A commonly used way of minimizing the occurrence of hot cracks, especially solidification cracks during component welding, is mainly to analyse and vary process parameters such as welding speed and consequently the heat input. Metallurgy and component design are however hardly ever considered due to special production requirements and therefore, restricted flexibility in material selection and design. Such conditions, especially crack-critical welding positions are given by slot-welds or welds near pre-deformed areas, for instance bending edges. Hence, it follows that increased local and global residual component stress caused cracking on reaching a solidification crack critical level, which is characterised by solidification crack initiation.