In 1981 the OECD published the Test Guideline on Particle size and size distribution. This TG is still a valid document for the measurement of particles all over the world.
When nanomaterials gained importance, ISO set up a technical commitee for Nanotechnologies in 2005 and the OECD followed this step in 2006 with the Working Party on Manufactured Nanomaterials.
In the following years ISO and OECD published several documents about nanomaterials and the systematisation developed.
In 2017 it was finally clear that nanomaterials need to be adressed in another way than chemicals and in 2020 ECHA revised the REACH-Annexes accordingly and included nanomaterials.
Unfortunately there is a little problem with this: Only a few applicable test guidelines exit for the measurement of the nanomaterials. Several test guidelines date from 1981 and do not address nanomaterials.
The logical next step for the OECD would be to publish a series of test guidelines which are indeed currently prepared and will be shown in this talk.
Finally there is an additional need for the future of NM standardisation: Digitalisation.
Vorstellung der Ergebnisse bei der Entwicklung einer neuen OECD Prüfrichtlinie zur Bestimmung der Partikelgröße und Anzahlgrößenverteilung von Nanomaterialien.
Ergebnisse:
Ideal sphärische Partikel sind gut und verlässlich mit vielen Methoden charakterisierbar.
Reale (Nicht ideale) Materialien sind gut charakterisierbar, wenn eine gewisse Homogenität und Stabilität vorliegt.
Stark inhomogene und stark agglomerierende Partikel liefern deutlich unterschiedliche Ergebnisse für verschiedene Methoden.
Partikel mit geringen Größenunterschieden lassen sich mit allen Methoden gut charakterisieren.
Partikel mit sehr deutlichen Größenunterschieden führen häufig zu einer Unterbewertung der kleineren Partikel.
Vollautomatische Partikeldetektion bei elektronenmikroskopischen Aufnahmen ist z.Zt. noch stark fehleranfällig und kann daher nicht empfohlen werden.
Es hat sich gezeigt, dass alle Methoden zur Bestimmung der Partikelgrößenverteilung Vor- und Nachteile haben. Es ist dringend zu empfehlen Größenverteilungen immer mit mindestens zwei unterschiedlichen Methoden zu bestimmen: Bildgebend und mit gute Anzahlstatistik.
Verschiedene Durchmesser wurden in der TG-PSD mit einem Indexsystem versehen, welches zukünftig Verwechslungen zwischen unterschiedlichen Durchmessern vermeiden soll.
Wird ein bestimmter Durchmesser benötigt (z.B. hydrodynamisch, aerodynamisch), muss die Methode passend gewählt werden. Eine Umrechnung von einem Durchmesser in einen anderen ist in der Regel fehlerbehaftet.
Es wurde ein einheitliches Reporting-System in der TG-PSD eingeführt.
OECD Prüfrichtlinie zur Bestimmung der Partikelgröße und Anzahlgrößenverteilung von Nanomaterialien
(2021)
Abschlusspräsentation des Projektes "OECD Prüfrichtlinie zur Bestimmung der Partikelgröße und Anzahlgrößenverteilung von Nanomaterialien" - Projektteil Nanopartikel.
Es hat sich gezeigt, dass alle Methoden zur Bestimmung der Partikelgrößenverteilung Vor- und Nachteile haben. Es wird dringend empfohlen Größenverteilungen immer mit mindestens zwei unterschiedlichen Methoden zu bestimmen: Bildgebend und mit gute Anzahlstatistik.
Verschiedene Durchmesser wurden in der TG-PSD mit einem Indexsystem versehen, welches zukünftig Verwechslungen zwischen unterschiedlichen Durchmessern vermeiden soll.
Wird ein bestimmter Durchmesser benötigt (z.B. hydrodynamisch, aerodynamisch), muss die Methode passend gewählt werden. Eine Umrechnung von einem Durchmesser in einen anderen ist in der Regel fehlerbehaftet.
Es wurde ein einheitliches Reporting-System in der TG-PSD eingeführt.
Tour de table - BAM
(2021)
Final Draft of the OECD Test Guideline for Particle Size and Particle Size Distribution of Nanomaterials.
The OECD Working Party on Manufactured Nanomaterials (WPMN) has actively worked towards understanding possible safety issues for manufactured nanomaterials and has contributed significantly to resolving these by developing Test Guidelines, Guidance Documents, Test Reports and other publications with the aim of a safe use of manufactured nanomaterials. The OECD website (www.oecd.org/science/nanosafety) and the referenced publications contain more background information.
Among others, the OECD Test Guideline “Particle Size Distribution/Fibre Length and Diameter Distributions” (TG 110, adopted in 1981) was identified to require an update to address the specific needs of manufactured nanomaterials as the TG 110 is currently only valid for particles and fibres with sizes above 250 nm. The WPMN prioritised to either update TG 110 to be applicable also to particles at the nanoscale or draft a new nanomaterial specific Test Guideline (TG). Eventually, it was decided to develop a new TG for particle size and particle size distribution measurements of nanomaterials covering the size range from 1 nm to 1000 nm for further justification. This TG overlaps with TG 110 in the size range from 250 nm to 1000 nm. When measuring particulate or fibrous materials, the appropriate TG should be selected depending on the size range of particles tested. In line with TG 110, the new TG for nanomaterials includes separate parts for particles and fibres. For the part of this TG which addresses particles, several methods applicable to nanomaterials were reviewed and included to take into account developments since 1981 when the TG110 was adopted. This TG includes the following methods: Atomic Force Microscopy (AFM), Centrifugal Liquid Sedimentation (CLS)/Analytical Ultracentrifugation (AUC), Dynamic Light Scattering (DLS), Differential Mobility Analysis System (DMAS), (Nano)Particle Tracking Analysis (PTA/NTA), Small Angle X-Ray Scattering (SAXS), Scanning Electron Microscopy (SEM), and Transmission Electron Microscopy (TEM).
For measuring the diameter and length of fibres, analysing images captured with electron microscopy is currently the only method available. This TG includes Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM).
To test the validity of this TG, an ILC was performed. Test materials were chosen to reflect a broad 68 range of nanomaterial classes, e.g. metals, metal oxides, polymers and carbon materials. Where possible, well-characterised test materials were used. Additionally, the test materials were chosen, so that they reflect a broad range of sizes representing the size range 1 nm to 1000 nm and finally,
for fibres only, aspect ratios from length/diameter of 3 to > 50.
Electron microscopy (EM) is the gold standard for the characterisation of the morphology (size and shape) of nanoparticles. Visual observation of objects under examination is always a necessary first step in the characterisation process. Several questions arise when undertaking to identify and count particles to measure their size and shape distribution. In addition to challenges with the dispersion and identification of the particles, more than one protocol for counting particles is in use. This paper focuses on precise rules for the counting of particles in EM micrographs, as this influences the measurement accuracy of the number of particles, thus implicitly affecting the size values of the counted particles. We review and compare four different, commonly used methods for counting, which we then apply in case studies. The impact of the selected counting rule on the obtained final particle size distribution is highlighted. One main aim of this analysis is to support the application of a specific, well-defined counting approach in accordance with regulatory
requirements to contribute to achieving more reliable and reproducible results. It is also useful for the new harmonised measurement procedures for determining the particle size and particle size distribution of nanomaterials.
The OECD Working Party on Manufactured Nanomaterials (WPMN) has actively worked towards understanding possible safety issues for manufactured nanomaterials and has contributed significantly to resolving these by developing Test Guidelines, Guidance Documents, Test Reports and other publications with the aim of a safe use of manufactured nanomaterials. To address the specific needs of manufactured nanomaterials, the OECD Test Guideline No. 110 “Particle Size Distribution/Fibre Length and Diameter Distributions” was identified as one of the test guidelines (TGs) to require an update. The current TG 110 (adopted in 1981) is only valid for particles and fibres with sizes above 250 nm. The WPMN prioritised to either update TG 110 to be applicable also to particles at the nanoscale or draft a new nanomaterial specific (TG).
Eventually, it was decided to develop a new TG that covers the size range from 1 nm to 1000 nm, intended for particle size and particle size distribution measurements of nanomaterials. Paragraph 11 provides further justification on the need for such measurements for nanomaterials. This TG overlaps with TG 110 in the size range from 250 nm to 1000 nm. When measuring particulate or fibrous materials, the appropriate TG should be selected depending on the size range of particles tested. In line with TG 110, the new TG for nanomaterials includes separate parts for particles and fibres.
For the part of this TG which addresses particles, several methods applicable to nanomaterials were reviewed and included to take into account developments since 1981 when the TG 110 was adopted. This TG includes the following methods: Atomic Force Microscopy (AFM), Centrifugal Liquid Sedimentation (CLS)/Analytical Ultracentrifugation (AUC), Dynamic Light Scattering (DLS), Differential Mobility Analysis System (DMAS), (Nano)Particle Tracking Analysis (PTA/NTA), Small Angle X-Ray Scattering (SAXS), Scanning Electron Microscopy (SEM), and Transmission Electron Microscopy (TEM). The method Single Particle Inductively Coupled Plasma Mass Spectrometry (sp-ICP-MS) could not be sufficiently validated within the interlaboratory comparison (ILC) carried out for the different methods in this TG (see also paragraph 6 for further details on the ILC). Applicability of sp-ICP-MS is strongly limited to nanomaterials with high mass values in combination with a sufficiently high particle size. However, the general method ICP-MS is widely used and the sp-mode for the size measurement of specific nanomaterials was successfully performed in ILCs elsewhere. The method is therefore included in the Appendix Part C of this TG, which further details the limitations of sp-ICP-MS.
For measuring the diameter and length of fibres, analysing images captured with electron microscopy is currently the only method available. This TG includes Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM).
To test the validity of this TG, an ILC was performed. Test materials were chosen to reflect a broad range of nanomaterial classes, e.g. metals, metal oxides, polymers and carbon materials. Where possible, well-characterised test materials were used.
Additionally, the test materials were chosen to reflect a broad range of sizes representing the size range 1 nm to 1000 nm. Specifically for fibres, a broad range of aspect ratios was included (length/diameter of 3 to > 50). Some of the test materials used are commercially available and further references are given in the validation report of the ILC. Sample preparation for physical chemical characterisation is critical for all listed methods. Due to the differences between individual nanomaterials and due to the wide range of individual material properties it is impossible to have a generic protocol to obtain the best possible sample preparation for every nanomaterial. Therefore, a generic protocol on sample preparation is not part of this TG. Information on sample preparation is given in the paragraphs 25-29, 33, 34 and 39 for particles and in paragraphs 159) for fibres. Further information on sample preparation of nanomaterials for physical chemical characterisation can be found in the OECD Guidance on Sample Preparation and Dosimetry for the Safety Testing of Manufactured Nanomaterials and elsewhere.