The interaction of nanosecond laser pulses in the ultraviolet wavelength range and femtosecond laser pulses in the near-infrared region with the direct semiconductor SiC and the composite compound SiC-TiC-TiB2 was investigated in respect to resulting physicochemical processes. Surface analytical techniques, such as XPS, µ-Raman, and EDX were used to identify the chemical changes between untreated and laser-treated areas. Single-pulse irradiation led to material
modifications in the condensed state in most instances. Multi-pulse results differed depending on the pulse duration. In the nanosecond case, melting of the surface and redeposited material (debris) were observed. With femtosecond pulses instead, only negligible melting and few debris could be detected. Additionally, periodic structures (ripples) appeared, with parallel orientation and in most cases two different periodicities for a particular material. Laser ablation of all the studied compound materials exhibited preferential ablation of the lighter component elements. Crystal structure changes of the irradiated surface were observed as a consequence of laser-induced melting and resolidification. An oxidation process interfered with all this processes so that unstoichiometric oxides were formed.
IR and Raman study of calcium aluminosilicate glasses of the composition xCaO.xAl2O3.(100-2x)SiO2
(2002)
Nonequilibrium vibrational excitations of para-nitroaniline (PNA, 4-nitroaniline) occurring after internal conversion from the photoexcited charge transfer state are studied by picosecond anti-Stokes Raman scattering. Vibrational excess populations with distinctly different picosecond rise and decay times are found for a number of modes with frequencies between 860 and 1510 cm1, including the overtone of a non-Raman active mode. A nonthermal distribution of vibrational populations exists up to about 6 ps after photoexcitation. The time-resolved experiments are complemented by steady-state infrared and Raman measurements as well as calculations based on density functional theory, providing a detailed analysis of the steady-state vibrational spectra of PNA and two of its isotopomers. A weakly Raman active vibration at about 1510 cm1 displays the fastest rise time and a pronounced excess population andthusrepresents the main accepting mode. We suggest that an out-of-plane mode giving rise to the overtone Raman band at this frequency acts both as coupling and accepting mode in the internal conversion process.
Selective Catalytic Reduction of Nitric Oxide by Ammonia over Egg-Shell MnOx/NaY Composite Catalysts
(2002)
A novel composite catalyst system for the selective catalytic reduction (SCR) of NOx by NH3 is described operating at temperatures lower than 470 K in the presence of water with NO conversions of 80100% at space velocities of 30,00050,000 h-1. The catalyst is prepared by egg-shell precipitation of MnO2 on the external surface of zeolite NaY. Structural and thermal stability of precipitated MnO2 as well as of the MnO2/NaY composite catalyst were characterized by N2 adsorption, X-ray diffraction, laser Raman spectroscopy, temperature-programmed reduction, and electron microscopy. MnO2 precipitated on zeolite NaY (15 wt% loading) retained its amorphous state up to calcination temperatures of 775 K. The zeolite component remained structurally intact. Calcination at higher temperatures destroyed the zeolite structure and transformed MnO2 into Mn3O4. DRIFT spectroscopic investigations revealed the presence of symmetric O=NON=O species formally corresponding to N2O3 on the composite catalyst after contact with NO. Catalytic measurements under integral flow conditions showed that the catalyst performance is associated with a close coupling of nitrite formation and its drain off from equilibria with NO/NO2 and nitrate by ammonia. Several results are in line with the diazotation mechanism, including NH3 protonation to NH4+, whereas prevailing Lewis acid sites should enable NH3 activation via amide species, thus leading to a parallel amide/nitrosamide SCR reaction route. The activity-temperature profile fulfills the requirements of a low-temperature NOx reduction catalyst for mobile diesel engines if an ammonia supply is implemented on board, e.g., by urea decomposition.