Filtern
Erscheinungsjahr
Dokumenttyp
Schlagworte
- Neutron radiography (8)
- LIBS (7)
- Hydrogen (5)
- In situ measurement (5)
- Hydrogen diffusion (4)
- Hydrogen embrittlement (4)
- TIG welding (4)
- Welding (4)
- X-ray refraction (4)
- Diffusion (3)
- Duplex stainless steel (3)
- Hydrogen assisted cracking (3)
- Neutron tomography (3)
- Steel (3)
- Austenitic stainless steels (2)
- Blister (2)
- Chemical composition (2)
- Computed tomography (2)
- Duplex stainless steels (2)
- Hot cracking (2)
- In situ (2)
- Iron (2)
- Synchrotron radiation (2)
- WRC 1992 diagram (2)
- 2101 duplex stainless steel (1)
- Aluminium alloy (1)
- Aluminium alloys (1)
- Analyser based imaging (1)
- Analyser-based imaging (1)
- Austenitic (1)
- Austenitic stainless steel (1)
- CT (1)
- Carrier gas hot extraction (1)
- Component design (1)
- Computed tomography (CT) (1)
- Crack criterion (1)
- Dduplex stainless steel (1)
- Diffusible hydrogen (1)
- EDS (1)
- Evaporation (1)
- External load test (1)
- GTA welding (1)
- Grain growth (1)
- Hydrogen assisted cracking (HAC) (1)
- Hydrogen effusion (1)
- Hydrogen embrittlement (HE) (1)
- Hydrogen measurement (1)
- Imaging (1)
- In-situ (1)
- LIBS TIG welding (1)
- Measurement (1)
- Metal vapor (1)
- Microcracking (1)
- Neutron imaging (1)
- Radiography (1)
- Real-time operation (1)
- Röntgenrefraktion (1)
- Stainless steel (1)
- Stainless steels (1)
- Synchrotron (1)
- TIG (1)
- Wasserstoffunterstützte Rissbildung (1)
- Wasserstoffversprödung (1)
- XRF (1)
Organisationseinheit der BAM
The purpose of the present study is to show the feasibility of examining hydrogen desorption in technical iron samples using neutron radiography at the ANTARES facility of the FRM II research reactor, Technische Universität München. It has been shown that this method is appropriate for in situ determination of hydrogen Desorption for concentrations as low as 20 ppmH. Experiments were carried out in the temperature range from room temperature up to 260 °C. Measurement was based on direct comparison between electrochemically hydrogen-loaded iron samples and hydrogen-free reference samples at the same temperature.
This enables the determination of hydrogen concentration as a function of time and temperature. Ex situ carrier gas hot extraction experiments using the same temperature–time profiles as the neutron radiography experiments have been used to calibrate the greyscale values of the radiographs to defined hydrogen concentrations. It can be stated that hydrogen desorption correlates with sample temperature.
The purpose of the present study was to show the feasibility of measuring hydrogen effusion in austenitic stainless steel (1.4301) using neutron radiography at the facility ANTARES of the research reactor FRM II of the Technische Universität München. This method is appropriate to measure in-situ hydrogen effusion for hydrogen concentrations as small as 20 ppmH. Experiments were carried out in the temperature range from room temperature up to 533 K. The measurement principle is based on the parallel comparison of electrochemically hydrogen charged specimen with hydrogen-free reference specimen at the same temperature. This allows the determination of the hydrogen concentration in the specimens as a function of time and temperature. Separate hot carrier gas extraction experiments using the same temperature–time profiles as the radiography experiments have been used to calibrate the grey values of the neutron transmission images into hydrogen concentrations. It can be stated that the hydrogen effusion correlates with the specimen temperature.
In situ crack detection in the mushy zone and the solid weld of a gas tungsten arc (GTA) weld using X-ray imaging during welding is a new research area for NDT inspection. Usually, NDT flaw detection is done after the complete solidification of the weld seam. In this paper, we present the use of real-time radiography with a minifocus X-ray source (YXLON X-ray tube Y.TU 225-D04) and a 75μm pixel size digital detector array (Dexela 1512) for the acquisition of 2D radiographic images by a sequence of exposures with time intervals of 80 ms for hot crack detection during single pass bead-on-plate GTA welding of 3 mm thick plates of aluminium alloy AlMgSi (6060). An analysis of the crack distribution in the weld sample is conducted from the acquired 2D radiographs and its corresponding 3D volumetric reconstruction achieved by linear coplanar digital laminography.
This in situ approach opens new possibilities in the field of hot crack research by having the direct information of both the crack initiation and growth and its correlation to the welding parameters.
Hydrogen embrittlement (HE) is a widely known phenomenon and under investigation already for more than a century. This phenomenon, though thoroughly studied, is not yet completely understood, and so far, there are several suggested mechanisms that try to explain the occurrence of HE. One important factor of understanding the HE phenomenon and predicting hydrogen-assisted failure is the descent knowledge about the hydrogen transport behaviour in the material. Neutron radiography is a proven method for tracking hydrogen diffusion and it was applied successfully in various research studies. In the presented study, we examined the hydrogen effusion behaviour in duplex stainless steel by means of neutron radiography and calculated the effective diffusion coefficient from the obtained transmission images.
A long list of criteria determining the hot cracking susceptibility already exists. A main influence on solidification cracking can result from the design of the welded construction, i.e. from the influence of external loads. Using the Controlled Tensile Weldability (CTW) test, an external load hot cracking test, the influence of constant pre-load and different extension rates on the solidification cracking behavior of GTA (Gas Tungsten Arc) welds in an austenitic (AISI 309) and a ferritic (AISI 441) steel were investigated. Compared to specimens welded allowing free shrinkage and welded with an applied constant tensile pre-load, the specimens welded during the application of increasing tensile load show solidification cracks. In the weld seams, a characteristic angle α between the predominantly columnar grains and the fusion line can be observed. Specimens showing solidification cracks show a significantly larger angle α compared to the crack-free specimens. Based on these observations, the characteristic angle α is proposed as a new hot cracking criterion.
Revealing hydrogen embrittlement mechanisms in steels is of great interest to scientists and engineers. Neutron radiography makes it possible to measure in-situ hydrogen diffusion with high spatial and temporal resolution at concentrations as low as 20 ppm. We compare hydrogen-charged specimens with hydrogen-free reference specimens and use calibration standards to normalize the hydrogen concentrations. This allows quantitative tracking of the hydrogen concentration evolution as a function of time, space and temperature. Furthermore, a view into the material with 'neutron eyes' facilitates the detection of cavities that contain molecular hydrogen.
Neutron radiography and tomography have been used for a time resolved in situ analysis and a 3D mapping of hydrogen diffusion in iron and steel. Samples were electrochemically charged with hydrogen and afterwards neutron transmission images were taken. Hydrogen diffusion coefficients in duplex stainless steel were determined at 623 K by measuring and comparing the sample's mean intensity with a hydrogen-free reference sample and subsequent normalisation to standards with known hydrogen content. In technical iron and in supermartensitic stainless steel the hydrogen distributions have been investigated. The radiographic images in iron show blisters, cracks and the distribution of molecular hydrogen inside cracks. The analysis of the diffusion behaviour of hydrogen out of a blister illustrates the capabilities of the method with respect to time and spatial resolution. The neutron tomography of supermartensitic tensile stressed samples illustrates the capability to visualise hydrogen distributions three-dimensionally. -------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
On a utilisé la radiographie neutronique et la tomographie pour une analyse in situ à résolution temporelle et une cartographie 3D de la diffusion de l'hydrogène dans le fer et l'acier. On a chargé des échantillons par électrochimie avec de l'hydrogène et ensuite on a pris des images par émission de neutrons. On a déterminé les coefficients de diffusion de lhydrogène dans l'acier inoxydable duplex à 623 K en mesurant et en comparant l'intensité moyenne de l'échantillon avec un échantillon de référence sans hydrogène et une normalisation subséquente à des échantillons références à teneur connue en hydrogène. On a examiné la distribution d'hydrogène dans le fer technique et dans l'acier inoxydable supermartensitique. Les images radiographiques du fer montrent des soufflures, des fissures, et la distribution de l'hydrogène moléculaire à l'intérieur des fissures. L'analyse du comportement de diffusion de l'hydrogène hors d'une soufflure illustre les possibilités de la méthode par rapport à la résolution temporelle et spatiale. La tomographie neutronique des échantillons supermartensitiques chargés en traction illustre la capacité de visualiser les distributions d'hydrogène en trois dimensions.
Neutron tomography has been applied to investigate the mechanism of hydrogen assisted cracking in technical iron and supermartensitic steel. Rectangular technical iron block samples showed blistering due to intense hydrogen charging and the tomographic method revealed in situ the spatial distribution of hydrogen and cracks. Hydrogen accumulated in a small region around cracks and the cracks are filled with hydrogen gas. Cracks close to the surface contained no hydrogen. Hydrogenous tensile test samples of supermartensitic steel were pulled until rupture and showed hydrogen accumulations at the notch base and in the plastically deformed region around the fracture surface.
We investigated hydrogen embrittlement and blistering in electrochemically hydrogen-charged technical iron samples at room temperature. Hydrogen-stimulated cracks and blisters and the corresponding hydrogen distributions were observed by neutron tomography. Cold neutrons were provided by the research reactor BER II to picture the sample with a spatial resolution in the reconstructed three-dimensional model of ~25 µm. We made the unique observation that cracks were filled with molecular hydrogen and that cracks were surrounded by a 50 µm wide zone with a high hydrogen concentration. The zone contains up to ten times more hydrogen than the bulk material. The hydrogen enriched zone can be ascribed to a region of increased local defect density. Hydrogen also accumulated at the sample surface having the highest concentration at blistered areas. The surfaces of the brittle fractured cracks showed micropores visualized by scanning electron microscopy. The micropores were located at grain boundaries and were surrounded by stress fields detected by electron backscattered diffraction. The cracks clearly originated from the micropores.