Filtern
Dokumenttyp
Sprache
- Englisch (18)
Referierte Publikation
- nein (18) (entfernen)
Schlagworte
- Tribofilm (4)
- Movable cellular automata (3)
- Sliding simulation (3)
- Third body (3)
- Automotive braking (2)
- Friction (2)
- MCA-modeling (2)
- Mechanically mixed layer (2)
- Amorphous silica (1)
- Bremse (1)
- Computer simulation (1)
- Copper (1)
- Copper particles (1)
- Dritter Körper (1)
- Dry friction (1)
- Dry sliding (1)
- Friction control (1)
- Friction film (1)
- Friction films (1)
- Friction layer (1)
- Friction materials (1)
- Friction-induced vibrations (1)
- MCA model (1)
- MCA-modelling (1)
- Modellierung (1)
- Modelling (1)
- Molecular dynamics (1)
- Nanocharakterisierung (1)
- Nanostructure (1)
- Noise propensity (1)
- Reibung (1)
- Resistance stress (1)
- Sliding behaviour (1)
- Solid lubricant (1)
- Thin tribofilm (1)
- Verschleiß (1)
- amorphous carbon film (1)
- amorphous silica film (1)
- dry friction (1)
- molecular dynamics (1)
- sliding simulation (1)
Organisationseinheit der BAM
The sliding behaviors of two simplified tribofilms with amorphous structure consisting either of SiO₂ molecules or C atoms were simulated by molecular dynamics modeling. The objective was to identify mechanisms explaining the experimentally observed lubricating properties of the two amorphous films. The impacts of layer thickness, normal pressure, temperature and different substrate materials were studied systematically, while the sliding velocity was kept constant at 30 m/s. While the layer thickness was not critical, all the other parameters showed special effects under certain conditions. Normal pressure impeded void formation and could even eliminate voids if applied at high temperature. Stick-slip sliding was changed to smooth sliding at high temperature due to void healing. Considering the carbon film, high friction forces and shearing of the entire film was observed with diamond substrates, whereas interface sliding at low friction forces and an amorphous layer of iron mixed with carbon was observed if the supporting substrates consisted of α-Fe. Both films show a decrease of friction forces and smooth sliding behavior at elevated temperature, corresponding well to the tribological behavior of and advanced nanocomposite sliding against a steel disc under severe stressing conditions when high flash temperatures can be expected.
In the mechanical friction and wear process, normal and tangential (shear) forces cause elastic and plastic deformations, generate cracks and form loose wear particles through fracture processes. Depending on the working conditions, the material properties and the real contact Situation (topography), a third body is formed as a mechanical ly mixed layer, which determines different running-in and steady-state behaviours.
Two dimensional (2D) MCA Simulation results will be described via empirical equations, which are related to the incubation time (period without wear) and the following running-in wear rate (kinetic concept of strength, fatigue wear model).
In order to understand the running-in and steady-state wear, kinetic model equations for mass balance of the third body are useful and are therefore to be included in the investigation.
For a more complex material behaviour, numerical Simulation results are also presented for friction at the pad-disk interface of automotive brakes.