- nein (1)
Unpigmented HDPE jerrycans filled with nitric acid (55%) and water respectively had been exposed to outdoor conditions for one Berlin summer season. As both liquids underwent equal temperature progression, exposure effects of UV radiation and nitric acid as well as of their combination can be separated and compared. On the basis of various property changes after these exposures, synergistic action is evaluated and compared to a damaged Intermediate Bulk Container (IBC) from a transport accident.
It is found that carbonyl formation goes along with lightness increase in color measurement due to microcracking and with a worsening in mechanical behavior, all of them showing synergistic effects of UV and nitric acid exposure. In contrast, embedding nitrogen compounds goes along with yellowing of the material but cannot be correlated to oxidation.
The reason for intensified damaging is the decomposition of the 55-percent nitric acid and formation of nitrogen oxides even at ambient temperatures, caused by UV radiation. Thus, damaging effects become similar to those caused by fuming nitric acid exposure at temperatures above 60 °C, with the result of strong oxidative degradation of the polyethylene.
In contrast, exclusive exposure to the 55-percent nitric acid at 40 °C does not cause any failure.
It can therefore be assumed that also the damaged IBC had been exposed to both UV radiation and nitric acid, probably outdoors.
Häufig ist es wünschenswert, für neue Materialien oder Anwendungen künstliche Bewitterungsverfahren zu benutzen, die auf die spezifischen Anforderungen besser zugeschnitten sind, als es bei bestehenden standardisierten Verfahren der Fall ist. Nachdem man die spezifischen Parameter der Beanspruchung unter Anwendungsbedingungen und die spezifische Empfindlichkeit des Materials erfasst hat, beginnt ein Prozess, der als „Test Tailoring“ häufig abstrakt verwendet, auf den aber nur selten näher eingegangen wird. Genau dieser Prozess soll hier am Beispiel der Entwicklung eines künstlichen Bewitterungstests unter saurer Beaufschlagung, dem in der BAM entwickelten Acid Dew and Fog Test, beispielhaft erläutert werden.