Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (85)
- Vortrag (67)
- Beitrag zu einem Sammelband (12)
- Beitrag zu einem Tagungsband (11)
- Posterpräsentation (4)
- Buchkapitel (1)
- Dissertation (1)
- Sonstiges (1)
Schlagworte
- Mikroplastik (32)
- Microplastics (22)
- Analytik (15)
- TED-GC-MS (14)
- Fire retardancy (12)
- Microplastic (12)
- Flame retardancy (9)
- Analysis (8)
- Pyrolysis (8)
- Flame retardance (7)
Organisationseinheit der BAM
- 6 Materialchemie (47)
- 6.6 Physik und chemische Analytik der Polymere (47)
- 1 Analytische Chemie; Referenzmaterialien (8)
- 5 Werkstofftechnik (6)
- 5.3 Polymere Verbundwerkstoffe (6)
- 1.4 Prozessanalytik (4)
- 1.7 Organische Spuren- und Lebensmittelanalytik (4)
- 4 Material und Umwelt (2)
- 4.3 Schadstofftransfer und Umwelttechnologien (2)
- 7 Bauwerkssicherheit (2)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (67)
The thermal decomposition and the fire behavior of glass fiber reinforced polyamide 66 (PA-66) and high impact polystyrene (HIPS) containing red phosphorus (P4) were investigated. For glass fiber reinforced PA-66, P4 promotes char formation in the condensed phase. Barrier effects and the reduction of combustible volatiles were identified as fire retardancy mechanisms. For HIPS, P4 acts in the gas phase, mainly trapping radicals. The heat release per mass loss polymer is reduced due to an incomplete combustion.
A comprehensive characterization of the thermal and the fire behaviour is presented for polypropylene (PP) flax compounds containing ammonium polyphosphate (APP) and expandable graphite as fire retardants. Thermogravimetry coupled with an evolved gas analysis (TG-FTIR) was performed to ensure a significant thermal analysis. The fire response under forced flaming conditions was studied using a cone calorimeter. The external heat flux was varied between 30 and 70 kW m-2 so that the results could be evaluated for different fire scenarios and tests. Different flammability tests (UL 94, limiting oxygen index, glow wire test, GMI 60261) were performed and the results compared with the cone calorimeter data. The different char forming mechanisms are described and the resulting fire retardancy is classified. The successful and ecological friendly fire retardancy is a technological breakthrough for PP/flax biocomposites.