The peel strength of aluminium to polypropylene and poly(tetrafluoroethylene) was determined in dependence on the type and the concentration of functional groups on the polymer surface. For this purpose the polymer surface was equipped with monotype functional groups. The first method to produce monotype functionalized surfaces was an introduction of O functional groups using an oxygen plasma treatment and converting these groups to OH groups applying a wet chemical reduction. In result of this two-step treatment the hydroxyl group concentration at the polymer surface could be increased from 34 to 1014 OH groups/100 C atoms. The second method consists in the deposition of a 150 nm adhesion-promoting layer of plasmapolymers or copolymers onto the polymer surface using the pulsed plasma technique. For that purpose functional groups carrying monomers as allyl alcohol, allylamine and acrylic acid were used. Applying the plasma-initiated copolymerization and using neutral monomers like ethylene or butadiene the concentration of the functional groups was varied.
A correlation of peel strength with the ability of forming chemical interactions between Al atoms and functional groups was found: COOH > OH >> NH2 > H(CH2CH2).
Melamine and melamine resins are widely used as fire retardants for polymer materials used in pharmaceutical, plastic, textile, rubber, and construction industry. Melamine-based flame retardants act by blowing off intumescent layers, char formation, and emission of quenching ammonia gas and diluent molecular nitrogen. Special advantages are: low cost, low smoke density and toxicity, low corrosive activity, safe handling, and environmental friendliness. Methylated poly(melamine-co-formaldehyde) (mPMF) was used as thick (≥40 µm) fire-retardant coating for plasma pretreated polymers. A combined low-pressure plasma pretreatment consisting of oxygen plasma exposure followed by deposition of thin poly(allylamine) (ppAAm) and poly(allyl alcohol) (ppAAl) plasma polymers as adhesion promoters have improved the adhesion of thick mPMF coatings strongly. Chemical structure and composition of deposited polymer films were characterized by infrared-attenuated total reflectance and X-ray photoelectron spectroscopy (XPS). After peeling, the peeled layer surfaces were also investigated for identification of the locus of failure and their topography using optical microscopy and XPS. Often the adhesion promotion was so efficient that the peeling of coating was not possible. Thermal properties of plasma polymers and dip-coating films were analyzed by thermogravimetric analysis. Significant improvement of fire-retardant properties of coated polymers was confirmed by flame tests.
Ultra-high molecular weight polyethylene membranes were modified and subsequently polymer coated using the underwater plasma produced by glow discharge electrolysis. This plasma pretreatment generated various O-functional groups among them OH groups have dominated. This modified inner (pore) surface of membranes showed complete wetting and strong adhesion to a hydrogel copolymerized by glow discharge electrolysis also. The deposited hydrogel consists of plasma polymerized acrylic acid crosslinked by copolymerization with the bifunctional N,N'-methylenebis(acrylamide). Tuning the hydrogel hydrophilicity and bio-compatibility poly(ethylene glycol) was chemically inserted into the copolymer. Such saturated polymer could only be inserted on a non-classic way by (partial) fragmentation and recombination thus demonstrating the exotic properties of the underwater plasma. The modification of membrane was achieved by squeezing the reactive plasma solution into the pores by plasma-induced shock waves and supported by intense stirring. The deposited copolymer hydrogel has filled all pores also in the inner of membrane as shown by scanning electron microscopy of cross-sections. The copolymer shows the characteristic units of acrylic acid and ethylene glycol as demonstrated by infrared spectroscopy. A minimum loss in carboxylic groups of acrylic acid during the plasma polymerization process was confirmed by X-ray photoelectron spectroscopy. Additional cell adhesion tests on copolymer coated polyethylene using IEC-6 cells demonstrated the bio-compatibility of the plasma-deposited hydrogel.
The adhesion of thick poly(allylamine)-polyphosphate layers (1 µm) deposited by the wet-chemical layer-by-layer technique (LbL) onto polyethylene or polystyrene (each 100 µm) was very low. To promote the adhesion of these LbL layers the polyolefin substrates were oxidized at the surface by short exposure to the oxygen plasma (2 or 5 s) and subsequently coated with an interlayer of plasma-deposited poly(allylamine) or poly(allyl alcohol) (100 nm). The plasma polymer interlayers have improved strongly the adhesion between polyolefin substrates and polyphosphate coatings. Such phosphate coatings are interesting for life sciences (nucleotide formation) but also for fire retardancy in combination with N-rich compounds such as melamine.
The intention was to prefer chemical and hydrogen bonds for adhesion promoting because of their high binding energy. Therefore, the introduced oxygen-containing groups at the polyolefin surface could interact with the OH or NH2 groups of the adhesion-promoting plasma polymer interlayer. These groups were also able to interact strongly with the poly(allylamine)-polyphosphate topcoating.
The coated polyolefins were investigated using Fourier Transform Infrared Spectroscopy in Attenuated Total Reflectance mode (FTIR-ATR), X-ray Photoelectron Spectroscopy (XPS), Thermo-Gravimetric Analyses (TGA) and Atomic Force Spectroscopy (AFM) and 90° peel test.