Filtern
Erscheinungsjahr
Dokumenttyp
Sprache
- Englisch (53)
- Deutsch (11)
- Mehrsprachig (3)
Schlagworte
- TEM (10)
- Alumina (4)
- Transmission electron microscopy (4)
- Alumina coatings (3)
- Alumosol (3)
- Coatings (3)
- Corrosion protection (3)
- Nanoparticles (3)
- Oxidation (3)
- Sol-gel (3)
Organisationseinheit der BAM
- 5 Werkstofftechnik (7)
- 5.1 Mikrostruktur Design und Degradation (7)
- 5.6 Glas (3)
- 6 Materialchemie (3)
- 6.7 Materialsynthese und Design (3)
- 6.1 Oberflächen- und Dünnschichtanalyse (2)
- 6.3 Strukturanalytik (2)
- 9 Komponentensicherheit (2)
- 9.5 Tribologie und Verschleißschutz (2)
- 6.2 Material- und Oberflächentechnologien (1)
TEM-Untersuchungen der Randzonenschädigung von Aluminiumoxidkeramiken nach Schleifbearbeitung
(1996)
Es werden elektronenmikroskopische Untersuchungsergebnisse an Al2O3-Keramiken, die verschiedenen Oberflächenbearbeitungsverfahren unterworfen wurden, vorgestellt.
Die Untersuchungen dienen dem Ziel der Optimierung der Oberflächenbearbeitung von keramischen Werkstoffen, wobei der Einfluß leistungsfähiger Bearbeitungsverfahren auf die Ausbildung möglichst schädigungsarmer Oberflächenschichten, die keinen negativen Einfluß auf Festigkeitskennwerte aufweisen, betrachtet wird.
Die Wirkung verschiedener Schleif- und Polierprozesse auf Oberflächenveränderungen bearbeiteter Werkstücke wird dargestellt. Es wurde sowohl die Mikrostruktur der geschädigten Randzonenschicht als auch die des unbeeinflußten Grundmaterials mit elektronenmikroskopischen Methoden charakterisiert. Die verschiedenen Schädigungsstadien gestatten eine Einschätzung der Stärke des Störungseintrages in das Material durch verschiedene Schleif- und Polierprozesse.
Transmission electron microscopy study of rapid thermally annealed Pd/Ge contacts on IN0.53Ga0.47As
(1996)
Single walled carbon nanotubes (SWNT) have been produced in an electric arc discharge by using a graphite rod as anode which is filled with a powder mixture of graphite and metallic catalysts like nickel and yttrium. The soot material containing approximately a third of SWNT was collected from the cathode region as a soft, voluminous material. The main by-products in this process are amorphous carbon and graphitic nanoparticles which have to be removed by an appropriate purification process. The as-produced soot material was purified by gas phase oxidation in air at 355 °C. The oxidation of amorphous carbon in air is advantageous against wet chemical methods because it is better controllable. Thermogravimetric analysis and electron microscopy were used to investigate the oxidation behavior of the different kinds of carbon. Oxidation of SWNT and amorphous carbon occurs simultaneously even at moderate temperatures, whereas amorphous carbon is more rapidly oxidized than SWNT. For optimizing the purification procedure by gas phase oxidation, kinetic studies were used to determine the oxidation time for each component in the soot at a given temperature. So it is possible to remove the amorphous carbon quantitatively with minimal losses of SWNT. But it was found that graphitic nanoparticles have the highest stability against oxidation and could therefore not be quantitatively removed by this method without the complete destruction of SWNT. Therefore, the electric arc discharge process has to be a controlled process for minimum production of graphitic nanoparticles to obtain a material with a high content of SWNT.