In the mechanical friction and wear process, normal and tangential (shear) forces cause elastic and plastic deformations, generate cracks and form loose wear particles through fracture processes. Depending on the working conditions, the material properties and the real contact Situation (topography), a third body is formed as a mechanical ly mixed layer, which determines different running-in and steady-state behaviours.
Two dimensional (2D) MCA Simulation results will be described via empirical equations, which are related to the incubation time (period without wear) and the following running-in wear rate (kinetic concept of strength, fatigue wear model).
In order to understand the running-in and steady-state wear, kinetic model equations for mass balance of the third body are useful and are therefore to be included in the investigation.
For a more complex material behaviour, numerical Simulation results are also presented for friction at the pad-disk interface of automotive brakes.
In part 1 it was shown that tribofilms usually are 100 nm thick and exhibit a multiphase nanocrystalline structure. The objective of our modelling efforts was to obtain a better understanding of the sliding behaviour and associated friction properties and to study the impact of internal and external parameters on these properties. The method of movable cellular automata (MCA) was used. The third bodies were considered as aggregates of linked nanoparticles which may decompose and form a layer of granulär material, the so-called mechanically mixed layer (MML), if certain fracture criteria are fulfilled. The basic model structure which consists of Fe3Ü4 nanoparticles with 13 % graphite inclusions was used. In order to assess the robustness of the model the following parameter studies were performed. The pressure ränge at an asperity contact was varied between 15 and 50 MPa. The mechanical properties of the oxide were varied between brittle and ductile behaviour corresponding to room temperature and high temperature behaviour. The mechanical properties of the soft ingredient were varied + 50 % of the properties of graphite. The influence