations are provided for parameters for XPS, MEIS, RBS and NRA to improve their accuracy.
First results of an inter-laboratory comparison (27 participants in Europe, Japan and USA) of XPS data obtained with non-conducting samples are presented. Binding energies of Al 2s for alumina, N 1s and imide C 1s for Kapton and Sr 3p3/2 for a strontium titanate film on glass were obtained after static charge referencing with the help of 15 nm gold particles deposited at the surface of the test samples. For the alumina sample C 1s static charge referenced data are also presented. Repeat standard deviations (sr), between standard deviations (sb), reproducibility standard deviations (sR) and total means are evaluated from the experimental data. It can be stated that although the repeat standard deviation is as small as 0.05 eV in the best case, the standard deviation characterizing the reproducibility of the method is obviously not better than 0.15 eV in the best case at the present time. The knowledge of these standard deviations is important for metrology, validations of analytical procedures relying on qualitative photoelectron spectroscopy and XPS databanking.
Methods for characterization of epoxy-functionalized substrates used for microarray applications, prepared by silanization with 3-glycidoxypropyltrimethoxysilane, have been developed. Contact angle measurements, X-ray photoelectron spectroscopy, time of flight secondary ion mass spectrometry and fluorescence based methods have been applied to investigate these epoxy-functionalized microarray substrates. The surface density of epoxy-functionalized glass slides was investigated by fluorescence labeling of surface species utilizing Rhodamine 110 as fluorescence probe.
Nitrogen rich plasma polymer films (L-PPE:N) were prepared by low-pressure RF plasma using a 1:1 mixture of ethylene and ammonia and aged for 345 d in four different ambient conditions: (i) at room temperature (RT) in air; (ii) at RT in nitrogen; (iii) at -20?°C in air and; (iv) at –20 °C in nitrogen. The films were analyzed by X-ray photoelectron spectroscopy (XPS) and by time-of-flight secondary ion mass spectrometry (ToF-SIMS) at various intervals over the duration of the experiment. The ageing of primary amines, NH2, was followed by chemical derivatization with 4-trifluoromethyl benzaldehyde. Storage at –20 °C, mostly independently of ambient atmosphere, slowed down ageing to almost undetectable levels as evaluated by the analytical methods used for this study.
A combined XPS, NEXAFS, and ToF-SIMS chemical surface characterization of carbohydrate-functionalized gold and glass surfaces is presented. Spot shape and chemical composition across a spot surface are provided by surface-sensitive methods as ToF-SIMS and XPS, used in their imaging modes. Moreover, the feasibility of this multimethod approach to control relevant production steps of a carbohydrate microarray prototype is demonstrated.
Functionalized organic layers prepared by plasma processes have complex surface chemistries. The problem of elucidating such chemistries is an extensively studied subject. One of the preponderant methods used to acquire information on specific functional groups is chemical derivatization XPS. In this communication, we focus on rather popular chemical derivatization XPS approaches, for instance, the quantification of amines with 4-trifluoromethyl benzaldehyde and of hydroxyl groups with trifluoroacetic anhydride. Although these procedures have been used for a long period by various laboratories, the use of varying protocols is obvious. Comparison of results is therefore difficult. We discuss steps toward a valid experimental procedure, in particular, the calculation of concentrations, the preparation of test samples, the pitfalls, and the shortcomings.
The wettability of the surfaces inside the microchannels of a microfluidic device is an important property considering a liquid flows through them. Contact angle measurements usually applied to test the wettability of surfaces cannot be used for an analysis of microchannel walls within microfluidic devices. A workaround is the use of surface analytical methods, which are able to reach points of interest in microchannels and may provide information on the surface chemistry established there. In calibrating these methods by using flat polymer wafers, where the contact angle can be measured as usual, data measured in real microchannels can be evaluated in terms of wetting properties. Reference wafers of bisphenol-A polycarbonate, a polymeric material that is often used in fluidic microdevice fabrication, were treated under different oxygen plasma conditions. The modified surfaces were characterized by using XPS, time of flight (ToF)-SIMS and atomic force microscope (AFM). Surface chemistry and surface topography have been correlated with contact angle measurements. In addition, effects of ageing or rinsing after plasma treatment have also been investigated.