Stress-induced damage evolution in cast AlSi12CuMgNi alloy with one- and two ceramic reinforcements
(2017)
Two composites, consisting of an as-cast AlSi12CuMgNi alloy reinforced with 15%vol. Al2O3 short fibres and with 7%vol. Al2O3 short fibres + 15%vol. SiC particles were studied. Synchrotron computed tomography disclosed distribution, orientation, and volume fraction of the different phases. In-situ compression tests during neutron diffraction in direction parallel to the fibres plane revealed the load partition between phases. Internal damage (fragmentation) of the Si phase and Al2O3 fibres was directly observed in CT reconstructions. Significant debonding between Al-matrix and SiC particles was also found. Finally, based on the Maxwell scheme, a micro-mechanical model was utilized for the new composite with two ceramic reinforcements; it rationalizes the experimental data, and predicts the evolution of all internal stress components in each phase.
The evolution of the internal strains during in situ tension and compression tests has been
measured in an MgY2Zn1 alloy containing long-period stacking ordered (LPSO) phase using
neutron diffraction. The alloy was extruded at two different temperatures to study the influence
of the microstructure and texture of the magnesium and the LPSO phases on the deformation
mechanisms. The alloy extruded at 623 K (350 °C) exhibits a strong fiber texture with the basal
plane parallel to the extrusion direction due to the presence of areas of coarse non-recrystallised
grains. However, at 723 K (450 °C), the magnesium phase is fully recrystallised with grains
randomly oriented. On the other hand, at the two extrusion temperatures, the LPSO phase
orients their basal plane parallel to the extrusion direction. Yield stress is always slightly higher
in compression than in tension. Independently on the stress sign and the extrusion temperature,
the beginning of plasticity is controlled by the activation of the basal slip system in the dynamic
recrystallized grains. Therefore, the elongated fiber-shaped LPSO phase which behaves as the
reinforcement in a metal matrix composite is responsible for this tension–compression asymmetry.