Microstructure and wear behavior of improved NbC cermets for (BS-1452) grey cast iron machining
(2017)
Tungsten carbide (WC) and cobalt (Co) based cermets are the most successful commercial cermets beacuse of the good combination of physical, mechanical and behavioral properties. Niobium carbide (NbC) has good mechanical and physical properties, such as high hardness, very high melting point and low density. SPS refined the NbC grains and increased the hardness, while substitution of Co with Ni improved the fracture toughness.
The effects of rapid pulse electric current sintering (PECS), substitution of WC by NbC and Co by Ni, and carbide additives (TiC and Mo2C) on the microstructure, elastic modulus, B3B transverse rupture strength (TRS) and high temperature sliding wear on WC-Co, WC-Ni, NbC-Co and NbC-Ni cermets were studied. High temperature sliding wear tests were carried out using a ball-on-disk tribometer, with a 10 N force, at a sliding speed of 1.34 m/s for 0.8 km (10 min) and 2.4 km (30 min), using 100Cr6 (AISI 52100) steel balls at 400 °C and 0% humidity. Additions of TiC and Mo2C to NbC-12Ni improved the sliding wear resistance, with TiC having the greater effect, reducing the sample wear rate by over 30% from 15.1×10−6mm3/N·m to 9.4×10−6mm3/N·m after sliding distance of 2.4 km. Generally, the LPS samples had lower wear volumes than the corresponding SPS samples, due to higher K1c and TRS.