Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (31)
- Vortrag (25)
- Beitrag zu einem Tagungsband (8)
- Posterpräsentation (3)
- Buchkapitel (2)
- Beitrag zu einem Sammelband (1)
- Sonstiges (1)
- Forschungsbericht (1)
Schlagworte
- Neutron radiography (15)
- Hydrogen (10)
- Neutron imaging (10)
- LIBS (9)
- Diffusion (8)
- Welding (8)
- Hydrogen embrittlement (7)
- In situ measurement (7)
- Neutron tomography (6)
- Hydrogen diffusion (5)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (25)
We report about investigations of typical material problems in steels. First, residual stresses in and around weld seams with low martensite transition temperature filler material were analyzed w/ and w/o additional transverse tensile load. The investigation was accompanied by x-ray diffraction measurements to track stress-induced phase transitions. Martensite formation during welding under external load yield strain gradients near the surface that improve the integrity of the weld. Further, the residual stress distribution close to laser-treated steel surfaces was analyzed. The method could be improved to reduce analysis artifacts. Finally, hydrogen diffusion in different steels was measured using neutron radiography and subsequent image analysis. Diffusion coefficients were derived by analyzing the time-dependent mass flux. In an outlook we describe the optimal ESS instrumentation from a metallurgists point of view.
Chemical compositions of a weld can be varying locally as a result of the welding process. These local variations can be due to the vaporization of individual alloying elements. In this work, tungsten inert gas (TIG) bead-on-plate stainless steel welds of EN grade 1.4404 and 1.4435 were investigated using laser-induced breakdown spectroscopy (LIBS) on the completed welds. This study aims to reveal the welding parameters’ influence on the resulting local chemical compositions of the stainless steel welds. We demonstrated Mn vaporize before Cr due to its lower latent enthalpy of vaporization. Hence, Mn accumulates on the heat-affected zone (HAZ) both sides across the weld bead by being swept away through the circulation flow of the welding plasma. Additionally, increasing the heat input tends to enhance the accumulated Mn content on the HAZ as well as increasing the shielding gas flow rate. The results are in good agreement with the literature and proved that LIBS is an effective method to inspect completed welds.
Polychromatic and wavelength-selective neutron transmission radiography were applied during bead-on-plate welding on 5 mm thick sheets on the face side of martensitic low transformation temperature (LTT) steel plates using gas tungsten arc welding (GTAW). The in situ visualization of austenitization upon welding and subsequent α’-martensite formation during cooling could be achieved with a temporal resolution of 2 s for monochromatic imaging using a single neutron wavelength and of 0.5 s for polychromatic imaging using the full spectrum of the beam (white beam). The spatial resolution achieved in the experiments was approximately 200 µm. The transmitted monochromatic neutron beam intensity at a wavelength of λ = 0.395 nm was significantly reduced during cooling below the martensitic start temperature Ms since the emerging martensitic phase has a ~10% higher attenuation coefficient than the austenitic phase. Neutron imaging was significantly influenced by coherent neutron scattering caused by the thermal motion of the crystal lattice (Debye–Waller factor), resulting in a reduction in the neutron transmission by approx. 15% for monochromatic and by approx. 4% for polychromatic imaging.
Polychromatic and wavelength-selective neutron transmission radiography were applied during bead-on-plate welding on 5 mm thick sheets on the face side of martensitic low transformation temperature (LTT) steel plates using gas tungsten arc welding (GTAW). The in situ visualization of austenitization upon welding and subsequent α’-martensite formation during cooling could be achieved with a temporal resolution of 2 s for monochromatic imaging using a single neutron wavelength and of 0.5 s for polychromatic imaging using the full spectrum of the beam (white beam).
The spatial resolution achieved in the experiments was approximately 200 µm. The transmitted monochromatic neutron beam intensity at a wavelength of λ = 0.395 nm was significantly reduced during cooling below the martensitic start temperature M s since the emerging martensitic phase has a ~10% higher attenuation coefficient than the austenitic phase. Neutron imaging was significantly influenced by coherent neutron scattering caused by the thermal motion of the crystal lattice (Debye–Waller factor), resulting in a reduction in the neutron transmission by approx. 15% for monochromatic and by approx. 4% for polychromatic imaging.
Neutron Bragg-edge imaging was applied for the visualization of a γ-Austenite to α'-martensite phase transformation. In the present study, a super martensitic
stainless steel sample was heated until complete austenitization and was subsequently cooled down to room temperature. The martensitic phase Transformation started at Ms = 190 °C. Using a monochromatic neutron beam with λ = 0.390 nm, the transmitted intensity was significantly reduced during cooling below Ms, since the emerging martensitic phase has a higher attenuation coefficient than the austenitic phase at this wavelength. The phase Transformation process was visualized by filming the transmission images from a scintillator screen with a CCD camera with a temporal resolution of 30 s and a spatial
resolution of 100 µm.
We investigated hydrogen embrittlement and blistering in electrochemically hydrogen-charged technical iron samples at room temperature. Hydrogen-stimulated cracks and blisters and the corresponding hydrogen distributions were observed by neutron tomography. Cold neutrons were provided by the research reactor BER II to picture the sample with a spatial resolution in the reconstructed three-dimensional model of ~25 µm. We made the unique observation that cracks were filled with molecular hydrogen and that cracks were surrounded by a 50 µm wide zone with a high hydrogen concentration. The zone contains up to ten times more hydrogen than the bulk material. The hydrogen enriched zone can be ascribed to a region of increased local defect density. Hydrogen also accumulated at the sample surface having the highest concentration at blistered areas. The surfaces of the brittle fractured cracks showed micropores visualized by scanning electron microscopy. The micropores were located at grain boundaries and were surrounded by stress fields detected by electron backscattered diffraction. The cracks clearly originated from the micropores.
Die Ergebnisse von in-situ Experimenten am Berliner Elektronenspeicherring (BESSY II) werden vorgestellt. Es wurden Zugversuche an wasserstoffbeladenen und wasserstofffreien supermartensitischen Proben durchgeführt und Diffraktionsspektren und radiographische Bilder aufgenommen. Die energiedispersive Röntgendiffraktion ermöglichte dabei in-situ die dehnungsinduzierte Phasenumwandlung von Restaustenit zu Martensit zu beobachten. Die Radiographiebilder der zerreisenden Probe gaben Einblicke in das Bruchverhalten in Abhängigkeit vom Wasserstoffgehalt.
In Neutron-Bragg-Edge Imaging (NBEI) in situ experiments, we studied the phase transitions in martensitic steel sheets during butt-welding. Gas tungsten arc welding was used with a motorized torch allowing automated weldments. The austenitization in the heat affected zone underneath the welding head could be clearly visualized. Also, the retransformation into the martensitic phase upon cooling. However, we observed an unexpected additional change in transmission at λ = 0.44 nm that is at a wavelength larger than the wavelength of the Bragg edges of both the martensitic and austenitic phases. We attribute this change to the Deybe-Waller-Factor that describes the temperature dependence of coherent scattering at a crystal lattice. With help of temperature field simulations that were calibrated by the reading of anattached thermo couple during welding, we could show that the Debye-Waller factor can produce an additional image contrast.
We could show in GTAW experiments with steel samples that the attenuation of neutron transmission underneath the welding torch due to the Debye-Waller-effect correlates well with sample temperatures obtained by FE numerical simulations. This would allow principally to determine sample temperatures by measuring the neutron beam attenuation.
Neutron radiography (NR) is compared with the commonly used carrier gas hot extraction (CGHE) technique. We performed isothermal hydrogen effusion experiments at 623 K to study the mass transport kinetics. The investigated material was technical iron. The quantification of the hydrogen mass flow is done for NR by using concentration standards. The temporal hydrogen concentration evolution in the sample coincides well for both methods, i.e. NR and CGHE, and is in good agreement with literature. The advantages of the NR method are the non-destructive nature of measuring and the in-situ determination of hydrogen concentrations with high spatial and temporal resolution. Remaining hydrogen inside the sample can be identified directly by the NR method.
This study was carried out to investigate the neutron transmission signal as a function of sample temperature during a welding process. A theoretical description that includes the Debye-Waller factor was used to describe the temperature influence on the neutron crosssections. Neutron imaging using a monochromatic beam helps to observe transmission variations related to the material temperature. In-situ neutron imaging of welding experiments show the distribution of the temperature in bulk steel samples. The performed finite element modelling of expected temperature distributions shows good agreement with the obtained experimental data.
The purpose of the present study was to show the feasibility of measuring hydrogen effusion in austenitic stainless steel (1.4301) using neutron radiography at the facility ANTARES of the research reactor FRM II of the Technische Universität München. This method is appropriate to measure in-situ hydrogen effusion for hydrogen concentrations as small as 20 ppmH. Experiments were carried out in the temperature range from room temperature up to 533 K. The measurement principle is based on the parallel comparison of electrochemically hydrogen charged specimen with hydrogen-free reference specimen at the same temperature. This allows the determination of the hydrogen concentration in the specimens as a function of time and temperature. Separate hot carrier gas extraction experiments using the same temperature–time profiles as the radiography experiments have been used to calibrate the grey values of the neutron transmission images into hydrogen concentrations. It can be stated that the hydrogen effusion correlates with the specimen temperature.
Duplex stainless steels (DSS) are used in all industries where corrosion problems play a major role. Examples include the chemical industry, the food industry and shipping industries. DSS have a balanced phase ratio of ferrite (α) and austenite (γ). Unlike single-phase stainless steels, DSS combine the advantages of these and can therefore fit many industry requirements, such as weight saving or high mechanical strength. When these steels are welded, alloying elements can burn off and condense as thin layers on cold surface regions. This loss of chemical elements can lead to changes in the microstructure. With the help of Laser-Induced Breakdown Spectroscopy (LIBS), chemical element distributions were visualized. The results were compared with those of conventional measurement methods, such as energy dispersive X-ray analysis (EDS) and X-ray fluorescence analysis (XRF), and the results from LIBS could be validated. LIBS is suitable as a fast, straightforward measurement method for producing line scans along the weld seam and provides spatially resolved information on accumulation phenomena of burned off alloying elements. LIBS is very well suited for the detection of sub-surface elements due to the exclusively superficial ablation of the material. In addition, the measurement method has been calibrated so that quantitative statements about element concentrations can also be made.
The Modified Varestraint Transvarestraint (MVT) test was used to investigate the solidification cracking susceptibility of an unstabilised, a Nb-stabilised and two (Ti + Nb) dual-stabilised ferritic stainless steels. Two different welding speeds of 6 and 3 mm/s using autogenous gas tungsten arc welding were employed. At the welding speed of 6 mm/s, the high-content (Ti + Nb) steel was resistant and the Nb-stabilised steel was marginally susceptible to solidification cracking. At the welding speed of 3 mm/s, the Nb and the high (Ti + Nb) steels were found to be marginally susceptible to solidification cracking while the unstabilised and low-content (Ti + Nb) grades were resistant to solidification cracking. The weld metal microstructures transverse to the welding direction revealed columnar grains in all the samples for both welding speeds. The ferritic stainless steels were generally resistant to solidification cracking, except the Nb-stabilised steel, which was marginally susceptible to solidification cracking.