The fabric of mineral liner materials that had been exposed to organic compounds over a 12-year period was investigated as part of a wider research project. Macromorphological and micromorphological changes in the fabric were identified using computed tomography and polarisation microscopy.
Special care was taken to ensure artefact free sampling and sample preparation, in particular, the drying method used, has a substantial influence on the quality of the thin sections.
Fabric changes due to contaminant permeation over several years are, by and large, relatively small and their intensity is material specific. Silty clay CML1, in particular, contains a somewhat greater number of fissures and voids in comparison with the original material. The superposition of various processes in both test procedures and sample preparation may lead to fabric changes which can impede interpretation of the results.
In this paper the characterisation of functionally graded materials is elucidated by several different methods. These methods described here are used for the quantitative analysis of materials with a local dependence of microstructure parameters. Using X-ray microscopy (computed tomography) for 3D-measurements and optical microscopy on polished sections for 1D and 2D measurements on the same sample, a ceramic filter consisting of sintered spherical particles, various mathematical evaluation methods are described and compared.
Micro-computed tomography (µCT) provides quantitative three-dimensional information of bone around titanium implants similar to classical histology. The study, based on an animal model, using cuboid-shaped biofunctionalised Ti6Al4V implants with surrounding bone after 4 weeks, is performed using 3 µCT-systems with X-ray tubes, one synchrotron-radiation-based µCT-system (SRµCT), and classical histology. Although the spatial resolution of the µCTsystems is comparable, only the results of SRµCT agree with results of classical histology. The X-ray tube sources give rise to huge artefacts in the tomograms (interface scattering, beam hardening), which impaired the quantitative analysis of bone up to about 200 µm from the implant surface. Due to the non-destructive character of µCT the specimens can be subsequently examined by classical histology
without restriction. The quantitative comparison of bone formation uncovers the strong dependence of the detected amount of newly formed bone from the selected slice. This
implies the necessity of 3D analysis. SRµCT and classical histology prove that surface modifications of the titanium implant significantly influence the bone formation. Using SRµCT, the preparation artefacts due to cutting and polishing are excluded.