Filtern
Erscheinungsjahr
- 2007 (10) (entfernen)
Dokumenttyp
Schlagworte
- LTCC (4)
- Inclusions (3)
- Sintern (3)
- Glasmatrixkomposite (2)
- Glass matrix composites (2)
- Lösung (2)
- Modeling (2)
- Sintering kinetics (2)
- Effective Viscosity (1)
- Glas Matrix Composites (1)
- Glass Matrix Composites (1)
- Glass transitions (1)
- Glasses (1)
- Grenzflächenreaktionen (1)
- Keramische Multilayer (1)
- Kinetic Modelling (1)
- Laser ablation (1)
- Modelling (1)
- Optical fibers (1)
- Physical radiation damage (1)
- Radiation treatment (1)
- Rigid Inclusion (1)
- Sintering (1)
- Sintering Kinetics (1)
Eingeladener Vortrag
- nein (2)
We studied sintering of LTCC-type glass matrix composites (GMCs) consisting of small glass and alumina particles of equal size. Primarily, crystals act as rigid inclusions, decelerating the densification rate. In later stages, they also dissolve, partially increasing the viscosity. Release of alumina finally induces crystallization of alumosilicates, which enables post-firing stability. To study both effects, two model GMCs were prepared: an α-Al2O3 + barium alumoborosilicate glass (BABS)GMC, which shows neither significant dissolution nor crystallization, and an α-Al2O3 + calcium alumoborosilicate glass (CABS)GMC, which dissolves readily and promotes crystallization. The kinetics of shrinkage for both GMC were modeled by utilizing Frenkel theory for the early stage and MackenzieShuttleworth theory for the late stage, assuming that sintering is superimposed by the weighted contributions of triparticle glasscrystal clusters, their random occurrence (ideal mixing), and a shrinkage rate controlled by the GMC effective viscosity. In agreement with modeling, the experimental results showed that the shrinkage rate of BABSGMC decreases progressively for crystal volume fractions Φ > 0.15. The attainable shrinkage is reduced by up to 8% for Φ = 0.45. For the CABSGMC with Φ = 0.25, a reduction of Φ to 0.20 was evident due to partial α-Al2O3 dissolution. This effect was found able to increase the sintering temperature by ~5060 K.
Optical multimode fibers are applied in materials processing (e.g. automotive industry), defense, aviation technology, medicine and biotechnology. One challenging task concerning the production of multimode fibers is the enhancement of laser-induced damage thresholds. A higher damage threshold enables a higher transmitted average power at a given fiber diameter or the same power inside a thinner fiber to obtain smaller focus spots.
In principle, different material parameters affect the damage threshold. Besides the quality of the preform bulk material itself, the drawing process during the production of the fiber and the preparation of the fiber end surfaces influence the resistance. Therefore, the change of the laser-induced damage threshold of preform materials was investigated in dependence on a varying thermal treatment and preparation procedure.
Single and multi-pulse laser-induced damage thresholds of preforms (F300, Heraeus) were measured using a Q-switched Nd:YAG laser at 1064 nm wavelength emitting pulses with a duration of 15 ns, a pulse energy of 12 mJ and a repetition rate of 10 Hz. The temporal and spatial shape of the laser pulses were controlled accurately.
Laser-induced damage thresholds in a range from 150 J cm-2 to 350 J cm-2 were determined depending on the number of pulses applied to the same spot, the thermal history and the polishing quality of the samples, respectively.