Gas sensors are an important tool in various areas for example in industrial process control as well as Gas sensors are an important tool in various areas for example in industrial process control as well as safety applications or in research. A useful gas detector should be selective, precise, stable and cost-effective. In the present research a surface based gas detection technique is investigated using the SPR effect with ellipsometric readout. This technique is called surface plasmon resonance enhanced ellipsometry (SPREE).
The sensor consists of a gold layer (40 nm) top-coated with a doped metal-oxide (M:SnOₓ,
5 nm). The coating is added by magnetron sputtering with doped targets with different doping concentrations. It could be shown that, without the top-coating, these type of sensors can detect various gases, e.g. CO, H2, O2, O3, He, N2, with sensitivities down to the ppm range (in air).
The goal of the present study is to characterize the additional coating materials in dependence of the coating conditions. With the help of the doped-metal oxide, the sensitivity increases dramatically by a factor of 100. Additionally, a selectivity for specific gases is observed which depends on the doping conditions of the coating. Changing the properties of the plasma coating process and the doping metal gives access to a variety of different layers and enables us to find the best conditions.
Coatings deposited by magnetron co-sputtering from a single RF magnetron with a ceramic SnO2 target with iron inset in argon plasma were studied. The mass spectra of the process identified Sn+ and SnO+ species as the dominant species sputtered from the target, but no SnO2+ species were detected. The dominant positive ions in argon plasma are Ar+ species. The only detected negative ions were O-. Sputtered neutral tin related species were not detected. Iron related species were also not detected because their concentration is below the detection limit.
The concentration of iron dopant in the tin oxide coatings was controlled by the RF bias applied on the substrate holder while the discharge pressure also has some influence. The iron concentration was in the range from 0.9 at.% up to 19 at.% increasing with the substrate bias while the sheet resistivity decreases. The stoichiometry ratio of O/(Sn + Fe) in the coatings increased from 1.7 up to 2 in dependence on the substrate bias from floating bias (- 5 V) up to - 120 V of RF self-bias, respectively. The tin in the coatings was mainly bonded in Sn4 + state and iron was mainly in Fe2 + state when other tin bonding states were detected only in a small amounts. Iron bonding states in contrary to elemental compositions of the coatings were not influenced by the RF bias applied on the substrate.
The coatings showed high transparency in the visible spectral range. However, an increased metallic behavior could be detected by using a higher RF bias for the deposition. The X-ray diffraction patterns and electron microscopy pictures made on the coatings confirmed the presence of an amorphous phase.
Background: Gas sensors are very important in several fields like gas monitoring, safety and environmental applications. In this approach, a new gas sensing concept is investigated which combines the powerful adsorption probability of metal oxide conductive sensors (MOS) with an optical ellipsometric readout. This concept Shows promising results to solve the problems of cross sensitivity of the MOS concept.
Results: Undoped tin oxide (SnOx) and iron doped tin oxide (Fe:SnOx) thin add-on films were prepared by magnetron sputtering on the top of the actual surface plasmon resonance (SPR) sensing gold layer. The films were tested for their sensitivity to several gas species in the surface plasmon resonance enhanced (SPREE) gas measurement. It was found that the undoped tin oxide (SnOx) shows higher sensitivities to propane (C3H8) then to carbon monoxide (CO). By using Fe:SnOx, this relation is inverted. This behavior was explained by a change of the amount of binding sites for CO in the layer due to this iron doping. For hydrogen (H2) no such relation was found but the sensing ability was identical for both layer materials. This observation was related to a different sensing mechanism for H2 which is driven by the Diffusion into the layer instead of adsorption on the surface.
Conclusion: The gas sensing selectivity can be enhanced by tuning the properties of the thin film overcoating. A relation of the binding sites in the doped and undoped SnOx films and the gas sensing abilities for CO and C3H8 was found. This could open the path for optimized gas sensing devices with different coated SPREE sensors.