Tris(3,5-dimethylpyrazolyl)arsane (1) is introduced as a low-cost and convenient to handle arsenic precursor for the straight Forward synthesis of InAs Quantum dots (QDs). Transamination of 1 with the solvent oleylamine (OLAH) gives trioleylarsane (As(OLA)3) which in the presence of the reducing agents diisobutylaluminum hydride (DIBAL-H) or trioleylphosphane (P(OLA)3) yields InAs QDs via a typical hot injection approach. The size of the obtained InAs core QDs are tuned by varying the reaction time, the amount of the applied reducing agent, or even more effectively by changing the Indium and/or zinc halide precursors, InX3, and ZnX2 (Cl, Br, or I). Passivation of the resulting InAs particles with a
protective ZnS or ZnSe shell results in improved photoluminescence of the core/shell QDs covering a spectral range between 600 and 1150 nm.
Eine modifizierte Syntheseroute auf der Basis wasserfreier Seltenerdacetate wurde zur Synthese aufwärtskonvertierender Kern/Schale‐Nanokristalle mit mittleren Größen zwischen 15 bis 45 nm eingesetzt. Die nahezu monodispersen Partikel bestehen aus einem NaYF4:Yb,Er‐Kern, dotiert mit 18 % Yb3+ und 2 % Er3+, und einer inerten Schale aus NaYF4, wobei die Dicke der Schale dem jeweiligen Radius des Kernpartikels entspricht. Absolutmessungen der Photolumineszenz‐Quantenausbeuten bei verschiedenen Anregungsleistungsdichten zeigen, dass die Quantenausbeuten von 45 nm Kern/Schale‐Partikeln schon fast an die Quantenausbeute des mikrokristallinen aufwärtskonvertierenden Leuchtstoffs heranreichen. Kleinere Kern/Schale‐Partikel, die nach der gleichen Methode hergestellt wurden, zeigen nur eine moderate Abnahme der Quantenausbeute. Beispielsweise ist die Quantenausbeute von 15 nm großen Kern/Schale‐Partikeln bei hohen Leistungsdichten (100 W cm−2) nur um einen Faktor drei kleiner als die des mikrokristallinen Leuchtstoffpulvers und um ungefähr einen Faktor 10 kleiner bei niedrigen Leistungsdichten (1 W cm−2).
Upconversion core/shell nanocrystals with different mean sizes ranging from 15 to 45 nm were prepared via a modified synthesis procedure based on anhydrous rare‐earth acetates. All particles consist of a core of NaYF4:Yb,Er, doped with 18 % Yb3+ and 2 % Er3+, and an inert shell of NaYF4, with the shell thickness being equal to the radius of the core particle. Absolute measurements of the photoluminescence quantum yield at a series of different excitation power densities show that the quantum yield of 45 nm core/shell particles is already very close to the quantum yield of microcrystalline upconversion phosphor powder. Smaller core/shell particles prepared by the same method show only a moderate decrease in quantum yield. The quantum yield of 15 nm core/shell particles, for instance, is reduced by a factor of three compared to the bulk upconversion phosphor at high power densities (100 W cm−2) and by approximately a factor of 10 at low power densities (1 W cm−2).
Absolute upconversion quantum yields of blue-emitting LiYF4:Yb3+,Tm3+ upconverting nanoparticles
(2018)
The upconversion quantum yield (QY) is an essential parameter for the characterization of the optical performance of lanthanoid-doped upconverting nanoparticles (UCNPs). Despite its nonlinear dependence on excitation power density, it is typically reported only as a single number. Here, we present the first measurement of absolute upconversion quantum yields of the individual emission bands of blue light-emitting LiYF4:Yb3+,Tm3+ UCNPs in toluene. Reporting the quantum yields for the individual emission bands is required for assessing the usability of UCNPs in various applications that require upconverted light of different wavelengths, such as bioimaging, photocatalysis and phototherapy.
Here, the reliability of the QY measurements is demonstrated by studying the same batch of UCNPs in three different research groups. The results show that whereas the total upconversion quantum yield of these UCNPs is quite high - typically 0.02 at a power density of 5 W/cm2 — most of the upconverted photon flux is emitted in the 794 nm upconversion band, while the blue emission band at 480 nm is very weak, with a much lower quantum yield of 6 times 10^5 at 5 W/cm2. Overall, although the total upconversion quantum yield of LiYF4:Yb3+,Tm3+ UCNPs seems satisfying, notably for NIR bioimaging, blue-light demanding phototherapy applications will require better-performing UCNPs with higher blue light
upconversion quantum yields.