Filtern
Dokumenttyp
Sprache
- Englisch (2)
Referierte Publikation
- ja (2)
Schlagworte
- Analysis and identification (1)
- Artificial weathering (1)
- Crosslinking (1)
- Degradation (1)
- FTIR imaging (1)
- Microplastics (1)
- Moisture (1)
- Polyurethane (1)
- Raman imaging (1)
- SEC (1)
Organisationseinheit der BAM
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.2 Biophotonik (1)
- 1.7 Organische Spuren- und Lebensmittelanalytik (1)
- 5 Werkstofftechnik (1)
- 5.6 Glas (1)
- 6 Materialchemie (1)
- 6.3 Strukturanalytik (1)
- 6.6 Physik und chemische Analytik der Polymere (1)
- 7 Bauwerkssicherheit (1)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (1)
In recent years, an increasing trend towards investigating and monitoring the contamination of the environment by microplastics (MP) (plastic pieces < 5 mm) has been observed worldwide. Nonetheless, a reliable methodology that would facilitate and automate the monitoring of MP is still lacking. With the goal of selecting practical and standardized methods, and considering the challenges in microplastics detection, we present here a critical evaluation of two vibrational spectroscopies, Raman and Fourier transform infrared (FTIR) spectroscopy, and two extraction methods: thermal extraction desorption gas chromatography mass spectrometry (TED-GC-MS) and liquid extraction with subsequent size exclusion chromatography (SEC) using a soil with known contents of PE, PP, PS and PET as reference material. The obtained results were compared in terms of measurement time, technique handling, detection limits and requirements for sample preparation. The results showed that in designing and selecting the right methodology, the scientific question that determines what needs to be understood is significant, and should be considered carefully prior to analysis. Depending on whether the object of interest is quantification of the MP particles in the sample, or merely a quick estimate of sample contamination with plastics, the appropriate method must be selected. To obtain overall information about MP in environmental samples, the combination of several parallel approaches should be considered.
Polyether and -ester urethanes (PU) were exposed to artificial weathering at 40 °C and artificial UV radiation in a weathering chamber. In 3 parallel exposures, humidity was varied between dry, humid, and wet conditions. Material alteration was investigated by various analytical techniques like size exclusion chromatography
(SEC), liquid chromatography-infrared spectroscopy (LC-FTIR), thermal-desorption gas chromatography-mass spectrometry (TD-GC-MS), fluorescence mapping and dynamic mechanical analysis (DMA). Our results show that depending on the weathering conditions, different degradation effects can be observed. By means of SEC an initial strong decrease of the molar masses and a broadening of the mass distributions was found. After a material dependent time span this was followed by a plateau where molar mass changes were less significant. A minor moisture-dependent degradation effect was only found for polyester PU. Fluorescence measurements on two materials revealed an increase in the luminescence intensity upon weathering process reaching a saturation level after about 500 h. The changes in the optical properties observed after different exposure conditions and times were very similar. The TD-GC-MS data showed the fate of the stabilizers and antioxidant in the course of weathering. LC-FTIR measurements revealed a change in peak intensities and the ratio of urethane and carbonyl bands.