Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (18)
- Beitrag zu einem Tagungsband (4)
- Vortrag (1)
- Forschungsbericht (1)
Schlagworte
- Welding (8)
- Energy dispersive diffraction (3)
- Low transformation temperature (3)
- Phase transformation (3)
- Residual stress (3)
- Hot cracking (2)
- Interpass temperature (2)
- LTT (2)
- LTT Weld Filler Materials (2)
- LTT weld filler materials (2)
Organisationseinheit der BAM
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (1)
Solid-state phase transformations and the evolution of thermal and elastic strains in novel low temperature transformation (LTT) weld filler materials in the near surface region are monitored in real time by means of an innovative experimental set-up at the PDIFF (powder diffraction) beamline at the synchrotron light source ANKA (Angströmquelle Karlsruhe) at the KIT (Karlsruhe Institute for Technology). The key components of the diffraction set-up are two fast microstrip line detectors, which enables the strain evolution to be followed as a function of time and temperature for a 0.5?s counting time. During controlled heating and cooling cycles, as well as during near welding cycles, the martensite–austenite–martensite phase transitions are analysed. The transformation kinetics are monitored during resistance heating of small chips of the pure LTT alloys and during gas tungsten arc welding of simplified LTT welds using a specially designed welding rig for in-situ studies on the diffraction instruments. Under the mechanically unconstrained condition allowing free thermal expansion and shrinkage, the LTT alloys are found to exhibit decreasing transformation temperatures Ac and MS and increasing phase fraction of retained austenite for increasing Ni content. The strain evolution during welding reveals increased compressive stresses upon welding, which is attributed to the martensite formation upon cooling, which counteracts the thermal contraction strains. Comparison of the transformation temperatures reveals higher values than in the pure LTT alloys, but no variation between the different alloys. On the one hand, this is attributed to preferred grain orientation affecting the diffraction measurements and the determination of the transformation temperatures. On the other hand, it is possible that with the different chemical compositions of the LTT alloys and the mechanical constraints during welding, the evolution of the residual strain and stress may vary and result in counteracting affects with respect to lowered martensite start temperatures.
We discuss the stability of weld residual strain under static and quasi cyclic transverse tensile loading in the elastic and elastic–plastic region. The test welds were joined with low transformation temperature weld filler materials with 10 wt% Cr and varying Ni-content from 8 to 12 wt%. Using neutron diffraction the residual lattice strain in the martensitic α'- and austenitic γ-phase in the fusion zone as well as the ferritic α-phase in the heat affected zone and base metal as induced by welding, superimposed by stepwise tensile loading and after unloading was measured. The amount of retained austenite in the fusion zone increases with increasing Ni-content, but it decreases with increasing load level due to stress induced martensite formation. In the as-welded condition the transverse macroscopic residual lattice strain was found to be in low compression in the fusion zone in each weld, while the heat affected zone was in tension. Local plastic deformation of the γ-phase as a result of yielding during tensile loading in combination with the change in phase fraction resulted in increased macroscopic compression in the fusion zone. The reduced yield strength in the heat affected zone resulted in plastic deformation and a considerable shift into compression. Comparison with the cross weld distribution of the hardness and FWHM of the neutron diffraction interference lines supported the assumption of plastic deformation of the γ- and α-phase in the fusion and heat affected zone, respectively, while the α'-phase in the fusion zone was stressed within the elastic regime only. Microstructural observations as well as measurement of the local γ-phase fraction by means of laboratory X-ray diffraction in the fusion zone strengthen these observations.
Crack and fatigue resistance are relevant evaluation criteria for welded joints and are decreased by tensile residual
stresses resulting from the welding and cooling process, while compressive residual stresses can have a positive
influence on the characteristics mentioned. In order to generate compressive residual stresses, a set of post weld
treatment procedures is available, like shot peening, hammering, etc. These procedures have the disadvantage that
they are time and cost extensive and have to be applied after welding. As another point, such technologies can only
produce compressive stresses at the top surface, i.e. can only contribute to the reduction of the risk of cracks initiated
at the surface, like fatigue cracks. A chance to generate compressive stresses over the complete weld joint during the
welding procedure is offered by the so-called Low Transformation Temperature (LTT -) filler wires. Compared to
conventional wires, these materials show lower phase transformation temperatures, which can work against coolingrelated
tensile stresses, resulting from respective shrinkage restraint. In consequence, distinct compressive residual
stresses can be observed within the weld and adjacent areas. The strength of these fillers makes them potentially
applicable to high-strength steel welding. Welds produced with different LTT filler wires have shown different levels
and distributions of the resulting residual stresses depending on the specific transformation temperature. The
transformation temperatures are determined by temperature measurement. Classical X-ray diffraction as well as
diffraction methods using high energy synchrotron radiation have been used for residual stress analysis. By means of
high energy synchrotron diffraction in reflection mode residual stress depth gradients can be determined nondestructively.
The phase selective nature of the diffraction measurements enables the simultaneous determination of
the phase specific residual stresses of all contributing crystalline phases within one experiment. The application of
white beam diffraction implies recording of a multitude of diffraction lines within the energy range of the provided
energy spectrum of the white beam. By this means phase specific residual stress depth distributions up to distances of
150 ìm below the surface can be analysed for steel using the energy dispersive set-up of the HMI-beamline EDDI at
the Bessy site, Berlin, providing an energy range between 20-150 keV. As a side effect quantitative phase analysis can
be carried out using white energy dispersive diffraction e.g. the determination of the content of retained austenite in the
weld.
Zugeigenspannungen, wie sie beim Schweißprozess durch inhomogene Temperaturverteilungen und Schrumpfungen hervorgerufen werden, können die Lebensdauer geschweißter Verbindungen signifikant herabsetzen. Eine neue und außerordentlich attraktive Methode, um Druckeigenspannungen bereits während des Schweißens gezielt einzustellen, gelingt mit sogenannten LTT (Low Transformation Temperature)-Legierungen. LTT-Legierungen weisen eine martensitische Phasenumwandlung bei relativ niedrigen Temperaturen auf, wobei die damit verbundene Volumenexpansion zu einer Reduktion der Schrumpfeigenspannungen bzw. Erzeugung von Druckeigenspannungen führt. Zum direkten Nachweis der Phasenumwandlungen und der damit verbundenen resultierenden Schweißeigenspannungen wurden erstmals In-situ-Schweißexperimente unter Nutzung hoch energetischer, polychromatischer Synchrotronstrahlung (Weißstrahl) realisiert, um die Umwandlungskinetik während eines realen Schweißprozesses und die daraus resultierenden Schweißeigenspannungen zu analysieren. Es wird gezeigt, dass mit LTT-Legierungen signifikante Druckeigenspannungen in der Schweißnaht erreicht werden.
Welding residual stress is of major concern for structural integrity assessment in industrial components. Shear and volume strains resulting from the austenite-martensite-transformation affect the development of residual stress during welding. Controlling the phase transformation allows adjustment of the welding residual stress. Low transformation temperature (LTT) weld filler materials exhibiting reduced MS-temperatures allow postponing the phase transformation. The associated strain arising from the delayed transformation compensates for the thermal contraction strains and as such may reduce tensile or even introduce compressive residual stress. In this article we discuss the tri-axial residual stress distribution in 15 mm S690Q steel plates joined with LTT filler materials with 10 wt% Cr and a Ni-content that varies from 8 to 12 wt%. Using complementary synchrotron X-ray and neutron diffraction stress analysis the macroscopic residual stress was derived from the phase specific lattice strain and phase fraction of martensite and retained austenite, respectively. The local phase specific unstrained lattice parameters were determined using stress relieved combs. The investigation revealed increasing phase fraction of retained austenite with increasing Ni-content. Further, independent of the Ni-content in each weld in the fusion zone, significant compressive residual stresses were found in the longitudinal direction, which are balanced by tensile residual stresses in the heat affected zone (HAZ). In the weld transverse and normal direction the stress distribution is qualitatively similar but less in magnitude. The increased amount of retained austenite reduces the compressive stress arising from shear and volume strains during the delayed phase transformation and therefore no significant increase in compression was observed for decreasing MS-temperatures.
Mikrostruktur- und Härteentwicklung in Schweißnähten mit neuartigen LTT-Schweißzusatzwerkstoffen
(2013)
Various test methods are available for assessing the susceptibility of materials to solidification cracking during welding. In the widely used Varestraint test, the crack length is selected as a criterion as a function of the applied bending strain.
Unfortunately, the crack length does not characterize the material behavior alone but depends to varying degrees on the individual test parameters used, which makes the interpretation of the results difficult. In addition, the crack length is not comparable under different test conditions. To overcome these disadvantages, we have developed a novel evaluation methodology that decouples the machine influence from the material behavior. The measured crack length is related to the maximum possible value specified by welding speed and deformation time. This relative crack length is calculated numerically, considering the orientation of the cracks. Experiments on two high-alloy martensitic welding consumables show that, in contrast to the conventional evaluation, a comparison of different welding parameters becomes possible. Furthermore, the strain rate proved to be a suitable crack criterion in agreement with Prokhorov's hot cracking model.