Filtern
Dokumenttyp
- Zeitschriftenartikel (24)
- Vortrag (15)
- Posterpräsentation (3)
- Beitrag zu einem Tagungsband (2)
Schlagworte
- Additive manufacturing (16)
- Additive Manufacturing (12)
- Residual stress (12)
- AGIL (10)
- Diffraction (8)
- Laser powder bed fusion (8)
- Neutron diffraction (5)
- Metrology (4)
- Residual stress analysis (4)
- Additive Fertigung (3)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (44)
- 8.5 Röntgenbildgebung (44)
- 9 Komponentensicherheit (31)
- 9.4 Integrität von Schweißverbindungen (25)
- 5 Werkstofftechnik (17)
- 5.1 Mikrostruktur Design und Degradation (16)
- 9.6 Additive Fertigung metallischer Komponenten (11)
- 5.2 Metallische Hochtemperaturwerkstoffe (9)
- 5.5 Materialmodellierung (4)
- 8.0 Abteilungsleitung und andere (4)
- 9.3 Schweißtechnische Fertigungsverfahren (4)
- 4 Material und Umwelt (1)
- 4.2 Material-Mikrobiom Wechselwirkungen (1)
- 5.0 Abteilungsleitung und andere (1)
- 5.4 Multimateriale Fertigungsprozesse (1)
- 8.4 Akustische und elektromagnetische Verfahren (1)
- S Qualitätsinfrastruktur (1)
- S.0 Abteilungsleitung und andere (1)
Eingeladener Vortrag
- nein (15)
The effect of two types of scanning strategies on the grain structure and build-up of Residual Stress (RS) has been investigated in an as-built IN718 alloy produced by Laser Powder Bed Fusion (LPBF). The RS state has been investigated by X-ray diffraction techniques. The microstructural characterization was performed principally by Electron Backscatter Diffraction (EBSD), where the application of a post-measurement refinement technique enables small misorientations (< 2°) to be resolved. Kernel average misorientation (KAM) distributions indicate that preferably oriented columnar grains contain higher levels of misorientation, when compared to elongated grains with lower texture. The KAM distributions combined with X-ray diffraction stress maps infer that the increased misorientation is induced via plastic deformation driven by the thermal stresses, acting to self-relieve stress. The possibility of obtaining lower RS states in the build direction as a consequence of the influence of the microstructure should be considered when envisaging scanning strategies aimed at the mitigation of RS.
This study reports on the stress relaxation potential of stress-relieving heat treatments for laser powder bed fused 316L. The residual stress is monitored non-destructively using neutron diffraction before and after the heat treatment. Moreover, the evolution of the microstructure is analysed using scanning electron microscopy. The results show, that a strong relaxation of the residual stress is obtained when applying a heat treatment temperature at 900°C. However, the loss of the cellular substructure needs to be considered when applying this heat treatment strategy.
The triaxial distribution of the residual stress in laser powder bed fused austenitic steel 316L was determined by X-ray and neutron diffraction. The residual stress analysis results were linked to the thermal history of the specimens, which were manufactured with varying inter-layer-times and scanning velocities. A clear link between the in-process temperature of the specimens and the residual stress was found, based on in-situ monitoring data.
The manufacturability of metallic alloys using laser-based additive manufacturing methods such as laser powder bed fusion has substantially improved within the last decade. However, local melting and solidification cause hierarchically structured and crystallographically textured microstructures possessing large residual stress. Such microstructures are not only the origin of mechanical anisotropy but also pose metrological challenges for the diffraction-based residual stress determination. Here we demonstrate the influence of the build orientation and the texture on the microstructure and consequently the mechanical anisotropy of as-built Inconel 718. For this purpose, we manufactured specimens with [001]/[011]-, [001]- and [011]/[111]-type textures along their loading direction. In addition to changes in the Young’s moduli, the differences in the crystallographic textures result in variations of the yield and ultimate tensile strengths. With this in mind, we studied the anisotropy on the micromechanical scale by subjecting the specimens to tensile loads along the different texture directions during in situ neutron diffraction experiments. In this context, the response of multiple lattice planes up to a tensile strain of 10% displayed differences in the load partitioning and the residual strain accumulation for the specimen with [011]/[111]-type texture. However, the relative behavior of the specimens possessing an [001]/[011]- and [001]-type texture remained qualitatively similar. The consequences on the metrology of residual stress determination methods are discussed.