Eingeladener Vortrag
- nein (2)
LTCC-modules with integrated ferrite layers - Strategies for material development and co-sintering
(2008)
Silver in LTCC - Interfacial reactions, transport processes and influence on properties of ceramics
(2009)
New applications of low-temperature co-fired ceramics (LTCC), such as pressure sensors or integrated functional layers, require materials that possess higher coefficients of thermal expansion (CTE). To fabricate LTCC with elevated CTE, two methods of material design are examined: firstly, glass ceramic composites (GCC), which consist of >50 vol% glass in the starting powder, and, secondly, glass-bonded ceramics (GBC), where glass is added as a sintering aid only. The CTE of GBC is mainly determined by the crystalline component. For GCC, the CTE can be well predicted, if CTE and elastic data of each phase in the microstructure are known. A nonlinear characteristic of the CTE versus phase composition was found with increasing Ecrystals/Eglass ratio and absolute CTE difference between the components. The glass composition and glass amount can be used to compensate the fixed properties of a crystalline material in a desired way. However, because the CTE and permittivity of a glass cannot be chosen independently, an optimum glass composition has to be found. For a given LTCC, it is possible to control the devitrification by shifting the glass composition. In this way, the resulting CTE values can be predicted more exactly and tailoring becomes possible. Different LTCC materials, based on the crystalline compounds Ba(La,Nd)2Ti4O12, ZrO2 (Y-TZP), SiO2 (quartz), and specially developed glasses, possessing an elevated CTE of around 10 × 10-6 K-1 while showing permittivity εr between 6 and 63, are introduced.
Due to addition of minor amounts of suitable additive combinations to BaTiO3 powder the sintering temperature was reduced to 900 °C. Excellent densification (more than 98% of theoretical density) and good dielectric properties were achieved after sintering at 900 °C for 2 hours. Dielectric properties can be improved by modifying the composition of sintering additives and additon of further dopants. The low sintering temperature of newly developed capacitor material allows a co-sintering with pure silver electrodes. No interfacial reaction between silver electrodes and ceramics was observed by microprobe analysis. The dielectric constants of about 1200 to 3000 and the dielectric losses of about 0.008 to 0.02 were measured (f = 1 kHz, T = 25 °C). The temperature dependency of dielectric constant for new capacitor materials is low, almost X7R characteristics. Furthermore, the densification and the dielectric properties of embedded capacitors in LTCC were investigated.
By addition of LiF-containing sintering additives to commercial BaTiO3 powder, more than 98% of the theoretical density was reached at a sintering temperature of 900 °C both on powder compacts and laminates. Dielectric measurements were performed on ceramic samples in the temperature and frequency ranges from -20 °C to 125 °C and from 103 to 106 Hz, respectively. High relative permittivity (εr ~ 3160) and low dielectric loss (tan δ ~ 0.014) were measured for tapes of the favoured material. The breakdown strength for tapes with a thickness of about 80 µm is 30 kV/mm. The microprobe analysis showed, that no interfacial reaction between the dielectric layer and the Ag-electrode had occurred.
The newly developed barium titanate ceramics completely densifying at 900 °C turned out to be promising for integration of buried capacitors in LTCC multilayers.
LTCC-Modules with integrated ferrite layers - Strategies for material development and co-sintering
(2009)
The integration of passive components (resistors, capacitors, inductors) into LTCC modules is a challenging task in multilayer ceramics technology. We report on multilayer assemblies consisting of combined layers of ferrite and dielectric LTCC tapes. Ni-Cu-Zn ferrites with maximum shrinkage at 900°C were processed to green tapes and laminated with dielectric LTCC tapes. Cosintering at 900°C led to multilayers with different defects such as incomplete densification of the ferrite layers, cracks, and warpage. Since ferrite tapes do not really allow compositional changes without deterioration of magnetic properties, the dielectric tape was modified with the following objectives: (i) matching of the shrinkage curves of dielectric and ferrite materials, (ii) adjusting the coefficients of thermal expansion to avoid cracking during cooling, and (iii) controlling of interface reactions. Using this concept we fabricated dense and defect-free multilayers consisting of dielectric and ferrite layers. However, compositional changes of the individual ferrite tapes require the development of a specific dielectric tape material with tailored properties.