Filtern
Dokumenttyp
Schlagworte
- Welding (4)
- Eigenspannungen (3)
- Schweißen (3)
- LTT (2)
- LTT Weld Filler Materials (2)
- Residual stress (2)
- Schwingfestigkeit (2)
- ADXRD (1)
- AXRD (1)
- Bauteilprüfung (1)
- Beanspruchungsanalyse (1)
- Creep resistant steel (1)
- Eigenspannung (1)
- Einspanngrad (1)
- Fatigue strength (1)
- Feinkornbaustahl (1)
- HSLA (1)
- High strength steel (1)
- Hochfester Stahl (1)
- Hot Cracks (1)
- LTT-Zusatzwerkstoff (1)
- Large-scale test (1)
- Low transformation temperature (1)
- Low transformation temperature filler materials (1)
- MAG (1)
- Multi-pass welding (1)
- Neutronenbeugung (1)
- Phase transformation (1)
- Synchrotron diffraction (1)
- Synchrotronbeugung (1)
- Wärmeführung (1)
- contour method (1)
- neutron diffraction (1)
- residual stress analysis (1)
- µCT-analysis (1)
Organisationseinheit der BAM
- 9 Komponentensicherheit (9) (entfernen)
Investigations on weldability often deal with hot cracking as one of the most prevalent failure mechanisms during weld fabrication. The modified varestraint transvarestraint hot cracking test (MVT) is well known to assess the hot cracking susceptibility of materials. The shortcoming of this approach is that the information is only from the very near surface region which inhibits access to the characteristic of the hot crack network in the bulk. Here, we report about an alternative approach to monitor the entire 3D hot crack network after welding by means of microfocus X-ray computer tomography (µCT). However, to provide sufficient high spatial resolution small samples must be sectioned from the MVT-welded joint. The sampling is accompanied by local relaxation of the residual stress distributions that are induced by welding, which can have an impact on the crack volumes prior to the sampling. The studies were carried out to investigate the hot cracking susceptibility of low transformation temperature filler materials (LTT). As high compression residual stresses up to -600 MPa in the area of the crack networks were determined by means of the contour method, stress relaxation caused by sectioning for µCT sample extraction can affect the detectability of the cracks later on. X-ray diffraction studies revealed surface residual stress relaxations up to about 400 MPa due to cutting. To investigate this effect, the specimens with hot cracks were subjected to a load test with known stress states. The results clearly show that local stress relaxations will have a strong impact on the volume images reconstructed from tomography analysis. This effect must be considered during hot crack assessment on basis of µCT data.
Die Verwendung von LTT-Zusatzwerkstoffen stellt einen alternativen Ansatz zu den sonst üblichen Verfahren der Schweißnahtnachbehandlung zur Schwingfestigkeitserhöhung geschweißter Stahlkonstruktionen dar. Der wesentliche Wirkmechanismus beruht auf der Beeinflussung des Eigenspannungszustands durch die niedrige Martensitstarttemperatur bereits während des Schweißens. Dadurch werden die Druckeigenspannungen aus der behinderten Volumenausdehnung infolge Phasenumwandlung voll wirksam. Weiter weist die Schweißnaht eine hohe Härte auf, die die Schwingrissbildung verzögern kann, allerdings auch zu einer niedrigen Kerbschlagarbeit führt.
Im ersten Teil dieses Beitrages werden grundlegende Untersuchungen zur schweißtechnischen Verarbeitung eines LTT-Zusatzwerkstoffes präsentiert. Dies beinhaltet zunächst die Sicherstellung der Schweißbarkeit sowie die Charakterisierung der Schweißgefüge und deren Härte mit dem Ziel, reproduzierbare Verbindungseigenschaften für die nachfolgende Schwingfestigkeitsprüfung herzustellen. Der zweite Teil des Beitrages beschäftigt sich mit den dazugehörigen Schwingfestigkeitsuntersuchungen an den Stählen S355J2 und S960Q unter Verwendung konventioneller Zusatzwerkstoffe im Vergleich zum LTT-Zusatz.
Das verwendete Schweißdetail ist eine Verbindungsschweißung am Stumpfstoß unter Variation der Schweißnahtausführung (DY-Naht und V-Naht). Weitergehend wird eine bauteilähnliche Probe (die Längssteife) untersucht, bei der der LTT-Zusatzwerkstoff als zusätzliche Schweißlage aufgebracht wurde. Neben der Schwingfestigkeit werden die Schweißnähte hinsichtlich der Eigenspannungen, der Eigenspannungsstabilität im Schwingversuch sowie metallografisch charakterisiert. Die Ergebnisse zeigen, dass LTT-Zusatzwerkstoffe unter Einhaltung wesentlicher Konstruktionsrichtlinien zu einem deutlichen Anstieg der Schwingfestigkeit führen. Dadurch kann das Leichtbaupotential hochfester Stahlgüten genutzt werden.
Compared to conventional welding consumables using low transformation temperature (LTT) filler materials is an innovative method to mitigate tensile residual stresses due to delayed martensite transformation of the weld. For the effective usage of LTT filler materials, a deeper understanding of the complex processes that lead to the final residual stress state during multipass welding is necessary. Transformation kinetics and the strain evolution of multi-pass welds during welding were investigated in situ at the beamline HEMS@PETRAIII, Germany. Compared to conventional welds, the total strain was reduced and compression strain was achieved when using LTT filler materials. For an optimal use of the LTT effect in the root of multi-pass welds, the alloying concept must be adapted taking care of dilution.
Residual stresses are crucial when assessing the performance of welded components. The present work deals with the possibilities of transferring the real-life boundary conditions of welding, which influence the residual stress, into the laboratory. The possibilities of a test system specifically developed for this purpose with a maximum capacity of 2 MN are shown. Due to the structural design, global process, geometry and material-dependent stresses are induced, which can be simulated and quantified within the system. Additionally, X-ray diffraction can be applied to determine the resulting local residual stress distribution precisely with high spatial resolution. Two examples are presented how the conditions to be found during production are simulated in the laboratory. It is shown how welding residual stresses in high-strength steels are affected by the heat control. It was possible to clarify why elevated working temperatures significantly increase the bending stresses in the welded joint and therefore the tensile residual stresses in the heat affected zone (HAZ). The effect of a heat treatment applied under mechanical stress resulting from welding is demonstrated by the example of a creep resistant steel. Reheat cracking is significantly increased in this case compared to small scale laboratory based tests.
Two-dimensional residual stress mapping of multilayer LTT weld joints using the contour method
(2018)
Low transformation temperature (LTT) weld filler materials offer an attractive alternative to cost intensive postweld treatments as they can mitigate detrimental welding residual stresses during the welding process. Compared to conventional weld filler materials, LTT alloys are characterized by a delayed martensite transformation at low temperatures, which can result in compressive residual stresses in the weld. The high strength of these filler materials makes them potentially applicable to high-strength steels as well as for a large amount of requested repair works in steel structures. The focus of the study is on the confirmation of the LTT idea with regard to the residual stress state for multipass weld lines processed by metal active gas welding. It is demonstrated that the contour method is a well-suited technique for measuring the residual stress in the weld joint as it gives an entire two-dimensional map of the residual stress state in the weld line, heat affected zone (HAZ), and base material. The technique was applied at different LTT alloys with varying chemical compositions. Additionally, the results are compared to residual stress maps that were determined by Neutron diffraction using the Strain Analyzer for Large Scale Engineering Applications, an
instrument referred to as SALSA, at the Institut Laue-Langevin in Grenoble. For all investigated specimens, compressive residual stress distributions were determined in the area of the weld joint and the HAZ. They are balanced by tensile residual stresses in the surrounding base material. However, it is shown that the size of theregion exhibiting compressive residual stresses and the absolute values of the compressive residual stresses depend on the chemical composition of the weld filler material.
The use of low transformation temperature (LTT) filler materials represents a smart approach for increasing the fatigue strength of welded high strength steel structures apart from the usual procedures of post weld treatment. The main mechanism is based on the effect of the low start temperature of martensite formation on the stress already present during welding. Thus, compressive residual stress formed due to constrained volume expansion in connection with phase transformation become highly effective. Furthermore, the weld metal has a high hardness that can delay the formation of fatigue cracks but also leads to low toughness. Fundamental investigations on the weldability of an LTT filler material are presented in this work, including the characterization of the weld microstructure, its hardness, phase transformation temperature and mechanical properties. Special attention was applied to avoid imperfections in order to ensure a high weld quality for subsequent fatigue testing. Fatigue tests were conducted on the welded joints of the base materials S355J2 and S960QL using conventional filler materials as a comparison to the LTT filler. Butt joints were used with a variation in the weld type (DY-weld and V-weld). In addition, a component-like specimen (longitudinal stiffener) was investigated where the LTT filler material was applied as an additional layer. The joints were characterized with respect to residual stress, its stability during cyclic loading and microstructure. The results show that the application of LTT consumables leads to a significant increase in fatigue strength when basic design guidelines are followed. This enables a benefit from the lightweight design potential of high-strength steel grades.
Die Verwendung von LTT-Zusatzwerkstoffen stellt einen alternativen Ansatz zu den sonst üblichen Verfahren der Schweißnahtnachbehandlung zur Schwingfestigkeitserhöhung geschweißter Stahlkonstruktionen dar. Der wesentliche Wirkmechanismus beruht auf der Beeinflussung des Eigenspannungszustands durch die niedrige Martensitstarttemperatur bereits während des Schweißens. Dadurch werden die Druckeigenspannungen aus der behinderten Volumenausdehnung infolge Phasenumwandlung voll wirksam. Weiter weist die Schweißnaht eine hohe Härte auf, die die Schwingrissbildung verzögern kann, allerdings auch zu einer niedrigen Kerbschlagarbeit führt.
Im vorliegenden Forschungsvorhaben wurden grundlegende Untersuchungen zur schweißtechnischen Verarbeitung eines LTT-Zusatzwerkstoffes durchgeführt. Dies beinhaltet die Sicherstellung der Schweißbarkeit sowie die Charakterisierung der Verbindungseigenschaften.
Untersuchungen zur Schweißeignung machten deutlich, dass ein sicherer Einsatz in dem für hochfeste Stähle zur Verfügung stehenden Arbeitsfenster möglich ist. Der verwendete LTT-Zusatz auf Cr-Ni-Basis lässt sich mit hoher Nahtgüte fügen. Auch die mechanischen Eigenschaften erlauben den Einsatz im Bereich hochfester Stähle mit einer Streckgrenze von 960 MPa. Entwicklungspotential gibt es hinsichtlich der Zähigkeit. Die in dieser Arbeit erreichten Kerbschlagwerte liegen deutlich unter denen kommerziell verfügbarer konventioneller Schweißgüter. Die Untersuchungen belegen, dass der Effekt der martensitischen Phasenumwandlung im gesamten Schweißgut zum Tragen kommt. Die angestrebten hohen Druckeigenspannungen finden sich vornehmlich im Schweißgutinnern.
Im weiteren Vorgehen wurden Schwingfestigkeitsuntersuchungen an den Stählen S355J2 und S960Q unter Verwendung konventioneller Zusatzwerkstoffe im Vergleich zum LTT-Zusatz durchgeführt. Die verwendeten Konstruktionsdetails sind ein Stumpfstoß unter Variation der Schweißnahtausführung (DY-Naht und V-Naht), ein Kreuzstoß mit HV-Naht sowie ein Überlappstoß mit einseitig und beidseitig geschweißter Kehlnaht.
Weitergehend wurde eine bauteilähnliche Probe (die Längssteife) untersucht, bei der der LTT-Zusatzwerkstoff als zusätzliche Schweißlage aufgebracht wurde. Neben der Schwingfestigkeit wurden die Schweißnähte hinsichtlich der Eigenspannungen, der Eigenspannungsstabilität im Schwingversuch sowie metallografisch charakterisiert.
Eine generell positive Wirkung des LTT-Zusatzwerkstoffes im Hinblick auf die Schwingfestigkeitssteigerung kann nicht bestätigt werden. Teilweise ist eine Steigerung der Schwingfestigkeit bei Substitution konventioneller Zusatzwerkstoffe zu beobachten, teilweise zeigt sich kein Effekt. Ursächlich hierfür ist die bei manchen Stoßformen mangelnde Steifigkeit quer zur Schweißnaht, die zur Ausbildung hoher Druckeigenspannungen infolge Phasenumwandlung notwendig wäre. Die bauteilähnliche Längssteife bestätigt allerdings das grundlegende Potential der LTT-Zusatzwerkstoffe bei Vorliegen hinreichender Steifigkeit.
Von der Anwendung ins Prüflabor: Maßstabsgetreues Bewerten von Spannungen in geschweißten Bauteilen
(2019)
Eigenspannungen sind von zentraler Bedeutung für die Performance geschweißter Bauteile. Die Bewertung schweißbedingter Beanspruchungen im Labormaßstab ist oft nicht zielführend. Reale Bauteilschweißungen weisen geometrisch und konstruktiv bedingt meist divergente Wärmeableitungs- und Einspannbedingungen auf. Dadurch lassen sich häufig nur eingeschränkt Aussagen über Eigenspannungshöhen, -verteilungen und die wesentlichen Einflussfaktoren treffen. Dies führt oftmals zur eher konservativen Konstruktionsauslegung und damit zu einer geringerenRessourcen- und Energieeffizienz. Dieser Beitrag widmet sich den Bestrebungen, reale Randbedingungen beim Bauteilschweißen in das Labor zu übertragen. Es werden die Möglichkeiten eines speziell für diesen Zweck an der BAM entwickelten Prüfsystems mit einer maximalen Tragkraft von 2 MN aufgezeigt. Durch die konstruktive Gestaltung der Anlage lassen sich in Schweißversuchen schweißbedingte Beanspruchungen nachbilden und die komplexen Einflüsse und Wechselwirkungen durch Schweißprozess, Bauteilgeometrie und -konstruktion sowie durch die eingesetzten Grund- und Zusatzwerkstoffe quantifizieren. Darüber hinaus können mittels Röntgenbeugung die resultierenden lokalen Eigenspannungen präzise und mit hoher Ortsauflösung bestimmt werden. Anhand von Beispielen wird die Nachbildung realer Produktionsbedingungen im Labor erörtert und gezeigt, wie die Spannungen beim Schweißen hochfester Baustähle von konstruktiven, werkstoff- und prozessseitigen Randbedingungen abhängen.
So wurde geklärt, wie erhöhte Arbeitstemperaturen zum signifikanten Anstieg der Beanspruchungen führen.
Bestrebungen zum Leichtbau sowie höhere Anforderungen an das ertragbare Lastkollektiv führen in der Auslegung von Schweißkonstruktionen zunehmend zum Einsatz hochfester Feinkornbaustähle. Ohne Anwendung kostenintensiver Nachbehandlungsverfahren ist die Lebensdauer hochfester Schweißverbindungen unter wechselnder zyklischer Beanspruchung jedoch limitiert. Neben der geometrischen Kerbe sind schweißbedingte Gefügeveränderungen und die Höhe und die Verteilung von Schweißeigenspannungen für die Eigenschaften von Schweißverbindungen von erheblicher Bedeutung. Sogenannte LTT-Zusatzwerkstoffe bieten eine äußerst lukrative Möglichkeit, die resultierenden Schweißeigenspannungen bereits während des Schweißens zu adaptieren. Durch die gezielte Ausnutzung der mit der martensitischen Phasenumwandlung verbundenen Volumenausdehnung können bei hinreichend niedriger Umwandlungstemperatur Druck oder niedrige Zugeigenspannungen induziert werden. Bisherige Untersuchungen konzentrieren sich vorrangig auf die Entwicklung von LTT-Legierungskonzepten sowie dem Nachweis von Druckeigenspannungen, bieten jedoch nur wenige Erkenntnisse zum Einfluss der Wärmeführung, vor allem der Zwischenlagentemperatur, oder der Schrumpfbehinderung auf die Beanspruchung von LTT- Mehrlagenschweißverbindungen unter realitätsnahen Fertigungsbedingungen.
Die Interaktion zwischen der martensitischen Phasenumwandlung und den thermischen bzw. den mechanischen Einflussfaktoren auf die Schweißeigenspannungen wurde einleitend durch elementare Schweißversuche analysiert. Mit Hilfe des Temperaturgradienten wurde der Einfluss der behinderten thermischen Schrumpfung auf den Eigenspannungszustand in LTT-Schweißverbindungen erstmalig richtungsabhängig verstanden. Unter der Vorlage eines hohen Einspanngrades wurden Druckspannungen bevorzugt aufgebaut, wenn der Temperaturgradient während der Phasenumwandlung nur schwach ausgeprägt war. Dabei durchgeführte In-situ-Beugungsexperimente haben gezeigt, dass der Einspanngrad nur in Zusammenhang mit der richtungsabhängig vorliegenden behinderten thermischen Schrumpfung zu betrachten ist, um die Beanspruchung einer Schweißverbindung unter konstruktiver Schrumpfbehinderung bauteilübergreifend bewerten zu können.
Anschließend wurden Mehrlagenschweißversuche unter freier Schrumpfung sowie in einer speziellen Prüfanlage unter konstruktiver Schrumpfbehinderung und realistischen Fertigungsbedingungen durchgeführt. Es gelang der Nachweis, dass durch die Verwendung von LTT-Legierungen das Reaktionsmoment Mx gegenüber einer konventionellen Schweißverbindung unabhängig von der Zwischenlagentemperatur reduziert wird. Dennoch nimmt die Reaktionsspannung σ_total mit zunehmender Zwischenlagentemperatur zu. Mit Hilfe des Temperaturgradienten wurde der Einfluss der behinderten thermischen Schrumpfung auf die lokale und die globale Beanspruchung der untersuchten Schweißverbindungen interpretiert. Unabhängig von der genutzten Zwischenlagentemperatur lag für die LTT-Stumpfstoßverbindungen vor allem in Longitudinalrichtung nur eine geringe Schrumpfbehinderung während der martensitischen Phasenumwandlung vor. Dadurch wurden während der Abkühlung vor allem im Volumen Druckspannungen in Longitudinalrichtung aufgebaut. Der Eigenspannungszustand von LTT-Verbindungen wird darüber hinaus durch inhomogene Phasenumwandlung der Schweißnaht infolge von Konzentrationsunterschieden verschiedener Elemente im Schweißgut bestimmt.