High temperature oxidation of 9–12% Cr ferritic/martensitic steels under dual-environment conditions
(2017)
In normal operations, the opposite surfaces of the power plant components are exposed to two different environments, i.e. air/flue gas on the one side and steam on the other side. Exposure under such dual-environment can lead to accelerated corrosion of the components on the air side. The oxidation behaviour of ferritic/martensitic steel T92 was investigated under dual-environment in a specially designed test equipment. The samples were exposed to dry oxyfuel flue gas (CO2–27%N2–2%O2–1%SO2) on one side and to steam on the other side up to 1000 h at 650°C. The formation of oxide scales was characterised by optical microscopy and scanning electron microscopy with attached energy-dispersive spectroscopy. Oxidation rate of specimens under dual-Environment condition was almost three times higher than that in single-environment condition. This is explained based on hydrogen transport through the bulk alloy from the steam side to the flue gas side.
T92 steel was oxidized at 650 °C for 1000 h in dry and wet oxyfuel gases. The microstructure of inner oxide layer was investigated using scanning transmission electron microscopy and energy dispersive spectroscopy on thin lamellas of oxide cross-sections. The oxides were composed of fine equiaxed grains and separated into Fe-rich and Cr-rich regions. Fe-rich regions were wustite and iron sulphide while Cr-rich regions consisted of Fe-Cr spinel with different stoichiometries. Precipitates of (W,Mo)-rich oxides were formed within the oxide scale and beneath the oxide/alloy interface. Often iron sulphide and (W,Mo)-rich oxide were surrounded by Cr-rich spinel.