Off-axis tests are widely used for the determination of the anisotropic mechanical properties of composite materials, this is, the longitudinal E-modulus and the strength. The mechanical properties are evaluated from the test data under idealising assumptions such as homogeneity of the material as well as a homogeneous stress distribution. In real off-axis tests, however, significant deviations from the idealising assumptions are present. The reduction of the accuracy of the results strongly depends on the off-axis angle.
In this paper a series of off-axis tests is analysed. The stresses on potential failure plane are calculated by finite element analyses. By varying the geometrical parameters it is shown how small deviations from the ideal case influence the measured elastic constants and the strength. Especially at low off-axis angles the mechanical properties strongly vary with the angle. In addition, fracture surfaces for different shear/normal stress combinations are studied and typical phenomena are identified.
The failure behaviour of unidirectional plies tested under off-axis loading is studied. The stress distribution occurring in standard off-axis tests is briefly discussed. The different failure modes, this is, pure fiber breakage, pure inter fiber failure as well as a superposition of both is analysed based on test data and fracture patterns. The large difference of the failure load depending on the failure mode at small off-axis angles is studied by comparison of a short and a long 3° off-axis angle specimen.
The energy release rate delivered during the debonding of a fiber inside a composite ply is analysed using a representative volume element. Two different fiber volume fractions are studied by a linear elastic fracture mechanical analysis by using the finite element method.
The dependency of the mixed mode energy release rate on the length of the crack increment is analysed. It is shown that the same general behaviour found in case of a straight Interface crack is valid also for circular cracks. As a result the discrimination of the energy release rate into mode I and mode II portions is questionable.