Filtern
Dokumenttyp
- Zeitschriftenartikel (18) (entfernen)
Schlagworte
- LTCC (7)
- Sintering (5)
- Glass ceramic composites (2)
- Glasses (2)
- Inclusions (2)
- Physical radiation damage (2)
- Radiation treatment (2)
- Al2O3-inclusions (1)
- Alumina dissolution (1)
- Coefficient of thermal expansion (CTE) (1)
For many applications, optical multimode fibers are used for the transmission of powerful laser radiation. High light throughput and damage resistance are desirable. Laser-induced breakdown at the end faces of fibers can limit their performance. Therefore, the determination of laser-induced damage thresholds (LIDT) at the surface of fibers is essential.
Nanosecond (1064 nm and 532 nm wavelength) single-shot LIDT were measured according to the relevant standard on SiO2 glass preforms (Suprasil F300) as basic materials of the corresponding fibers. For 10 kinds of fused silica fibers (FiberTech) with core diameters between 180 µm and 600 µm, an illumination approach utilizing a stepwise increase of the laser fluence on a single spot was used. For both wavelengths, the LIDT values (0% damage probability) obtained by means of the two methods were compared. The influence of surface preparation (polishing) on damage resistance was investigated. For equal surface finishing, a correlation between drawing speed of the fibers and their surface LIDT values was found. In addition to the surface measurements, bulk LIDT were determined for the preform material.
New applications of low-temperature co-fired ceramics (LTCC), such as pressure sensors or integrated functional layers, require materials that possess higher coefficients of thermal expansion (CTE). To fabricate LTCC with elevated CTE, two methods of material design are examined: firstly, glass ceramic composites (GCC), which consist of >50 vol% glass in the starting powder, and, secondly, glass-bonded ceramics (GBC), where glass is added as a sintering aid only. The CTE of GBC is mainly determined by the crystalline component. For GCC, the CTE can be well predicted, if CTE and elastic data of each phase in the microstructure are known. A nonlinear characteristic of the CTE versus phase composition was found with increasing Ecrystals/Eglass ratio and absolute CTE difference between the components. The glass composition and glass amount can be used to compensate the fixed properties of a crystalline material in a desired way. However, because the CTE and permittivity of a glass cannot be chosen independently, an optimum glass composition has to be found. For a given LTCC, it is possible to control the devitrification by shifting the glass composition. In this way, the resulting CTE values can be predicted more exactly and tailoring becomes possible. Different LTCC materials, based on the crystalline compounds Ba(La,Nd)2Ti4O12, ZrO2 (Y-TZP), SiO2 (quartz), and specially developed glasses, possessing an elevated CTE of around 10 × 10-6 K-1 while showing permittivity εr between 6 and 63, are introduced.
The sintering of Low Temperature Co-fired Ceramics prepared from alumoborosilicate
glass- and Al2O3 powders of similar small particle size was studied by dilatometry, heating microscopy,
microstructure analysis, glass- and effective viscosity measurements. The steric effect of
Al3O3 inclusions was studied using a gnon-reactiveh model composite. With increasing Al3O3 volume
fraction (Φ ≤ 0.45), sintering decelerates and its final stage shifts to higher temperature. The
attainable shrinkage is reduced as Al2O3 particle clusters bearing residual pores become more frequent.
The kinetics of sintering could be described formally superposing the weighed contributions
of differentially sized and randomly composed glass-crystal particle clusters and assuming a sintering
rate controlled by the effective matrix viscosity, which increases with Φ and with progressive
wetting of Al2O3 particles during densification. The "reactive" model composite shows significant
dissolution of Al2O3 into the glass, which has two opposed effects on sintering: reducing Φ and increasing
glass viscosity. For the present case (Φ = 0.25), the latter effect dominates and sintering is
retarded by Al2O3 dissolution. Crystallization of wollastonite starts after full densification. Dissolution
of Al2O3 was found to promote the subsequent growth of anorthite.
The relation between ablation threshold fluence upon femtosecond laser pulse irradiation and the average dissociation energy density of silicate based multicomponent glass is studied. A simple model based on multiphoton absorption quantifies the absorbed energy density at the ablation threshold fluence. This energy density is compared to a calculated energy density which is necessary to decompose the glass compound into its atomic constituents. The results confirm that this energy density is a crucial intrinsic material parameter for the description of the femtosecond laser ablation threshold fluence of dielectrics.
Single and multi pulse laser-induced damage thresholds (LIDT) of core, cladding, and coating materials of high-power
optical multimode fibers were determined in accordance with ISO 11254 for 532 nm and 1064 nm wavelength in the 10-ns
pulse duration regime with spatial Gaussian beam shape. For all-silica fibers, LIDT increases with rising core diameter in a range between 100-600 µm for a constant cladding-core ratio of 1.2. The damage resistance of the low refracting cladding (0.3 % fluorine doped fused silica) is comparable to the undoped SiO2 core. Coating materials show significantly lower LIDT than light-guiding parts of the fibers.
High-power optical multimode fibers are essential components for materials processing
and surgery and can limit the reliability of expensive systems due to breakdown at the end faces.
The breakdown threshold of fibers is determined by intrinsic materials properties and parameters of
the technology applied. The aim of this paper is the identification of technological parameters that
are crucial for the fiber quality.
Fibers were drawn from preforms of Heraeus SWU with core material F300 and a low amount of
OH-. Both, the cladding (fluorine doped SiO2) to core diameter ratio (CCDR) and the drawing speed
were varied. CCDR values between 1.05 and 1.4 were used. Afterwards, the laser-induced damage
thresholds (LIDT) of the fibers were determined. For comparison, also samples from preforms,
which underwent different thermal treatments above the transition temperature, were tested with
respect to their damage resistivity. Single and multi pulse LIDT measurements were done in
accordance with the relevant ISO standards. Nd:YAG laser pulses with durations of 15 ns (1064 nm
wavelength) and 8.5 ns (532 nm) at a repetition rate of 10 Hz were utilized. For the fibers, LIDT
values (1-on-1, 1064 nm and 532 nm) increased with growing CCDR and with decreasing drawing
velocities.