Polymer deposition morphology by electrospray deposition - Modifications through distance variation
(2014)
Electrospray deposition (ESD) of highly diluted polymers was examined with regard to the deposited surface structure. Only the flight distance (flight time) onto the resulting deposited surface was varied from 20 to 200 mm.
An apparatus without any additional heating or gas flows was used. Polyacrylic acid (PAA) and polyallylamine (PAAm) in methanol were deposited on Si wafers. The polymer layers were characterized by scanning electron microscopy, X-ray photoelectron spectroscopy, derivatization reactions and Fourier transform infrared spectroscopy using a grazing incidence unit.
SEM images illustrated the changing structures of PAA and PAAm. For PAA the deposited structure changed from a smooth film (20 mm) to a film with individual droplets on the coated surface (100 mm and 200 mm), while for PAAm individual droplets can be seen at all distances. The ESD process with cascades of splitting droplets slows down for PAA after distances greater than 40 mm. In contrast, the ESD process for PAAm is nearly stopped within the first flight distance of 20 mm. Residual solvent analysis showed that most of the solvent evaporated within the first 20 mm capillary-sample distance.
Substrate-induced self-assembly of donor-acceptor type compounds with terminal thiocarbonyl groups
(2013)
Two types of conjugated thiocarbonyl-terminated compounds have been synthesized and their ability to be adsorbed on surfaces of the different nature, namely, glass, polytetrafluoroethylene (PTFE), and gold has been studied. Different morphology of the films prepared by thermal vacuum evaporation and drop-casting from solutions has been observed depending on the surface used. It has been found that gold surface has a unique property to influence self-assembly of both monolayer and larger aggregates or crystals of the compounds, in contrast to glass and PTFE substrates. It was found that thiocarbonyl group is able to be chemisorbed to the gold surface. However, it was concluded that in spite of the fact that the thiocarbonyl groups are important for the chemical interaction with the gold surface, physical adsorption on the substrate surface, compoundcompound and compound–solvent (when using solution) interactions are of great significance to drive self-assembly of the final film.
Degradation behavior of thin polystyrene films on exposure to Ar plasma and its emitted radiation
(2013)
Spin-coated films of amorphous polystyrene (PS) were exposed to argon plasma for a few seconds to several minutes. The PS film was either in direct contact with the plasma or was shielded from the direct plasma contact by filters with different cutoff wavelengths in the vacuum UV region or by a Faraday cage (FC) made from metal mesh to prevent the impinging of charged species. Only energy-rich neutrals and plasma radiation may be operative in presence of the FC. lithium fluoride (LiF) filter protects the sample from direct contact with the plasma. Wavelengths of plasma radiation shorter than c. 105 nm (≈ 11.8 eV) were cut off. Glass filters made of fused SiO2 have a cutoff at λ ≈175?nm completely the vacuum UV radiation of plasma (ca. 175 nm ≈ 7.0 eV). These energies are sufficient to produce C–C, C–H bond scissions in case of direct Ar plasma exposure and Ar plasma exposure with use of the LiF filter. Only quartz glass shielding did not produce significant effects on the polymer surface in comparison to the reference PS, either in surface energy or O/C ratio or in IR spectra. Oxygen plasma has worked most aggressive and had etched the PS film, thus establishing a steady state between introduction of new oxygen functionalities and polymer etching. Ar plasma exposure produces also oxidation and etching of the polymer films as the oxygen plasma. Using of a FC during Ar plasma exposure or the LiF filter a slightly weaker oxidation was observed.
Copolymers of acrylic acid and styrene (AA/S) were prepared by pulsed plasma deposition and their structures were studied in dependence on the duty cycle (DC) for a fixed composition of 1:1. As a result, low values of DC doses preserve the structure of monomers in the plasma deposited polymers while high DC leads to a higher degree of fragmentation and a loss in regular structure. Regarding plasma copolymerisation as a feasible method to finish surfaces with a definite number of functional groups it is necessary to characterize both, the chemical nature and the physical properties of the deposited layer. Therefore, a combination of different methods was employed for the characterization of thin plasma copolymer films (FTIR, dielectric spectroscopy, differential scanning calorimetry, X-ray photoelectron spectroscopy (XPS)). Special attention was paid on the unambiguous identification of COOH groups at the surface after derivatization with trifluoroethanol by XPS and in the volume by FTIR. The glass transition temperature of the copolymer system is lower than that for the both plasma deposited homopolymers and increases with the DC in difference to plasma deposited poly(acrylic acid). The dielectric measurements showed that the plasma deposited films were not thermally stable and underwent an undesired post-plasma chemical reaction. The results obtained by dielectric spectroscopy are discussed in detail in comparison with the data from FTIR and XPS measurements.
Polystyrene (PS) spin coated thin films were modified by O2 and Ar plasma as
well as by UV irradiation treatments. The modified PS samples were compared with
plasma polymerized and commercial polystyrene. The effects of plasma (O2 and Ar) and
UV irradiation treatments on the surface and the bulk properties of the polymer layers were
discussed. The surface properties were evaluated by X-ray Photoelectron Spectroscopy and
Contact angle measurements and the bulk properties were investigated by FTIR and
dielectric relaxation spectroscopy. As a result only one second treatment time was sufficient
to modify the surface. However, this study was also dedicated to understand the effect
of plasma and plasma irradiation on the deposited layers of plasma polymers. The
dielectric measurements showed that the plasma deposited films were not thermally stable
and underwent an undesired post-plasma chemical oxidation.
Copolymers of acrylic acid and styrene (AA/S) were prepared by pulsed plasma deposition technique. Their structure–property relationships were studied in dependence on the comonomer ratio. Both, the regularity of the structure and the composition of the thin copolymer films were investigated by bulk-sensitive (dielectric spectroscopy, FTIR, and differential scanning calorimetry) as well as surface-sensitive methods such as X-ray photoelectron spectroscopy (XPS). For an unambiguous identification of the functionality of the deposited films the COOH groups were estimated by derivatization with trifluoroethanol and subsequent XPS measurement as well as by the quantitative analysis of the FTIR data. As a result, the concentration of COOH groups on the surface and in the bulk is increasing with the fraction of AA in precursor mixture in a non-monotonous way but similar to the dependence obtained by conventional free radical polymerization.
Poly(acrylic acid) films with a thickness of about 150?nm were deposited using a pulsed plasma onto aluminum and glass. The structure/property relationships of these samples were studied in dependence to the duty cycle (DC) of the plasma by a broad combination of different techniques and probes. For the first time, volume sensitive methods (FTIR, dielectric spectroscopy, and differential scanning calorimetry) are combined with surface analyses i.e. XPS. For an unambiguous identification of COOH groups by XPS, derivatization with trifluoroethanol was accomplished. Quantitative FTIR investigations give qualitatively a dependence of the concentration of COOH groups upon DC similar to that given by XPS investigations. The observed differences are discussed considering the different analytical depths of both methods. The dielectric measurements reveal that the structure of the plasma deposited films is different from that of the bulk material. Moreover, these measurements show also that the plasma deposited films are not thermally stable but undergo a post plasma chemical reaction during heating, where the reaction kinetics depends on DC.
Poly(allyl alcohol) films with a thickness of about 150 nm were deposited by pulse plasma polymerization onto different substrates (inorganic and organic). The structure/property relationships of these samples were studied in dependence on the duty cycle (DC) of the plasma by a broad combination of different techniques and probes. For the first time volume sensitive methods (FTIR and dielectric spectroscopy) are combined with surface analytics by employing XPS for that system. FTIR spectroscopy gives qualitatively the same dependence of the concentration of the OH groups on DC like XPS.
The observed differences are discussed considering the different analytical depths of both the methods. The dielectric measurements show that the plasma deposited films are not thermally stable but undergo a post plasma chemical reaction during heating. The results obtained by dielectric spectroscopy are discussed in detail with the data from FTIR and XPS measurements.
The pulsed plasma polymerization of allyl alcohol was employed under the aspect of maximal retention of OH groups and the formation of a regular polymer structure. It should be noted that earlier investigations on plasma polymers deposited from allyl alcohol did not show extensive postplasma addition of oxygen and water vapor from ambient air during storage, measuring the elemental O/C ratio by means of X-ray photoelectron spectroscopy (XPS).The identification of OH groups in the plasma polymerized polymer using FTIR spectroscopy was such an indicator for fragmentation. The peak area of OH groups in the film which was stored was increased by about 20% compared to that measured ('in situ'). These phenomenons reflected that moisture and O2 in air played an important role in scavenging the free radicals. The addition of water and more specifically chemical bonding of OH of water in the deposited plasma polymer may serve as an indicator for monomer fragmentation, poly recombination, and the remaining radicals responsible for film formation. Moreover, the dielectric measurements show that the plasma deposited films are not thermally stable but undergo a postplasma chemical reaction during heating, where the reaction kinetics depends on pressure.
Chemical heterogeneities and molecular weight distributions of poly(ethylene oxide) (PEO)-co-polymethylene (PM) model oligomers, which are relevant to the synthesis of commonly used tensides, were investigated. For analytical characterization, the well-known principle of liquid adsorption chromatography at 'critical conditions' (LACCC) was modified. Near the critical conditions of adsorption of the PEO unit, e.g., at slight adsorption conditions of PM, the copolymers could be separated according to their PM chain length. The eluates were separated and single fractions of each peak were continuously transferred onto the MALDI target by means of a commercially available device. Simultaneously, the MALDI matrix solution was continuously added with a second pump. This procedure offers the possibility of the formation of homogeneous matrix-polymer textures. By MALDI-MS a complete characterization of the chemical composition (PEO and PM chain length) of each peak could be achieved. The obtained MALDI mass spectra of the eluates at different retention times could be used for the molecular weight calibration of the LAC system. In this way, an additional application of SEC, as in conventional 2D-chromatography, was avoided by using the MALDI method as quasi chromatographic separation
The adhesion of thick poly(allylamine)-polyphosphate layers (1 µm) deposited by the wet-chemical layer-by-layer technique (LbL) onto polyethylene or polystyrene (each 100 µm) was very low. To promote the adhesion of these LbL layers the polyolefin substrates were oxidized at the surface by short exposure to the oxygen plasma (2 or 5 s) and subsequently coated with an interlayer of plasma-deposited poly(allylamine) or poly(allyl alcohol) (100 nm). The plasma polymer interlayers have improved strongly the adhesion between polyolefin substrates and polyphosphate coatings. Such phosphate coatings are interesting for life sciences (nucleotide formation) but also for fire retardancy in combination with N-rich compounds such as melamine.
The intention was to prefer chemical and hydrogen bonds for adhesion promoting because of their high binding energy. Therefore, the introduced oxygen-containing groups at the polyolefin surface could interact with the OH or NH2 groups of the adhesion-promoting plasma polymer interlayer. These groups were also able to interact strongly with the poly(allylamine)-polyphosphate topcoating.
The coated polyolefins were investigated using Fourier Transform Infrared Spectroscopy in Attenuated Total Reflectance mode (FTIR-ATR), X-ray Photoelectron Spectroscopy (XPS), Thermo-Gravimetric Analyses (TGA) and Atomic Force Spectroscopy (AFM) and 90° peel test.
Several reaction mechanisms have been proposed for the formation of plasma polymers, such as monomer fragmentation followed by poly-recombination into randomly structured and crosslinked films; fragmentation, accompanied by the formation of acetylene or other film-forming intermediates and deposition of polystyrene-like material; plasma-initiation of a radical chain-growth polymerization; and ion-molecule reactions, as well as ionic chain-growth polymerization. The bulk structure of plasma polymers is completely irregular, far from that of conventional polymers. The retention of functional groups during plasma polymerization tends to be greater than that of the entire monomer structure found again as an intact repeat unit in the resulting plasma polymer. An alternative method for depositing ultra-thin, pin-hole free coatings, ones that possess regular structures, is by electrospray ionization (ESI) of pre-fabricated polymers.
Plasma-chemical bromination applied to graphitic materials, in particular to highly ordered pyrolytic graphite is reviewed. The resulting bromination efficiency of the plasma-chemical treatment was subject of systematic process optimization. The plasma of elemental bromine vapour produced bromine concentrations on graphene surfaces of more than 30 % Br/C using either inductively or capacitively coupled low-pressure radio-frequency plasmas. Plasma brominated graphite surfaces have been studied by Near Edge X-ray Absorption Fine Structure, X-ray Photoelectron Spectroscopy, Atomic Force Microscopy and Scanning Electron Microscopy. The introduction of bromine into graphene-like graphite layers and its binding situation were investigated. To study the physical effect of the plasma bromination process, Kr plasma was also used because of its chemical inertness but similar atomic mass. Covering the samples with a Faraday cage or with a LiF window should help to differentiate between physical, chemical and radiation effects of the plasma. Bromination was assigned to radical or electrophilic addition of bromine onto fully substituted aromatic double bonds (sp² C) with exothermal reaction enthalpy. Low bromination shows a strong decay of aromatic double bonds, higher bromination percentage let disappear all aromatic rings. The formed C–Br bonds were well suited for efficient grafting of organic molecules by post-plasma wet-chemical nucleophilic substitution. This grafting onto the graphene surface was demonstrated using aminosilane and different diamines. The bromination of double bonds changes the hybridization of carbon atoms from plane sp² to tetrahedral sp³ hybridization. Thus, the plane topography of graphene is destroyed and the conductivity is lost.
The retention of chemical structure and functional groups during pulsed plasma polymerization was used for producing adhesion-promoting plasma polymer layers with high concentrations of exclusively one kind of functional groups, such as OH, NH2, or COOH. The maximum content of functional groups was 31 OH using allyl alcohol, 18 NH2 using allylamine, or 24 COOH per 100 C atoms using acrylic acid. To vary the density of functional groups, chemical co-polymerization with ethylene as 'chain-extending' co-monomer, or butadiene as 'chemical crosslinker' was initiated in the pulsed plasma. The composition of these co-polymers was investigated by XPS and IR spectroscopy. The concentrations of functional groups were measured by derivatizing with fluorine-containing reagents and using XPS. A set of plasma parameters was found to be a good compromise between a high number of functional groups and complete insolubility in water, ethanol or THF,which is needed for further chemical processing. Here, these monotype-functionalized surfaces were used in metal-polymer systems as adhesion-promoting interlayers to examine the influence of type and density of functional groups on adhesion. As expected, COOH- and OH-group-terminated interlayers showed maximum peel strengths to evaporated aluminium layers. The adhesion increased linearly with the number of OH groups to a maximum at about 27 OH per 100 C atoms. Higher concentrations of OH groups did not increase the peel strength further.
Monotype functionalizations with different types of functional groups (OH, NH2, COOH) on polypropylene and poly(tetrafluoroethylene) surfaces were synthesized using pulsed plasma-initiated homo- or copolymerization of functional group-carrying monomers. The maximum concentrations of functional groups were 31 OH, 18 NH2 or 24 COOH groups per 100 C atoms using allyl alcohol, allylamine or acrylic acid respectively as the monomer. The measured peel strengths of aluminium deposits increased linearly with the concentration of functional groups. Near the maximum concentration of OH (>27 OH/100 C atoms) or at moderate concentrations of COOH groups (>10 COOH/100 C atoms), constant (maximum) peel strengths were measured due to the mechanical collapse of one component in the composite (cohesive failure). Interface failures in Al-PP composites were found with COOH, NH2 and OH groups and cohesive failures were seen when higher concentrations of COOH groups were applied (>10 COOH/100 C atoms).
Polyethylene foils, used as greenhouse foils stabilized with various types of sterically hindered amine light stabilizers (HALS), showed an extraordinary prolonged lifetime on exposure to natural or artificial weathering if a gas-phase fluorination under low-pressure conditions was applied. The fluorination was performed using F2/N2 mixtures and provided ca. 50 F/100 C (fluorination degree ap25%). The lifetimes of fluorinated PE foils on exposure to artificial or natural weathering were increased at least by a factor of 2-4 as measured in terms of tensile strength and elongation at break.
Different surface treatments of polypropylene (PP) were tested to improve the peel strength of aluminium-PP systems. Plasma exposure followed by chemical grafting of spacers with -SiOH endgroups and thin adhesion promoting layers deposited by aerosol-assisted DBD using aqu. solutions of classic polymers were compared. Both methods were effective, however, –SiOH terminated spacers effected no peeling also after ageing.
Functional groups bearing monomers were pulsed plasma polymerised with a degree of retained functional groups of 5591%. The following functional groups could be produced at a maximum of: 30 OH, 18 NH2, and 24 COOH per 100 C atoms. A plasma-initiated radical copolymerisation could also be realised using the functional group bearing monomers as a source of functionalities, olefins as chain-extenders and dienes as chemical cross-linkers. The peel strengths of Al layers on such plasma polymers were correlated to the type and density of functional groups.
The peel strength of aluminium to polypropylene and poly(tetrafluoroethylene) was determined in dependence on the type and the concentration of functional groups on the polymer surface. For this purpose the polymer surface was equipped with monotype functional groups. The first method to produce monotype functionalized surfaces was an introduction of O functional groups using an oxygen plasma treatment and converting these groups to OH groups applying a wet chemical reduction. In result of this two-step treatment the hydroxyl group concentration at the polymer surface could be increased from 34 to 1014 OH groups/100 C atoms. The second method consists in the deposition of a 150 nm adhesion-promoting layer of plasmapolymers or copolymers onto the polymer surface using the pulsed plasma technique. For that purpose functional groups carrying monomers as allyl alcohol, allylamine and acrylic acid were used. Applying the plasma-initiated copolymerization and using neutral monomers like ethylene or butadiene the concentration of the functional groups was varied.
A correlation of peel strength with the ability of forming chemical interactions between Al atoms and functional groups was found: COOH > OH >> NH2 > H(CH2CH2).
The production of chemically-defined plasma polymers and the introduction of monotype functional groups onto polymer surfaces are described. One method is to lower the energetic level of low-pressure plasmas. Pressure- and plasma-pulsed plasmas were successfully tested for the production of chemically-defined plasma polymers by increasing the monomer supply during the plasma-off period. Well-defined ultra-thin polymer films with regular structure were deposited from atmospheric plasmas by electrospray techniques. Post-plasma wet-chemical processing was also applied, as were gas/liquid-based aerosols and underwater plasmas.
Polyolefins are chemically inert and do not adhere well to metals, polymers or inorganics. To overcome this problem, polyolefin surfaces were modified thermally, plasmachemically, or by flame treatment with different oxygen-containing groups, however, unfortunately, such treatments were accompanied by undesired, adhesion lowering polymer degradation. To solve this dilemma, solutions of synthetic polymers and copolymers were prepared, sprayed into the barrier discharge or electrosprayed without discharge and deposited as thin adhesion-promoting layers. The deposited polymer layers from poly(vinylamine), poly(ethylene glycol)-poly(vinyl alcohol) copolymers and poly(acrylic acid) were endowed with monotype functional groups. Using the aerosol - dielectric barrier discharge only a fraction of functional groups survived the deposition process in contrast to the electrospray in which all functional groups were retained.
A new concept for molecular interface design in metal-polymer systems is presented. The main features of this concept are the replacement of weak physical interactions by strong covalent bonds, the flexibilization of the interface for compensating different thermal expansions of materials by using long-chain flexible and covalently bonded spacers between the metal and the polymer as well as its design as a moisture-repellent structure for hindering diffusion of water molecules into the interface and hydrolysis of chemical bonds.
For this purpose, the main task was to develop plasmachemical and chemical techniques for equipping polymer surfaces with monotype functional groups of adjustable concentration. The establishing of monotype functional groups allows grafting the functional groups by spacer molecules by applying usual wet-chemical reactions. Four processes were favoured for production of monotype functional groups by highly selective reactions: the plasma bromination, the plasma deposition of plasma polymers, the post-plasma chemical reduction of O-functionalities to OH-groups, and the chemical replacement of bromine groups by NH2-groups. The grafting of flexible organic molecules as spacers between the metal layer and polymer improved the peel strength of the metal. To obtain maximal peel strength of aluminium coatings to polypropylene films and occurrence of cohesive failure in the polypropylene substrate, about 27 OH groups per 100 C-atoms or 6 COOH groups per 100 C-atoms were needed. Introducing C6-11-aliphatic spacers 1 OH or COOH group per 100 C-atoms contributed about 60% of the maximal peel strength of the Al-PP system, i.e. 2 or 3 spacer molecules per 100 C-atoms were sufficient for maximal peel strength.
The retention of chemical structure and functional groups during plasma polymerization was investigated. Usually plasma polymer layers, prepared by a continuous wave radio-frequency plasma, are often chemically irregular in their structure and composition. To minimize these irregularities low wattages and the pulsed plasma technique were applied to avoid fragmentations. The first goal was to produce plasma polymers comprising double or triple bonds as precursors for electrically conducting polymers. Acetylene, ethylene, butadiene and polystyrene were used as monomers and deposited as thin polymer films by pulsed plasmas of low wattages. Styrene polymerization was strongly enhanced in the dark phase (plasma off) of a pulsed r.f. plasma caused by the reactivity of the vinyl-type double bond. This could be confirmed by a verification of a rather high chemical regularity of the film sample. The oxygen content of this film measured by X-ray photoelectron spectrometry (XPS) was in situ 0% and after 24 h exposure to air lower than 1%. Additionally, post-plasma oxidations of trapped radicals with air could be suppressed using NO gas as radical quencher. Such quenched plasma polymer layers were completely stable against oxidation for a number of weeks. During the low-wattage pulse plasma polymerization metal atoms were simultaneously or layer by layer evaporated into the growing layer and in situ measured by XPS. These metal atoms are acting as dopants. Here, Li, K, Mg and Cr were used at different concentrations providing electrical conductivity and magnetic properties for the film.
Modelling plasma-induced reactions on polymer surfaces using aliphatic self-assembling and LB layers
(1998)
The chemical and morphological stabilities of polymer segments in the near-surface layer were investigated by spectroscopic methods such as X-ray photoelectron spectroscopy and near-edge X-ray absorption fine structure spectroscopy. Model studies were undertaken with LangmuirBlodgett films, self-assembled monolayers and oligomer films. For thin polymer layers (30 to 500 nm), the changes in molecular-weight distributions of some polymers were investigated systematically by size exclusion chromatography, matrix-assisted laser desorption/ionizationtime-of-flight mass spectrometry and thermal-field flow fractionation for oxygen- and helium-plasma exposures. The polymer surfaces were found to be relatively stable at exposure to an oxygen low-pressure plasma up to ca. 2 s. This is important information to get maximum adhesion to metals in composites. In correlation to their redox potentials, potassium, aluminium and chromium react with oxygen functional groups at the polymer/metal interface. In a dedicated study, chromium was found to attack aromatic rings and form different reaction products.
Plasma-chemical bromination has been shown to be well-suited for highly selective and efficient C–Br-functionalization of polyolefin surfaces and has now been applied to graphitic materials, including highly oriented pyrolytic graphite (HOPG), natural graphite, carbon nanotubes, and graphitized carbon fibres. In contrast to the radical substitution of hydrogen by bromine at hydrogen-terminated sp3-hybridized carbon, bromination of all-carbon bound sp2-hybridized carbon in graphene requires addition to aromatic double bonds. The related change of sp2 to sp3 hybridization of the carbon atoms involved helps to explain experimental results of a loss in surface planarity on brominated HOPG. Bromine concentrations of up to 50 bromine atoms per 100 C-atoms were achieved in elemental bromine vapour under low-pressure plasma conditions using low-energetic inductively coupled radio-frequency plasma excitation. The time scale of the bromination progress was found to increase with the specific surface area of the material. The results of plasma-chemical bromination are compared to that of wet-chemical electrophilic addition reactions, which achieved 28 Br per 100 C for MWCNT. The resulting C–Br bonds from plasma-chemical processing of graphitic materials were shown to be well-suited for hydroxyl functionalization and for grafting of organic molecules by nucleophilic substitution with 1,6-diaminohexane and (3-aminopropyl)triethoxysilane.
Polyolefin surfaces (polyethylene and polypropylene) were exposed to haloform (CHX3) plasmas for introduction of monosort halogen groups. Bromoform and chloroform plasmas produced selectively C-Br (100 Br/100 C) and C-Cl (200 Cl/100 C) groups in high yields. The bromoform plasma showed 1-3 and the chloroform plasma 2-7 post-plasma introduced O-functionalities per 100 C. The polyolefin C-Br groups were grafted wet-chemically or by exposure to the vapour of amines, diols and glycols. Thus, spacer molecules could be covalently bonded to maximal 15 spacer molecules per 100 C for the smallest grafted molecules and 1.2 molecules/100 C for larger molecules as octaaminophenylene-POSS. After metal evaporation the end groups of these polymer-bonded spacer molecules formed also covalent bonds to the metal. Thus, flexible, hydrophobic and barrier elements were introduced into the polymer-metal interfaces for high-impact, high-durable and water-resistant metal-polymer composites as measured by means of peel strengths.
Barrier properties of plasma and chemically fluorinated polypropylene and polyethyleneterephthalate
(1995)
The functionalization, perfluorination or an coating of polypropylene (PP) and polyethyleneterephthalate (PET) surfaces in different plasma atmospheres and in an F[2] + N[2] gas mixture were investigated. The aim of this work was to form a barrier layer against solvent and fuel permeation. Typical test solvents were n-pentane, toluene, tetrachloroethylene and mixtures of n-pentane and methanol. The permeation was gravimetrically measured. The permeation of the solvent mixtures was analyzed by mass spectrometry and Fourier transform IR spectroscopy. The permeation of the solvent mixtures through the plasma-modified polymer samples was associated with increased absorption of polar solvent components in the polymer film. The thickness of the plasma-fluorinated PP surface layer was 10-100 nm and that of chemically fluorinated PP about 5000 nm. Nearly the same barrier efficiency was measured for both plasma- and chemically fluorinated samples.
Different types of plasma, irradiative and chemical activation were compared in terms of surface functionalization. Corona and spark jet plasmas are characterized by low gas temperatures and high rates in surface modification. UV irradiation in the presence of ozone does not involve any particle bombardment and acts only by enhanced photooxidative processes. Although ion implantation can be avoided, this method is not free of radiative damage in both the surface-near region and the bulk of polymers. Furthermore, its functionalization rate is low. In relation to low-pressure O2 plasma modification, all treatments mentioned here have a low efficiency in adhesion promotion due to oxidative degradation of macromolecules and formation of molecular debris known as the ''weak boundary layer''.
Single walled carbon nanotubes (SWNT) have been produced in an electric arc discharge by using a graphite rod as anode which is filled with a powder mixture of graphite and metallic catalysts like nickel and yttrium. The soot material containing approximately a third of SWNT was collected from the cathode region as a soft, voluminous material. The main by-products in this process are amorphous carbon and graphitic nanoparticles which have to be removed by an appropriate purification process. The as-produced soot material was purified by gas phase oxidation in air at 355 °C. The oxidation of amorphous carbon in air is advantageous against wet chemical methods because it is better controllable. Thermogravimetric analysis and electron microscopy were used to investigate the oxidation behavior of the different kinds of carbon. Oxidation of SWNT and amorphous carbon occurs simultaneously even at moderate temperatures, whereas amorphous carbon is more rapidly oxidized than SWNT. For optimizing the purification procedure by gas phase oxidation, kinetic studies were used to determine the oxidation time for each component in the soot at a given temperature. So it is possible to remove the amorphous carbon quantitatively with minimal losses of SWNT. But it was found that graphitic nanoparticles have the highest stability against oxidation and could therefore not be quantitatively removed by this method without the complete destruction of SWNT. Therefore, the electric arc discharge process has to be a controlled process for minimum production of graphitic nanoparticles to obtain a material with a high content of SWNT.
Surface-Enhanced Infrared Absorption (SEIRA) and Its Use in analysis of Plasma-Modified Surface
(1999)
Organic thin films with defined chemical structures and physical properties are required for various applications. Plasma polymerization is of technological interest, since the deposition of plasma polymers is possible on any material of any shape in the desired thickness. We report on the TOF-SIMS (TOF: time-of-flight) and XPS investigations of pulse plasma poly(acetylene) and alkali metal doped pulse plasma poly(acetylene) films. The combination of TOF-SIMS and XPS supplies detailed information on the surface chemistry of these films. Application of both methods provides the possibility for cross-checking certain results. Moreover the different sensitivities of the methods can be utilized. According to the TOF-SIMS and XPS data it can be concluded that the interaction of alkali metals with plasma poly(acetylene) results in electrovalent bonds of the type Me?+C?- between carbon and metal. Furthermore carbonoxygenmetal interactions were observed. These interactions are of the type C=O?-cdots, three dots, centeredMe?+ and/or CO?-Me?+.
Thin metal-filled polyterafluoroethylene films with various metal concentration were produced by co-deposition in vacuum. Metal nanocluster size increased with metal concentration. Films were heated up to 300 degrees C, their optical spectra were recorded during heating. The changes in plasmon band shape and wavelength of the nanocluster ensemble during heating are not linearly related with metal concentration and heating temperature. This is caused by different thermal behavior of the complex processes, which are taking place in each of the two materials present in the film. The metal cluster size and optical properties of the whole ensemble can be purposefully formed by varying metal nature, its concentration and annealing temperature of the film. Nano- and micro-domains with properties different from original film were generated by focused excimer laser or electron beam. Gold-filled PTFE nano-structured films were used as substrate for surface enhanced Raman scattering measurements of ultrathin film of Rhodamine 6G dye.
Polytetrafluoroethylene (PTFE) films have been deposited onto polycarbonate (PC) substrates from the products of PTFE evaporation, activated by a cloud of accelerated electrons. A 40.68 MHz glow discharge was used during the deposition process. The polymer films have been characterised by XPS, FTIR and AFM. The use of the low power plasma during film growth led to the formation of PTFE films with modified structure. Films are amorphous and contain more cross-links, but in general, the structure of their macromolecules is still linear. An increase of RF-power leads to the formation of films with large amount of double bonds and enhanced internal stresses.
Deposition of PTFE on PC without plasma treatment led to the formation of PTFE clusters up to 50 nm in diameter. The RMS roughness of the films, deposited without plasma, was about 4 nm, while the films deposited with plasma treatment had a roughness of 1.5 nm. The use of plasma has an additional effect if a PTFE coating is deposited on the PC substrate with submicrometer-sized steps. Without plasma the steps retain a rectangular shape. Deposited with the RF-discharge the PTFE layers resemble plasma-polymerised films. Under certain conditions the deposited films can fill trenches in the substrate like a wetting liquid, while under other conditions they avoid trenches and grow in between them.
Indirect UV-absorption spectrometry was shown to be a valuable tool for chemical characterization of functionalized carbon nanotubes (CNTs). It complements data from X-ray photoelectron spectroscopy (XPS) or FTIR analysis since it helps to clarify the type and concentration of functional groups. The principles of indirect application of UV-spectrometry and its mathematical interpretation are discussed. Their facile application, together with their adequate sensitivity and high flexibility, make UV-absorption-based approaches a valuable alternative to fluorescence spectrometry. Here, the approach was applied to the chemical analysis of oxidizing substances on CNTs. For this, pristine CNTs of low but finite oxygen content as well as brominated CNTs were analyzed by reaction in suspension with UV-active thiol reagents and a styrene derivative. It was shown that carefully selected reagents allow differentiation and quantification of bromine and generally oxidizing entities like oxygen. For brominated CNTs, it was shown that physisorbed bromine may dominate the overall bromine content.
Chemical functionalization of carbon nanotubes (CNT) with nucleophiles requires introduction of electrophilic reactive sites on the CNTs. This can, for instance, be accomplished by the chemical bromination procedure with elemental bromine and a set of Lewis acids (BBr3, BF3 × Et2O, AlBr3, FeBr3, ZnBr2, TiBr4, SiBr4, SnBr4, VBr3) or a radical starter like dibenzoylperoxide (DBPO) in appropriate solvents at varied temperature. The present approach to electrophilic sites relies on the well-known electrophilic aromatic substitution or addition of bromine with aromatic structural units. In addition to the use of bromine, the introduction of haloalkyl groups was also investigated here using bis-electrophiles or haloalcohols and Brønsted acids. The advantages and drawbacks of the studied reaction conditions, the obtained degree of bromination as analyzed by X-ray photoelectron spectroscopy (XPS) and the amount of introduced bromine that can be substituted by a nucleophile are presented and discussed.
Wet-chemically oxidized carbon nanotubes (CNTs) generally exhibit both covalently-bound acidic functional groups on the surface and surface-adsorbed acidic substances, i.e. carbonaceous CNT fragments from the oxidation procedure. Direct potentiometric titration of oxidizable high surface area materials with dynamically desorbing acidic fragments is slow and inaccurate. Adsorbed acidic fragments are deprotonated by sodium hydroxide and form anions in solution which is not the case for covalently bound acidic groups on the CNTs, so the following filtration after NaOH treatment separates desorbable acidic substances from non-desorbable or covalently bound groups. For a known concentration of NaOH, titration of the eluate with hydrochloric acid (HCl) allows determination of the concentrations of both types of acidities. However, contrary to reports in the literature, the NaOH consumed by non-desorbed acidic groups has to be accounted for and impedes distinction of desorbed acidic groups via their pKa values. Results are presented of a study on the information content and the reliability of indirect potentiometric Boehm titration for different oxidized multi-walled CNTs.
Activators regenerated by electron transfer–atom radical transfer polymerization (ATRP) as a controlled living polymerization are distinguished by their acceptance of small amounts of transition-metal complexes and oxygen and by their tolerance of reducing agents at a high concentration. The precondition of all ATRP applications is the use of homolytic or heterolytic cleavable halides as a dormant species; this allows the propagation of monomer chains. Hence, alkyl bromides are slightly cleavable and are the preferred initiators for ATRP. The bromination of polymer slides used as macroinitiators was carried out under gentle bromoform plasma conditions. This led to an oxidation-resistant stable bromine layer. More than 20 bromines per 100 carbons on the polymer scaffold were permanently bound to the substrate after plasma treatment. The resulting amounts of secondary and tertiary bromines on the polymer scaffold exhibited a suitable macroinitiator concentration for the surface-initiated polymerization of methyl methacrylate and glycidyl methacrylate.
Polypropylene supports were functionalized by plasma-deposition of polymeric allylamine layers. The surface amino groups generated were wet-chemically reacted with xanthene dyes resulting in fluorescent polymer films. The effect of polymer-attachment of the dyes on their emission features was studied fluorometrically and different methods were tested to improve the fluorescence properties of the films. Modification with cucurbit[6]uril (CB6) yields a moderately enhanced fluorescence as well as an improved photostability. The observed effect is most likely due to CB6-induced rigidization of the linker molecules which seems to reduce fluorescence quenching dyedye and fluorophoresurface interactions.
A straightforward strategy toward the sensitive fluorometric detection of primary amino groups on plasma-chemically modified polypropylene supports is presented, exploiting the transformation of the sterically nonhindered pyrylium dye Py-1 into its pyridinium counterpart. The reaction-induced blue-shifted absorption and emission bands and an increased fluorescence quantum yield provide the basis for the spectroscopic distinction between covalently bound and free, that is, nonspecifically adsorbed label molecules. With this label, for the first time, plasma-chemically introduced amino functionalities could be monitored on the surface of a polymer film employing fluorescence spectroscopy and confocal laser scanning microscopy.
Molecular engineering of polymer surfaces that includes the attachment of functional molecules to existing or previously generated reactive chemical groups like e.g., - OH, - NH2, or - CHO requires simple strategies and tools for the controlled generation of surface functionalities and their derivatization as well as for their identification and eventually quantification. Here, we systematically investigate the plasma-chemical surface modification of polypropylene films in combination with dansyl labeling chemistry and conventional, yet costly, XPS and highly sensitive fluorescence spectroscopy for the detection of surface groups. Based on these results, the potential of and requirements on the fluorometric characterization and quantification of surfaces functionalities are discussed.
Ultra-high molecular weight polyethylene membranes were modified and subsequently polymer coated using the underwater plasma produced by glow discharge electrolysis. This plasma pretreatment generated various O-functional groups among them OH groups have dominated. This modified inner (pore) surface of membranes showed complete wetting and strong adhesion to a hydrogel copolymerized by glow discharge electrolysis also. The deposited hydrogel consists of plasma polymerized acrylic acid crosslinked by copolymerization with the bifunctional N,N'-methylenebis(acrylamide). Tuning the hydrogel hydrophilicity and bio-compatibility poly(ethylene glycol) was chemically inserted into the copolymer. Such saturated polymer could only be inserted on a non-classic way by (partial) fragmentation and recombination thus demonstrating the exotic properties of the underwater plasma. The modification of membrane was achieved by squeezing the reactive plasma solution into the pores by plasma-induced shock waves and supported by intense stirring. The deposited copolymer hydrogel has filled all pores also in the inner of membrane as shown by scanning electron microscopy of cross-sections. The copolymer shows the characteristic units of acrylic acid and ethylene glycol as demonstrated by infrared spectroscopy. A minimum loss in carboxylic groups of acrylic acid during the plasma polymerization process was confirmed by X-ray photoelectron spectroscopy. Additional cell adhesion tests on copolymer coated polyethylene using IEC-6 cells demonstrated the bio-compatibility of the plasma-deposited hydrogel.
Plasma chemical methods are well suited for introducing functional groups to the surfaces of chemically inert polymers such as polyolefins. However, a broad variety of functional groups are often formed. Unfortunately, for further chemical processing such as grafting of molecules for advanced applications a highly dense monotype functionalized polyolefin surface is needed. Therefore, the main task was to develop a selective surface functionalization process, which formed preferably only a single type of functional groups at the surface in high concentration. Amongst the novel plasma methods, the underwater plasma process (UWP) is one of most attractive options to solve the problem of monotype functionalization. Such plasma is an efficient source of ions, electrons, UV-radiation, high-frequency shock waves, radicals such as hydroxyl radical, and reactive neutral molecules such as hydrogen peroxide. In contrast to established gas phase glow discharge processes, the water phase limits the particle and radiation energies and thus the energy input into the polymer. By virtue of the liquid water environment, which moderates highly energetic plasma species, extensive oxidation, degradation, cross-linking and radical formation on the polymer are more limited as compared to gas plasma exposure. The variety of plasma produced species in the water phase is also much smaller because of the limited reaction possibilities of the plasma with water. The possibility to admix a broad variety of chemical additives makes underwater plasma even more attractive. Hydrogen peroxide and the catalyst (Fe-ZSM5) should influence and increase the equilibrium concentration of OH radicals in the underwater plasma process. It was found that these radicals played a very important role in OH functionalization of polyolefin surfaces. Hydrogen peroxide was identified to be the most prominent precursor for OH group formation in the UWP. The catalyst would affect the steady state of OH radical formation and its reaction with the substrate surface and thus accelerates the functionalization process.
Study of carboxylic functionalization of polypropylene surface using the underwater plasma technique
(2009)
Non-equilibrium solution plasma treatment of polymer surfaces in water offers the possibility of more dense and selective polymer surface functionalization in comparison to the well-known and frequently used low-pressure oxygen plasma. Functional groups are introduced when the polymer surface contacts the plasma moderated solution especially water solutions. The emission of ions, electrons, energy-rich neutrals and complexes, produced by the ion avalanche are limited by quenching, with the aid of the ambient water phase. The UV-radiation produced in plasma formation also helps to moderate the reaction solution further by producing additional excited, ionized/dissociated molecules. Thus, monotype functional groups equipped polymer surfaces, preferably OH groups, originating from the dissociated water molecules, could be produced more selectively. An interesting feature of the technique is its flexibility to use a wide variety of additives in the water phase. Another way to modify polymer surfaces is the deposition of plasma polymers carrying functional groups as carboxylic groups used in this work. Acetic acid, acrylic acid, maleic and itaconic acid were used as additive monomers. Acetic acid is not a chemically polymerizing monomer but it could polymerize by monomer/molecular fragmentation and recombination to a cross linked layer. The other monomers form preferably water-soluble polymers on a chemical way. Only the fragmented fraction of these monomers could form an insoluble coating by cross linking to substrate. The XPS analysis was used to track the alterations in -O-CO- bond percentage on the PP surface. To identify the -COOH groups on substrate surface unambiguously, which have survived the plasma polymerization process, the derivatization with trifluoroethanol was performed.
Underwater plasma and glow discharge electrolysis are interesting new methods for polymer surface functionalization. The achievable content of O-containing functional groups exceeds that of oxygen glow discharge gas plasmas by a factor of two (up to ca. 56 O/100 C). The percentage of OH groups among all O-containing groups can reach 25 to 40%, whereas it is about 10% in the gas plasmas. Addition of hydrogen peroxide increases the fraction of OH groups to at most 70% (27 OH/100 C). The liquid plasma systems are also able to polymerize acrylic acid and deposit the polymer as very thin film on substrate surfaces or membranes, thereby retaining about 80% of all COOH functional groups (27 COOH/100 C).