In situ analysis of hydrogen behaviour in stainless steels by high energy synchrotron radiation
(2011)
Hydrogen generally causes lattice distortions and phase transformations when introduced into a metal matrix. The present contribution provides a report of first in situ investigations of hydrogen effects on the lattice of the austenite and the martensite phase in a supermartensitic stainless steel using hard synchrotron radiation for respective energy dispersion diffraction measurements. Lattice distortions, such as the planar spacing expansion, have been monitored during the complete hydrogen effusion process over 24 h and are directly correlated to the dissolved hydrogen in the metal matrix. Among other results, it turned out that hydrogen at the introduced concentration level causes a reversible lattice expansion and after hydrogen effusion the lattice nearly regained its original dimensions. Hydrogen much more significantly affects the austenite phase with respect to lattice expansion than the martensite phase, but no phase transformations occur during the hydrogen desorption process.
We investigated the hydrogen distribution spatially and temporally in technical iron at room temperature. Samples were charged electrochemically and subsequently analysed by means of neutron radiography and tomography. The radiographic images allowed for a time-resolved analysis of hydrogen fluxes. The three-dimensional distribution of hydrogen measured by neutron tomography delivered valuable information for the damage analysis of hydrogen-induced cracks. For the first time hydrogen concentration gradients inside the material could be detect directly together with the cracks. The neutron radiography and tomography results were gained at the Research Reactor BER II of the HZB in Berlin.
We investigated hydrogen embrittlement and blistering in electrochemically hydrogen-charged technical iron samples at room temperature. Hydrogen-stimulated cracks and blisters and the corresponding hydrogen distributions were observed by neutron tomography. Cold neutrons were provided by the research reactor BER II to picture the sample with a spatial resolution in the reconstructed three-dimensional model of ~25 µm. We made the unique observation that cracks were filled with molecular hydrogen and that cracks were surrounded by a 50 µm wide zone with a high hydrogen concentration. The zone contains up to ten times more hydrogen than the bulk material. The hydrogen enriched zone can be ascribed to a region of increased local defect density. Hydrogen also accumulated at the sample surface having the highest concentration at blistered areas. The surfaces of the brittle fractured cracks showed micropores visualized by scanning electron microscopy. The micropores were located at grain boundaries and were surrounded by stress fields detected by electron backscattered diffraction. The cracks clearly originated from the micropores.