Martensitic phase transformations were studied in ultrafine grained Ni-rich pseudoelastic NiTi wires during cyclic deformation under small imposed strain amplitudes. Small strain variation tests were complemented by a thermographic analysis of the emerging temperature distributions in the specimens. The characteristics of the observed thermal profiles result from the specific phase transitions which take place at different stress levels. Homogeneous temperature changes, corresponding to a non-localized transformation activity along the specimen length, were observed throughout the whole range of applied stresses, starting from values as low as 100 MPa. This behavior is in line with previous literature reports for the stress-induced transformation from B2 austenite to R-phase as long as the critical stress for B19' martensite formation is not reached. In the present study, similar type of transformation activity could also be demonstrated at higher strains/stresses, even after the stress induced transformation to B19' was apparently completed. These findings suggest that transformation activity involving the B2 phase is present throughout the whole pseudoelastic stressstrain cycle; i.e., it is not restricted to the initial loading portion. Finally, non-localized transformation to or from B19' was identified during small amplitude strain variations in the plateau-like coexistence ranges of the pseudoelastic cycle.
On the stress-induced formation of R-phase in ultra-fine-grained Ni-Rich NiTi shape memory alloys
(2011)
Phase transformations in binary ultra-fine-grained (UFG) pseudoelastic NiTi wires were studied in a wide temperature range using mechanical loading/unloading experiments, resistance measurements, differential scanning calorimetry (DSC), thermal infrared imaging, and transmission electron microscopy (TEM). The formation of R-phase can be detected in the mechanical experiments. It is shown that the stress-strain response of the R-phase can be isolated from the overall stress-strain data. The R-phase always forms prior to B19¢ when good pseudoelastic properties are observed. The stress-induced B2 to R-phase transition occurs in a homogeneous manner, contrary to the localized character of the B2/R to B19' transformations. The temperature dependence of the critical stress values for the formation of the martensitic phases shows a Clausius Clapeyron type of behavior with constants close to 6 MPa/K (B19') and 18 MPa/K (R-phase). A stress-temperature map is suggested that summarizes the experimentally observed sequences of elementary transformation/deformation processes.
The transformation between the cubic B2 and monoclinic B19' phases in ultrafine-grained pseudoelastic NiTi can occur as a two-step process involving the intermediate rhombohedral R-phase. Experimental work using differential scanning calorimetry, electrical resistance measurements and transmission electron microscopy has demonstrated the formation of this intermediate phase during thermal cycling and during mechanical loading. In the present paper, complementary mechanical and thermographic results are presented which allow to further assess the character of the stress-induced R-phase formation. The transformation from B2 to R-phase is demonstrated to occur homogeneously within the gauge length rather than via advancing Lüders-type transition regions as it is the case in the localized transformation from B2 or R-phase to B19'.