Dielectric and electromechanical properties of the cellular polypropylene ferroelectret films (EMFIT), combining strong piezoelectric response with a low density and softness, evidence their high potential for the air-coupled ultrasonic applications. The disadvantage of the low coupling factor is compensated by the extremely low acoustic impedance, which provides excellent matching to air and promises efficient sound transmission through the airtransducer interface. The influence of the electrodes on the electromechanical properties was investigated. Electron beam evaporation technology was adapted to the EMFIT films, and films with both-sided Au and Al electrodes were prepared without reducing or suppressing of the electromechanical properties. Finally, prototype transducers based on the EMFIT films were developed. In spite of the simple construction and absence of matching layers, high sensitivity of the EMFIT transducers was proved in the air-coupled ultrasonic experiment. Amplitude and delay time scanned images of the polyethylene step wedge with holes, obtained in both pulse-echo and transmission modes, demonstrate that non-contact ultrasonic imaging and testing with EMFIT transducers is possible.
Analysis of the dielectric and electromechanical properties of the cellular polypropylene ferroelectret films (EMFIT) evidences their high potential for the application in the air-coupled ultrasonic transducers. Simple prototype transducers, based on the EMFIT films, were developed and their high sensitivity was proved in the air-coupled ultrasonic experiment. Amplitude and delay time scanned images of the polyethylene step wedge with holes, obtained in both pulse-echo and transmission modes, demonstrate that non-contact ultrasonic imaging with EMFIT transducers is possible.
The extremely low acoustic impedance of polypropylene ferroelectret combined with its piezoelectric properties makes this material suitable for construction of aircoupled ultrasonic transducers for non-destructive testing. For the fabrication of transducers with a stable quality, the reproducibility of their key parameters is of interest.
The reproducibility was evaluated by means of (i) impedance spectroscopy and (ii) pulse-echo measurements. (i) Impedance spectroscopy was applied to identify the resonance frequency, the coupling factor and the acoustic impedance of several nominally identical transducers. (ii) Pulse-echo measurements yielded the signal form of these transducers.
The variation of the signal amplitude measured with pulseecho technique was about 10 dB. A part of this variation Comes from the deposition of transducer electrodes and another part from local variations of ferroelectret properties. The variation of the signal amplitude was caused by the observed variation of the coupling factor, which was also about 10 dB. The variation of the acoustic impedance was only about 1 dB, thus having no effect on the variation of the signal amplitude.
These results indicate that the variability can be reduced by improving the control of electrode deposition and by optimizing the production technology affecting the reproducibility of material properties.