Filtern
Dokumenttyp
- Zeitschriftenartikel (8)
- Vortrag (3)
- Beitrag zu einem Tagungsband (1)
- Posterpräsentation (1)
Schlagworte
- Foam (5)
- Polyurethane (5)
- Cone calorimeter (4)
- Flame retardant (4)
- Fire behaviour (3)
- Fire behavior (2)
- Flammability (2)
- Polyisocyanurate (2)
- 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide; DOPO (1)
- Burning behavior (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (3)
The concreting of prefabricated concrete structures can lead to insufficient bonding or even to remaining cavities. Honeycombs (aggregate clusters without cement) represent potential weakening of the structure and need to be detected non-destructively. In our study we tested the capability of ground penetrating radar (GPR)techniques for this purpose. We applied GPR in reflection mode and zero-offset profiling (ZOP) Transmission mode on a precast concrete twin wall with built-in honeycombs. GPR measurements were performed as twochannel measurement with ground coupled antennas with centre frequencies of 1.5 GHz and 2.6 GHz mounted to an automated scanner system.
Our findings show that ZOP transmission measurements are a more efficient method to detect voids in reinforced concrete structures compared to reflection mode measurements. This holds for both the effort needed for the measurement and the evaluation as well as the validity of the data. Honeycombs (basically representing voids) are usually characterized by strongly reduced amplitudes and earlier arrivals of the transmitted wave.
Polyurethanes (PU) represent one of the most versatile classes of plastics. They are processed and used as thermoplastic, elastomer, and thermoset. The requirements regarding flammability are correspondingly versatile. Depending on the material and the field of application, specific fire tests have to be fulfilled. This paper describes the different concepts used to fulfil these requirements by choosing the right raw materials and flame retardants.
Polyurethane (PU) bilden eine der vielseitigsten Klassen der Polymerwerkstoffe. Kein anderer Kunststoff wird sowohl als Thermoplast, als Elastomer wie auch als Duroplast verarbeitet und eingesetzt. Entsprechend vielfältig sind auch die Anforderungen an den Flammschutz. Je nach Material und Anwendung müssen spezifische Brandnormen erfüllt werden. Der vorliegende Aufsatz gibt einen Überblick über die verfügbaren Ansätze, um durch geeignete Auswahl der Rohstoffe und der Flammschutzmittel diese verschiedensten Anforderungen an das Brandverhalten zu erfüllen.
The impact of phosphorus-containing flame retardants (FR) on rigid polyisocyanurate (PIR) foams is studied by systematic variation of the chemical structure of the FR, including non-NCO-reactive and NCO-reactive dibenzo[d,f][1,3,2]dioxaphosphepine 6-oxide (BPPO)- and 9,10 dihydro-9-oxa-10 phosphaphenanthrene-10-oxide (DOPO)-containing compounds, among them a number of compounds not reported so far. These PIR foams are compared with PIR foams without FR and with standard FRs with respect to foam properties, thermal decomposition, and fire behavior. Although BPPO and DOPO differ by just one oxygen atom, the impact on the FR properties is very significant: when the FR is a filler or a dangling (dead) end in the PIR polymer network, DOPO is more effective than BPPO. When the FR is a subunit of a diol and it is fully incorporated in the PIR network, BPPO delivers superior results.
A series of new flame retardants (FR) based on dibenzo[d,f][1,3,2]dioxaphosphepine 6-oxide (BPPO) incorporating acrylates and benzoquinone were developed previously. In this study, we examine the fire behavior of the new flame retardants in polyisocyanurate (PIR) foams. The foam characteristics, thermal decomposition, and fire behavior are investigated. The fire properties of the foams containing BPPO-based derivatives were found to depend on the chemical structure of the substituents. We also compare our results to state-of-the-art non-halogenated FR such as triphenylphosphate and chemically similar phosphinate, i.e. 9,10-dihydro-9-oxa-10- phosphaphenanthrene-10-oxide (DOPO), based derivatives to discuss the role of the phosphorus oxidation state.
Rigid polyurethane foams (RPUFs) exhibit short times to ignition as well as rapid flame spread and are therefore considered to be hazardous materials. This paper focuses on the fire phenomena of RPUFs, which were investigated through a multimethodological approach. Water-blown polyurethane (PUR) foams without flame retardants (FRs) as well as waterblown PUR foams containing triethyl phosphate as a gas phase-active FR were examined. The aim of this study is to clarify the influence of the FR on the fire phenomena during combustion of the foams. Additionally, materials’ densitieswere varied to range from 30 to 100 kg/m3. Thermophysical properties were studied bymeans of thermogravimetry; fire behavior and flammability were investigated via cone calorimeter and limiting Oxygen index, respectively. During the cone calorimeter test, the temperature development inside the burning specimens was monitored with thermocouples, and cross sections of quenched specimens were examined visually, giving insight into the morphological changes during combustion.
The present paper delivers a comprehensive study, illuminating phenomena occurring during foam combustion and the influence of a FR active in the gas phase. The superior fire performance of flameretarded PUR foams was found to be based on flame inhibition, and on increased char yield leading to a more effective protective layer. It was proven that in-depth absorption of radiation is a significant factor for estimation of time to ignition. Cross sections investigated with the electron scanning microscope exhibited a pyrolysis front with an intact foam structure underneath. The measurement of temperature development inside burning specimens implied a shift of burning behavior towards that of non-cellular materials with rising foam density.
Rigid polyurethane foams (RPUFs) typically exhibit low thermal inertia, resulting in short ignition times and rapid flame spread. In this study, the fire phenomena of RPUFs were investigated using a multi-methodological approach to gain detailed insight into the fire behaviour of pentaneand water-blown polyurethane (PUR) as well as pentane-blown polyisocyanurate Polyurethane (PIR) foams with densities ranging from 30 to 100 kg/m3. Thermophysical properties were studied using thermogravimetry (TG); flammability and fire behaviour were investigated by means of the limiting oxygen index (LOI) and a cone calorimeter. Temperature development in burning cone calorimeter specimens was monitored with thermocouples inside the foam samples and visual investigation of quenched specimens’ cross sections gave insight into the morphological changes during burning. A comprehensive investigation is presented, illuminating the processes taking place during foam combustion. Cone calorimeter tests revealed that in-depth absorption of radiation is a significant factor in estimating the time to ignition. Cross sections examined with an electron scanning microscope (SEM) revealed a pyrolysis front with an intact foam structure underneath, and temperature measurement inside burning specimens indicated that, as foam density increased, their burning behaviour shifted towards that of solid materials. The superior fire performance of PIR foams was found to be based on the cellular structure, which is retained in the residue to some extent.
Flexible polyurethane foams (FPUF) are easy to ignite and exhibit rapid flame spread. In this paper, the fire phenomena of two standard foam formulations containing tris (1,3-dichloro-2-propyl) phosphate (FR-2) and a halogen-freepoly (ethyl ethylene phosphate) (PNX), respectively, as flame retardants are compared. A multimethodological approach is proposed which combines standard fire tests as well as new investigatory approaches. The thermophysical properties of the foams were determined by thermogravimetric analysis (TG), reaction to small flames was studied by means of the limiting oxygen index (LOI) and UL 94 HBF test, and the burning behavior was investigated with the cone calorimeter. Further, temperature development in burning cone calorimeter samples was monitored using thermocouples, and rheological measurements were performed on pyrolyzed material, delivering insight
into the dripping behavior of the foams. This paper gives comprehensive insight into the fire phenomena of flame-retarded FPUFs that are driven by the two-step decomposition behavior of the foams. LOI and UL 94 HBF tests showed a reduced flammability and reduced tendency to drip for the flame-retarded foams. TG and cone calorimeter measurements revealed that the two-step decomposition behavior causes two stages during combustion, namely structural collapse and pool fire. The flame-retardant mode of action was identified to take place primarily during the foam collapse and be based mainly on flame inhibition. However, some condensed-phase action was been measured, leading to significantly increased melt viscosity and improved dripping behavior for foams containing PNX.
This work investigates the fire phenomena of rigid polyurethane foams (RPUFs) in detail. To elucidate structure-property relationships, systematically varied sets of materials were prepared covering polyurethane, polyisocyanurate-polyurethane and flame retarded polyurethane foams. Advanced cone calorimeter investigations provide insight into the fire behavior under forced flaming conditions. Thermocouples inside specimens give information about the temperature gradient during combustion. Furthermore, fire phenomena were characterized using cross sections of quenched samples and the scanning electron microscope. By using a Multi methodological approach and systematically varied sets of foam materials, new insights into the burning of RPUFs were won. For the flame retarded foams, the dominant flame retardant mode of action changed with density. PIR foams exhibited a cellular structure in the residue leading to the superior fire performance compared to polyurethane foams. The understanding of fire phenomena contributes to future development of tailored flame retardant strategies for RPUFs.
This work investigates the fire phenomena of rigid polyurethane foams (RPUF) in detail. To elucidate structure-property relationships systematically varied sets of foams were prepared. RPUF were synthesized with different densities using water and pentane as blowing agent. What is more, a flame retarded RPUF and rigid polyisocyanurate-polyurethane foams were examined. The comprehensive understanding of the processes taking place during combustion is the foundation of customized development of successful flame retardant approaches.
Advanced cone calorimeter investigations provide insight into the fire behavior under forced flaming conditions. Thermocouples in the inside of specimens give information about the temperature gradient and temperature of the pyrolysis zone during combustion. Furthermore, fire phenomena were characterized using SEM, LOI and thermal analysis. By using a multi-methodological approach and systematically varied sets of foam materials, new insights into the burning of RPUF were won. The detailed knowledge of fire phenomena is essential for future development of tailored flame retardant strategies for RPUF.