Filtern
Dokumenttyp
- Vortrag (4)
- Beitrag zu einem Tagungsband (3)
- Posterpräsentation (2)
- Zeitschriftenartikel (1)
Schlagworte
- Quenching and partitioning (7)
- Heat treatment (6)
- Martensitic stainless steels (4)
- EBSD (3)
- High ductility (3)
- KorroPad (3)
- Martensite (3)
- Transformation induced plasticity (3)
- Corrosion resistance (2)
- Stainless steel (2)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (4)
The novel heat treatment concept of “Quenching and Partitioning” (Q&P) enables producing low alloyed martensitic steels with high strength and formability. Therefore austenite, retaining from a quenching temperature between Mf and Ms, is stabilised by carbon diffusion. This stabilised austenite transforms in martensite (TRIP effect) under mechanical loading. Current investigations on the Q&P heat treatment of martensitic stainless steels reveal a further enhancement of mechanical properties due to higher amounts of austenite. Thus a tensile strength of 1.800 MPa and a maximum elongation of 20 % are possible, while mechanical properties under compression are much higher due to a distinct SD effect.
The presentation aims to gain a further understanding of the Q&P heat treatment and the resulting mechanical properties for the steel X46Cr13, especially the mechanical behaviour under dynamic mechanical loading condition. Results of drop work and Split Hopkinson Pressure Bar test confirms the findings of quasi static compression test. Furthermore, Charpy impact tests show higher impact toughness compared to the common heat treatment of quenching and tempering (Q&T). Complementary investigations indicate a higher corrosion resistance of Q&P compared to Q&T.
Das innovative Wärmebehandlungskonzept des „Quenching and Partitioning“ (Q&P) ermöglicht die Herstellung hochfester, martensitischer Stähle mit hoher Verformbarkeit und Duktilität. Dabei wird Restaustenit im Prozessabschnitt des Partitionierens durch Kohlenstoffdiffusion stabilisiert. Dies ermöglicht die dehnungsinduzierte Phasenumwandlung von Austenit in Martensit und erhöht die Verformbarkeit, ohne dabei die Festigkeit zu reduzieren. Bisher wenig erforscht ist die Anwendung des Q&P-Prozesses bei korrosionsbeständigen Stählen. Die vorliegende Arbeit ergänzt erste Untersuchungen von YUANG und RAABE um wichtige werkstofftechnische Kennwerte sowie um die erreichbare Korrosionsbeständigkeit. Es konnte gezeigt werden, dass im Vergleich zur standardmäßig angewandten Wärmebehandlung die mechanischen und korrosiven Eigenschaften enorm durch den Q&P-Prozess gesteigert werden.
Co-Cr-Mo-Werkstoffe sind im Bereich der Biomaterialien weit verbreitet und werden für Endoprothesen eingesetzt. Deren Lebensdauer ist jedoch durch tribologische und korrosive Dauerbelastung begrenzt. Um die Anzahl operativer Eingriffe am Patienten zu minimieren, ist es notwendig den Werkstoff hinsichtlich Verschleißbeständigkeit und Korrosionsbeständigkeit zu optimieren. Hierfür ist ein umfassendes Verständnis der legierungsabhängigen Phasenbildung und –entwicklung während Herstellung und Wärmebehandlung notwendig. An einer speziellen Co-Cr-Mo Legierung werden verschiedene Untersuchungen zur Gefügecharakterisierung durchgeführt. Dabei werden die auftretenden Phasen thermodynamisch berechnet, mittels XRD nachgewiesen, die Phasenmorphologie durch EBSD analysiert, die Elementverteilung durch EDX-Analyse ermittelt und die Ergebnisse durch Farbätzen verifiziert. Das Ziel der Untersuchungen ist es, Optimierungspotentiale bei Herstellung und Wärmebehandlung zu identifizieren.
Quenching and partitioning (Q&P) heat Treatment increases the deformability of high-strength martensitic steels. Therefore, it is necessary to have some metastable austenite in the microstructure, which transforms in martensite during plastic deformation (TRIP effect). The austenitic-martensitic microstructure is gained by an increased austenitization temperature, water quenching and additional partitioning. The partitioning enables local carbon diffusion, which stabilizes retained austenite and leads to partial reversion of martensite to austenite. The influence of partitioning time was studied for the martensitic stainless steel AISI 420 (X46Cr13, 1.4034). In line with these efforts, metallographic, XRD and EBSD measurements were performed to characterize the microstructural evolution. The mechanical properties were tested using tension and compression loading. Additional corrosion investigations showed the benefits of Q&P heat treatment compared to conventional tempering. The reversion of austenite by the partitioning treatment was verified with EBSD and XRD. Furthermore, the results of the mechanical and corrosion testing showed improved properties due to the Q&P heat treatment.
The quenching and partitioning (Q&P) heat treatment enables a higher deformability of high strength martensitic steels. The Q&P heat treatment was applied on the martensitic stainless steel 1.4034 (X46Cr13) to study the influence of partitioning time. Therefore, extensive characterizations of the mechanical properties, focussing on the materials behaviour under different mechanical load scenarios, were performed. A comprehensive analysis of the microstructural evolution was per-formed for different heat treatment and mechanical loading states. A complete solution of chromium carbides was detected to be a first requirement for successful Q&P heat treatment. The comparison of common quenching and tempering with the Q&P heat treatment verifies the extensively enhanced materials strength whereat the formability is still acceptable. The microstructural reason was detected to be an increasing aus-tenite fraction due to austenite reversion at subgrain boundaries of martensite besides the stabilising of retained austenite. Further a distinctive strength differential effect was observed.
The novel heat treatment concept, “quenching and partitioning” (Q&P) has been devel-oped for high strength steels with enhanced formability. This heat treatment involves quenching of austenite to a temperature between martensite start and finish, to receive a several amount of retained austenite. During the subsequent annealing treatment, the so called partitioning, the retained austenite is stabilized due to carbon diffusion, which results in enhanced formability and strength regarding strain induced austenite to mar-tensite transformation. In this study a Q&P heat treatment was applied to a Fe-0.45C-0.65Mn-0.34Si-13.95Cr stainless martensite. Thereby the initial quench end temperature and the partitioning time were varied to characterize their influence on microstructural evolution. The microstructural changes were analysed by dilatometer measurements, X-ray diffraction and scanning electron microscopy, including electron back-scatter diffrac-tion. Compression testing was made to examine the mechanical behaviour. It was found that an increasing partitioning time up to 30 min leads to an enhanced formability with-out loss in strength due to a higher amount of stabilized retained and reversed austenite as well as precipitation hardening.
The novel heat treatment concept, “quenching and partitioning” (Q&P) has been developed for high strength steels with enhanced formability. This heat treatment involves quenching of austenite to a temperature between martensite start and finish, to receive a several amount of retained austenite. During the subsequent annealing treatment, the so called partitioning, the retained austenite is stabilized due to carbon diffusion, which results in enhanced formability and strength regarding strain induced austenite to martensite transformation. In this study a Q&P heat treatment was applied to a Fe-0.45C-0.65Mn-0.34Si-13.95Cr stainless martensite. Thereby the initial quench end temperature and the partitioning time were varied to characterize their influence on microstructural evolution. The microstructural changes were analysed by dilatometer measurements, X-ray diffraction and scanning electron microscopy, including electron back-scatter diffraction. Compression testing was made to examine the mechanical behaviour. It was found that an increasing partitioning time up to 30 min leads to an enhanced formability without loss in strength due to a higher amount of stabilized retained and reversed austenite as well as precipitation hardening.
The novel heat treatment concept, “quenching and partitioning” (Q&P) has been developed for high strength steels with enhanced formability. This heat treatment involves quenching of austenite to a temperature between martensite start and finish, to receive a several amount of retained austenite. During the subsequent annealing treatment, the so called partitioning, the retained austenite is stabilized due to carbon diffusion, which results in enhanced formability and strength regarding strain induced austenite to martensite transformation. In this study a Q&P heat treatment was applied to a Fe-0.45C-0.65Mn-0.34Si-13.95Cr stainless martensite. Thereby the initial quench end temperature and the partitioning time were varied to characterize their influence on microstructural evolution. The microstructural changes were analysed by dilatometer measurements, X-ray diffraction and scanning electron microscopy, including electron backscatter diffraction. Compression testing was made to examine the mechanical behaviour. It was found that an increasing partitioning time up to 30 min leads to an enhanced formability without loss in strength due to a higher amount of stabilized retained and reversed austenite as well as precipitation hardening.
The novel heat treatment concept, “quenching and partitioning” (Q&P) has been developed for high strength steels with enhanced formability. This heat treatment involves quenching of austenite to a temperature between martensite start and finish, to receive a several amount of retained austenite. During the subsequent annealing treatment, the so called partitioning, the retained austenite is stabilized due to carbon diffusion, which results in enhanced formability and strength regarding strain induced austenite to martensite transformation. In this study a Q&P heat treatment was applied to a Fe-0.45C-0.65Mn-0.34Si-13.95Cr stainless martensite. Thereby the initial quench end temperature and the partitioning time were varied to characterize their influence on microstructural evolution. The microstructural changes were analysed by dilatometer measurements, X-ray diffraction and scanning electron microscopy, including electron back-scatter diffraction. Compression testing was made to examine the mechanical behaviour. It was found that an increasing partitioning time up to 30 min leads to an enhanced formability without loss in strength due to a higher amount of stabilized retained and reversed austenite as well as precipitation hardening.
The quenching and partitioning (Q+P) heat treatment enables a higher deformability of high strength martensitic steels. Therefore, it is necessary to have some metastable austenite in the microstructure, which transforms in martensite during plastic deformation (TRIP-effect). This condition is guaranteed by the quenching and the additional partitioning treatment. Due to local carbon diffusion retained austenite is stabilized and a partial reversion of austenite from martensite occurs. The Q+P heat treatment was investigated for the martensitic stainless steel 1.4034 (X46Cr13) concerning the influence of partitioning time. In line with these efforts metallographic, XRD- and EBSD-measurements were performed to characterize the microstructural evolution. The mechanical experiments included mechanical testing with different strain rates. The reversion of austenite by the partitioning treatment could be detected with EBSD- and XRD-measurements. Further-more the results of the mechanical testing showed improved values of strength and de-formability because of the Q+P heat treatment.