Filtern
Dokumenttyp
- Zeitschriftenartikel (15)
- Vortrag (8)
- Beitrag zu einem Tagungsband (2)
Schlagworte
- LIBS (7)
- Welding (6)
- In situ measurement (5)
- Neutron imaging (5)
- TIG welding (4)
- Hydrogen (3)
- Neutron radiography (3)
- Austenite-to-martensite transformation (2)
- Bragg-edge imaging (2)
- Chemical composition (2)
- Debye-Waller-Faktor (2)
- Debye–Waller factor (2)
- Duplex stainless steel (2)
- Gas tungsten arc welding (GTAW) (2)
- Hydrogen embrittlement (2)
- Low transformation temperature (LTT) steel (2)
- Neutron (2)
- Radiography (2)
- Steel (2)
- WRC 1992 diagram (2)
- 2101 duplex stainless steel (1)
- Austenitic (1)
- Austenitic stainless steel (1)
- Austenitic stainless steels (1)
- Backlight (1)
- Bragg-edge neutron 2D imaging (BENI) (1)
- Computed tomography (1)
- Crystallographic texture control (1)
- Dduplex stainless steel (1)
- Debye waller factor (1)
- Debys-Waller-Factor (1)
- Diffusible hydrogen (1)
- Duplex stainless steels (1)
- EDS (1)
- Electron backscatter diffraction (EBSD) (1)
- Evaporation (1)
- Ferritic stainless steel (1)
- GTAW (1)
- Hydrogen assisted cracking (1)
- Hydrogen diffusion (1)
- Hydrogen measurement (1)
- IN718 PBF-LB/M (1)
- In situ (1)
- LIBS TIG welding (1)
- Materialschaedigung (1)
- Materialschädigung (1)
- Measurement (1)
- Metal additive manufacturing (MAM) (1)
- Metal vapor (1)
- Microcracking (1)
- Microstructure (1)
- Modified Varestraint Transvarestraint (1)
- Neutron Imaging (1)
- Neutron tomography (1)
- Refraction (1)
- Röntgenradiographie (1)
- Scattering (1)
- Snergiedispersive Röntgendiffraktion (1)
- Solidification cracking (1)
- Stainless steel (1)
- Stainless steels (1)
- Supermartensitic steel (1)
- Supermatensitischer Stahl (1)
- Susceptibility (1)
- Synchrotron (1)
- Synchrotron radiation (1)
- TIG (1)
- Temperature distribution determination (1)
- Tomography (1)
- Wasserstoff (1)
- Wasserstoffdegradation (1)
- X-ray refraction (1)
- XRF (1)
- Zugversuch (1)
Organisationseinheit der BAM
- 9 Komponentensicherheit (25) (entfernen)
Eingeladener Vortrag
- nein (8)
We could show in GTAW experiments with steel samples that the attenuation of neutron transmission underneath the welding torch due to the Debye-Waller-effect correlates well with sample temperatures obtained by FE numerical simulations. This would allow principally to determine sample temperatures by measuring the neutron beam attenuation.
Die Ergebnisse von in-situ Experimenten am Berliner Elektronenspeicherring (BESSY II) werden vorgestellt. Es wurden Zugversuche an wasserstoffbeladenen und wasserstofffreien supermartensitischen Proben durchgeführt und Diffraktionsspektren und radiographische Bilder aufgenommen. Die energiedispersive Röntgendiffraktion ermöglichte dabei in-situ die dehnungsinduzierte Phasenumwandlung von Restaustenit zu Martensit zu beobachten. Die Radiographiebilder der zerreisenden Probe gaben Einblicke in das Bruchverhalten in Abhängigkeit vom Wasserstoffgehalt.
In Neutron-Bragg-Edge Imaging (NBEI) in situ experiments, we studied the phase transitions in martensitic steel sheets during butt-welding. Gas tungsten arc welding was used with a motorized torch allowing automated weldments. The austenitization in the heat affected zone underneath the welding head could be clearly visualized. Also, the retransformation into the martensitic phase upon cooling. However, we observed an unexpected additional change in transmission at λ = 0.44 nm that is at a wavelength larger than the wavelength of the Bragg edges of both the martensitic and austenitic phases. We attribute this change to the Deybe-Waller-Factor that describes the temperature dependence of coherent scattering at a crystal lattice. With help of temperature field simulations that were calibrated by the reading of anattached thermo couple during welding, we could show that the Debye-Waller factor can produce an additional image contrast.
Die dehnungsinduzierte Martensitbildung wurde mittels Röntgen-Diffraktion und -Radiographie mit dem EDDI-Instrument am BESSY II in supermartensitischem Stahl mit Anlassaustenit untersucht. Die Bildung wird durch Wasserstoff im Gefüge unterdrückt. Die Duktilität von wasserstofffreiem SMSS korreliert mit dem Anteil an dehnungs-induziertem Martensit
Neutron imaging is a valuable tool for measuring hydrogen distributions qualitatively and quantitatively in metals. Time-resolved neutron radiography allows to measure hydrogen mass flow inside cm thick steel samples with ~10 s temporal resolution. Hydrogen accumulations around cracks in embrittled iron samples can be visualized three-dimensionally by neutron tomography. This quality of information allows new insights for the analysis of damage mechanisms on a micrometer scale, e.g. of hydrogen blistering. Even the gas pressure of molecular hydrogen in crack cavities has been measured from tomographic reconstructions to be in the range of 5 MPa to 15 MPa for technical iron. Further, this method is non-destructive and provides local information in situ and in all three dimensions with a spatial resolution of 20 - 30 µm. The combination with other methods gives a new quality of information, e.g. of the hydrogen allocation on fractured surfaces.
We investigated the phase transformations during butt-welding of supermartensitic steel plates with help of Neutron-Bragg-Edge Imaging (NBEI). Gas tungsten arc welding (GTAW) was used with a motorized torch allowing for automated weldments. The austenitization in the heat affected zone (HAZ) could be clearly visualized at λ = 0.39 nm, a wavelength smaller than the Bragg edge wavelengths of both austenite and martensite. The re-transformation into the martensitic phase during cooling was clearly detected. However, we observed an unexpected additional change in transmission at λ = 0.44 nm, a wavelength larger than the wavelength of the Bragg edges of both the martensitic and austenitic phases. We attribute this change to the Deybe-Waller-Factor that describes the temperature dependence of coherent scattering at a crystal lattice. The observed two-dimensional attenuation map corresponds well with a temperature distribution modelling by software macros in ANSYS [3]. Here, the absolute temperature values could be achieved by calibrating the modelled attenuation with help of a thermocouple placed at the steel plate. This allows in return for a direct two-dimensional temperature reading based on the Debye-Waller-relation between neutron attenuation and sample temperature.
In Neutron-Bragg-Edge Imaging (NBEI) experiments, we studied the phase transition during butt-welding of supermartensitic steel plates. Gas tungsten arc welding (GTAW) was used with a motorized torch allowing for automated weldments. The austenitization in the heat affected zone (HAZ) underneath the welding head could be clearly visualized at λ = 0.39 nm, a wavelength smaller than the Bragg edge wavelengths of both austenite and martensite. Also, the re-transformation into the martensitic phase upon cooling was detected. However, we observed an unexpected additional change in transmission at λ = 0.44 nm that is a wavelength larger than the wavelength of the Bragg edges of both the martensitic and austenitic phases. We attribute this change to the Deybe-Waller-Factor that describes the temperature dependence of coherent scattering at a crystal lattice. The observed two-dimensional attenuation map corresponds well with a temperature distribution modelling by software macros in ANSYS. Here, the absolute temperature values could be achieved by calibrating the modelled attenuation with help of a thermocouple placed at the steel plate. This allows in return for a direct two-dimensional temperature reading based on the Debye-Waller-relation between neutron attenuation and sample temperature.
Polychromatic and wavelength-selective neutron transmission radiography were applied during bead-on-plate welding on 5 mm thick sheets on the face side of martensitic low transformation temperature (LTT) steel plates using gas tungsten arc welding (GTAW). The in situ visualization of austenitization upon welding and subsequent α’-martensite formation during cooling could be achieved with a temporal resolution of 2 s for monochromatic imaging using a single neutron wavelength and of 0.5 s for polychromatic imaging using the full spectrum of the beam (white beam). The spatial resolution achieved in the experiments was approximately 200 µm. The transmitted monochromatic neutron beam intensity at a wavelength of λ = 0.395 nm was significantly reduced during cooling below the martensitic start temperature Ms since the emerging martensitic phase has a ~10% higher attenuation coefficient than the austenitic phase. Neutron imaging was significantly influenced by coherent neutron scattering caused by the thermal motion of the crystal lattice (Debye–Waller factor), resulting in a reduction in the neutron transmission by approx. 15% for monochromatic and by approx. 4% for polychromatic imaging.
Neutron cameras allow visualizing hydrogen distributions with radiographic or tomographic imaging methods in iron and steel. The necessary contrast between hydrogen and iron stems from the high difference in the total neutron cross section of both elements. This allows e.g. the in situ measurement of hydrogen mass flow inside cm thick steel samples with a temporal resolution of 20 s using neutron radiography as well as the quantitative measurement of hydrogen accumulations at the crack’s inner surfaces in hydrogen embrittled iron samples with neutron tomography. We could detect directly gaseous hydrogen in the crack cavities and we measured the gas pressure. This new quality of the information on a micrometer scale allows new insights for the analysis of hydrogen-induced damage mechanisms. Further, this method is non-destructive and provides local information in situ and in three dimensions with a spatial resolution of 20-30 µm. In this contribution, we show examples that demonstrate the spatial and temporal resolution of the neutron radiography and tomography methods in order to visualize and quantify hydrogen accumulations at cracks. The measurements were performed at the research reactor BER II of the HZB in Berlin and at the FRM II reactor of the neutron source Heinz Maier-Leibnitz in Garching.
Polychromatic and wavelength-selective neutron transmission radiography were applied during bead-on-plate welding on 5 mm thick sheets on the face side of martensitic low transformation temperature (LTT) steel plates using gas tungsten arc welding (GTAW). The in situ visualization of austenitization upon welding and subsequent α’-martensite formation during cooling could be achieved with a temporal resolution of 2 s for monochromatic imaging using a single neutron wavelength and of 0.5 s for polychromatic imaging using the full spectrum of the beam (white beam).
The spatial resolution achieved in the experiments was approximately 200 µm. The transmitted monochromatic neutron beam intensity at a wavelength of λ = 0.395 nm was significantly reduced during cooling below the martensitic start temperature M s since the emerging martensitic phase has a ~10% higher attenuation coefficient than the austenitic phase. Neutron imaging was significantly influenced by coherent neutron scattering caused by the thermal motion of the crystal lattice (Debye–Waller factor), resulting in a reduction in the neutron transmission by approx. 15% for monochromatic and by approx. 4% for polychromatic imaging.