The shape of X-ray reflections from the cuboidal γ/γ'-microstructure was investigated. The measurements were performed on the 4th generation single-crystal nickel-base superalloy TMS138. It is shown that reflections from non-cubic crystallographic planes split not only in d-scale due to the different spacing of the γ- and γ'-lattices but also in the pole figure due to the tilting of γ-lattice planes. This tilting results from the elastic distortion of the γ-lattice caused by the γ/γ'-misfit. The results obtained are discussed under the methodical aspect of misfit measurement.
Mit Hilfe des HIP-Verfahrens („Hot Isostatic Pressing“) werden Poren in der einkristallinen Nickel-Basis Superlegierung CMSX-4 kontinuierlich geschrumpft und dadurch die nach der Erstarrung und der Wärmebehandlung vorhandene Porosität stark reduziert. In diesem Beitrag werden experimentelle und numerische Untersuchungen zu den Mechanismen der Porenschrumpfung zusammengefasst. Es zeigt sich, dass das Verformungsverhalten während Kriechversuchen bei der HIP-Temperatur durch Versetzungsgleitung auf oktaedrischen Ebenen dominiert wird.
Dagegen zeigen Messungen der Porositätsabnahme und Simulationen des Porenschließens, dass die Kinetik der Porenschrumpfung durch das Phänomen der Leerstellendiffusion zwischen Poren und Kleinwinkelkorngrenzen („Low Angle Boundary“, LAB) bestimmt wird. Im Gegensatz führt die klassische Kristallviskoplastizität zu einer systematischen Überschätzung dieser Kinetik. Der scheinbare Widerspruch lässt sich auflösen, wenn man bedenkt, dass auf der Skala der Poren Versetzungsquellen nicht gleichmäßig verteilt sind, wie in der konventionellen Kristallplastizität implizit angenommen wird. Stattdessen wird in einem weiterführenden Modell davon ausgegangen, das Kleinwinkelkorngrenzen (LABs) als Versetzungsquellen fungieren, während die Scherspannungen sehr stark in der Nähe der Poren lokalisiert sind, was die Emission von Versetzungen deutlich reduziert.
Single-crystal components made of nickel base superalloys contain pores after casting and homogenization heat treatment. Hot isostatic pressing (HIP), which is carried above the γ' -solvus temperature of the alloy, is industrially applied to reduce porosity. A modeling of HIP based on continuously distributed dislocations is developed in a 2D setting. Glide and climb of straight-edge dislocations, as well as vacancy diffusion, are the deformation mechanisms taken into account.
Thereby, dislocation glide is controlled by dragging a cloud of large atoms, and climb is controlled by vacancy diffusion. Relying on previous investigations of the creep behavior at HIP temperatures, it is assumed that new dislocations are nucleated at low-angle boundaries (LAB) and move through subgrains until they either reach the opposite LABs or react with other dislocations and annihilate.
Vacancies are created at the pore surface and diffuse through the alloy until they are either consumed by climbing dislocations or disappear at the LABs. The field equations are solved by finite elements. It is shown that pore shrinking is mostly controlled by vacancy diffusion as the shear stresses at the LABs are too low to
nucleate a sufficient amount of dislocations.
Initially, as-cast and homogenized single crystals of nickel-base superalloy CMSX-4 are subjected to hot isostatic pressing at 1288 °C. Two series of experiments are conducted: under the same pressure of 103 MPa but with different durations, between 0.5 and 6 h, and under different pressures, between 15 and 150 MPa, but for the same time of 0.5 h. The porosity annihilation is investigated metallographically and by high-resolution synchrotron X-ray tomography. The obtained experimental results are compared with the predictions of the vacancy model proposed recently in the group. Herein, the model is further refined by coupling with X-ray tomography. The model describes the evolution of the pore arrays enclosed in the 3D synchrotron tomograms during hot isostatic pressing and properly predicts the time and stress dependences of the pore annihilation kinetics. The validated model and the obtained experimental results are used for selecting the optimal technological parameters such as applied pressure and processing time
Rafting during high temperature deformation in a single crystal superalloy: experiments and modeling
(2012)
Pore annihilation during hot isostatic pressing (HIP) was investigated in the single-crystal nickel-base superalloy CMSX-4 experimentally by interrupted HIP tests at 1288 °C/103 MPa. The kinetics of pore annihilation was determined by density measurement and quantitative metallography. Transmission electron microscopy of a HIPed specimen showed that the pores shrink via dislocation movement on octahedral glide planes. Theoretically pore closure under HIP condition was modelled by the finite element method using crystal plasticity and large strain theories. The modelling gives a similar kinetics of pore annihilation as observed experimentally, however somewhat higher annihilation rate.
A new experimental technique (repeated load annealing of flat wedge shaped specimens) was proposed for characterization of microstructural degradation under creep conditions. This technique was applied to investigate the microstructural degradation of the nickel-base superalloy CMSX-4 in a wide range of temperatures and stress levels. The results obtained allowed to describe analytically the kinetics of rafting, which is important to predict the reduction of fatigue lifetime and yield stress.
The elastic properties of the single-crystal nickel-base superalloy CMSX-4 used as a blade material in gas turbines were investigated by the sonic resonance method in the temperature interval between room temperature and 1300 °C. Elastic constants at such high temperatures are needed to model the mechanical behavior of blade material during manufacturing (hot isostatic pressing) as well as during technical accidents which may happen in service (overheating). High reliability of the results was achieved using specimens of different crystallographic orientations, exciting various vibration modes as well as precise measurement of the material density and thermal Expansion required for modeling the resonance frequencies by finite element method. Combining the results measured in this work and literature data the elastic constants of the gamma and gamma' phases were predicted.
This prediction was supported by measurement of the temperature dependence of the gamma'fraction.
All data obtained in this work are given in numerical or analytical forms and can be easily used for different scientific and engineering calculations.
It is shown experimentally that, during annealing and creep under low applied stresses, matrix dislocation loops frequently cross-glide. The periodic length of the zigzag dislocations deposited in the interfaces is equal to that of the γ/γ'-microstructure. Initially, the zigzag dislocations move in the (001) interface by a combination of glide and climb but then they stop near the γ'-edges and align along (100). Reactions of such dislocations lead to the formation of square interfacial networks consisting of (100) oriented edge dislocations. The complex dislocation movement is explained by the inhomogeneity of the misfit stresses between γ- and γ'-lattices. The tensile components of the stress tensor drive the dislocations through the channel, whereas the shear components near the γ'-edges cause the zigzag movement and the (100) alignment. The total effect is the most efficient relaxation of the misfit stresses. The results are relevant, especially for single-crystal superalloys of the newest generations, which have an increased γ/γ'-misfit due to the high level of refractory elements.