The present paper investigates the electromagnetic porosity reduction in partial penetration laser beam welding of 6 mm aluminum die casting AlSi9MnMg. Applying an electromagnetic field, a significant reduction of the porosity as well as smoothing of the surface of aluminum die casting can be observed. Starting from the reference case without an electromagnetic support, the porosity was reduced by 76 %. Especially big pores can be removed from the weld pool effectively due to their beneficial volume-to-area ratio whereas very small metallurgical pores tend to remain within the weld pool even when higher magnetic flux densities are applied.
The present paper investigates the electromagnetic porosity reduction in partial penetration laser beam welding of 6 mm aluminum die casting AlSi9MnMg. Applying an electromagnetic field, a significant reduction of the porosity as well as smoothing of the surface of aluminum die casting can be observed. Starting from the reference case without an electromagnetic support, the porosity was reduced by 76 %. Especially big pores can be removed from the weld pool effectively due to their beneficial volume-to-area ratio whereas very small metallurgical pores tend to remain within the weld pool even when higher magnetic flux densities are applied.
Elektromagnetische Porenreduktion beim Laserstrahlschweißen von Aluminium-Druckgusslegierungen
(2017)
- Erfolgreiche Porenreduktion beim Laserstrahlschweißen von Aluminium-Druckguss unter EM-Einfluss von bis zu 75 % Flächenanteil
- Entfernung von großvolumiger Poren aus dem Schmelzbad
- Einige kleine metallurgische Poren verbleiben im Schmelzbad aufgrund des Volumen-Flächenverhältnisses
- Restporosität ist abhängig vom Ausgangsgasgehalt im Grundmaterial
The paper describes an experimental investigation of the electromagnetic porosity reduction in partial penetration laser beam welding of 6 mm thick aluminum die casting AlSi9MnMg. The Investigation reveals that the usage of an electromagnetic field leads to a significant reduction of the porosity as well as to a surface smoothing of aluminum die casting. Based on the reference case without an electromagnetic influence, the porosity area was reduced gradually up to 76%.
Metallurgical pores as well as process pores were removed from the weld pool. Also the weld reinforcement was improved up to 78%. Best results were reached with a frequency of 4325 Hz and a magnetic flux density of 348 mT. Although a complete prevention of porosity was not achieved, the best weld seam reached a high quality and can be ranked in valuation group B of DIN EN ISO 13919-2:2001–12.
- EM-Schmelzbadunterstützung auch auf ferromagnetische Werkstoffe übertragbar
- Erfolgreiche Kompensation des hydrostatischen Drucks von bis zu 20 mm dicken Werkstücken aus Duplex- und Baustahl
- Anwendung von EM-Schmelzbadstütze auf Laserhybridschweißen
Einfluss von oszillierendem Magnetfeld auf Lichtbogen vernachlässigbar
- Erfolgreiche Kompensation beim Schweißen von bis zu 20 mm dicken Baustählen mit Y-Nahtvorbereitung
Die experimentellen Untersuchungen innerhalb dieses Berichtes zeigen die erfolgreiche Anwendung einer elektromagnetischen Schmelzbadstütze beim Laser-strahl(hybrid)schweißen von ferromagnetischen Stäh-len mit einer Werkstückdicke von bis zu 20 mm. Bis-lang wurde dieses System zur Kompensation des hydrostatischen Druckes von Aluminiumlegierungen und austenitischen Stählen eingesetzt. Zunächst wur-den die Versuche an Duplexstählen vorgenommen, die jeweils zur Hälfte aus Austenit und Ferrit bestehen. Im Anschluss daran wurden die Versuche auf bis zu 20 mm dicke Werkstücke aus Baustahl erweitert. In-nerhalb der Versuchsreihen wurden die AC-Leistung sowie die Oszillationsfrequenz variiert. Für Werk-stückdicken von 15 mm war eine AC-Leistung von ca. 1 kW notwendig, um die Wurzelüberhöhung in die Bewertungsgruppe B der für laserstrahlgeschweißten Stähle gültigen DIN EN ISO 13919-1:1996-09 einord-nen zu können. Mit zunehmender AC-Leistung wird die Wurzelüberhöhung sukzessive reduziert. Nach erfolg-reicher Erweiterung auf ferromagnetische Werkstoffe wurde die Anwendung der Technologie für das Laser-strahlhybridschweißen demonstriert, indem praxisrele-vante Y-Nähte an 20 mm dicken Baustählen ohne Wurzelüberhöhung einlagig in Wannenlage geschweißt wurden. Trotz der Beeinflussung des Lichtbogens durch das oszillierende Magnetfeld sowie des zusätz-lich zum hydrostatischen Druck zu berücksichtigenden Lichtbogendruckes wurde eine ideale Kompensation auf der Wurzelseite erzielt.
Die Erweiterung des Anwendungsspektrums der elekt-romagnetischen Schmelzbadstütze auf ferromagneti-sche Werkstoffe sowie auf das Laserstrahlhybrid-schweißen eröffnet für zukünftige industrielle Anwen-dungen ein großes Potenzial. Das einlagige Schwei-ßen dickwandiger Bauteile mittels Hochleistungslasern wird in Kombination mit der elektromagnetischen Schmelzbadstütze attraktiver. In nachfolgenden Un-tersuchungen wird der Einsatz der elektromagneti-schen Schmelzbadstütze beim Laserstrahlhybrid-schweißen von Pipelinestählen angestrebt, v. a. im Hinblick auf die Spaltüberbrückbarkeit und der me-chanisch-technologischen Eigenschaften der Schweißverbindungen. Zudem ist beim Schweißen von Duplexstählen der Einsatz von Zusatzwerkstoffen zu berücksichtigen, um das Gleichgewicht zwischen austenitischer und ferritischer Phasen zu stabilisieren.
Hybrid laser-arc welding of thick-walled ferromagnetic steels with electromagnetic weld pool support
(2018)
The hybrid laser-arc welding (HLAW) process provides many advantages over laser welding and arc welding alone, such as high welding speed, gap bridgeability, and deep penetration. The developments in hybrid laser-arc welding technology using modern high-power lasers allow single-pass welding of thick materials. This technology can be used for the heavy metal industries such as shipbuilding, power plant fabrication, and line-pipe manufacturing. The obvious problem for single-pass welding is the growth of the hydrostatic pressure with increasing thickness of materials leading to drop-out of molten metal. This phenomenon is aggravated at slow welding velocities because of increasing weld seam width followed by a decrease of Laplace pressure compensating the hydrostatic pressure. Therefore, weld pool support is necessary by welding of thick materials with slow welding velocities. The innovative electromagnetic weld pool support system is contactless and has been used successfully for laser beam welding of aluminum alloys and austenitic and ferromagnetic steels. The support system is based on generating Lorentz forces within the weld pool. These are produced by an oscillating magnetic field orientated perpendicular to the welding direction. The electromagnetic weld pool support facilitates a decrease in the welding speed without a sagging and drop-out of the melt thus eliminating the limitations of weldable material thickness.
The hybrid laser arc welding (HLAW) process provides many advantages such as improved gap bridgeability, deep penetration and misalignment of edges, that is why the process is used increasingly in industrial applications e.g. shipbuilding, power plant industry and line-pipe manufacturing. The obvious encountered problem for single pass welding in flat position is the gravity drop-out at low welding velocities. With the usage of an electromagnetic weld pool support system, which is based on generating Lorentz forces within the weld pool, wide seams followed by reduced welding velocities could be achieved in this study leading to the realization of a gap bridgeability up to 1 mm, misalignment of edges up to 2 mm and a single pass weld up to 28 mm thickness with a 20-kW fibre laser. These developments expand the boundaries of the HLAW process for different industrial applications. As a result, less accurate preparation of the edges would be sufficient, which saves time for manufacturing.
EM-Schmelzbadunterstützung auch auf ferromagnetische Werkstoffe übertragbar
Erfolgreiche Kompensation des hydrostatischen Drucks von bis zu 20 mm dicken Werkstücken aus Duplex- und Baustahl
Erfolgreiche Porenreduktion beim Laserstrahlschweißen von Aluminium-Druckguss unter EM-Einfluss von bis zu 75 % Flächenanteil
Entfernung von großvolumigen Poren aus dem Schmelzbad
Einige kleine metallurgische Poren verbleiben im Schmelzbad aufgrund des Volumen-Flächenverhältnisses
Restporosität ist abhängig vom Ausgangsgasgehalt im Grundmaterial
Elektromagnetische Porenreduktion beim Laserstrahlschweißen von Aluminium-Druckgusslegierungen
(2019)
Innerhalb der vorliegenden Untersuchung wurde ein elektromagnetisches Schmelzbadbeeinflussungssys-tem zur Reduktion des Porenanteils beim Laserstrahlschweißen von Aluminium-Druckguss verwendet. Hierbei wird der Unterschied der elektrischen Leitfähigkeiten zwischen Gas- bzw. Lufteinschlüssen und geschmolzenem Aluminium gezielt genutzt, um die im Schmelzbad eingeschlossenen Poren während des Laserstrahlprozesses zur Oberfläche zu verdrängen. Die dafür erforderlichen Lorentzkräfte werden durch ein oszillierendes Magnetfeld erzeugt. Bei den Laserstrahlschweißversuchen handelt es sich um Ein-schweißungen in Wannenlage (PA-Position) von 6 mm dickem Aluminium-Druckguss AC-AlSi9MnMg. Über einen zuvor optimierten Laserschweißprozess wurde durch zusätzlichen Einsatz eines elektromag-netischen Feldes dessen Wirkung hinsichtlich des Porengehaltes und der Oberflächenrauheit untersucht. Die Auswertung der Schweißnähte erfolgte anhand von Querschliffaufnahmen, Röntgenbildern sowie Computer-Tomographie (CT) Aufnahmen. In Abhängigkeit von der verwendeten magnetischen Fluss-dichte konnte eine Reduktion des Porenanteils von bis zu 75 % erzielt werden, wobei vor allem großvolu-mige Poren erfolgreich aus dem Schmelzbad entfernt werden konnten. Zudem konnte eine Reduktion der Oberflächenrauigkeit von ebenfalls bis zu 75 % erreicht werden.