Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (130)
- Vortrag (31)
- Beitrag zu einem Tagungsband (27)
- Buchkapitel (10)
- Posterpräsentation (7)
- Beitrag zu einem Sammelband (4)
- Monografie (1)
- Video (1)
Sprache
- Englisch (211) (entfernen)
Schlagworte
- Laser-induced periodic surface structures (LIPSS) (71)
- Femtosecond laser ablation (39)
- Femtosecond laser (32)
- Surface functionalization (31)
- Laser processing (23)
- Laser ablation (19)
- Laser-induced periodic surface structures, LIPSS (12)
- Silicon (12)
- Nanostructures (11)
- Applications (10)
Organisationseinheit der BAM
- 6 Materialchemie (101)
- 6.2 Material- und Oberflächentechnologien (101)
- 9 Komponentensicherheit (15)
- 9.5 Tribologie und Verschleißschutz (15)
- 6.1 Oberflächen- und Dünnschichtanalyse (10)
- 4 Material und Umwelt (7)
- 4.1 Biologische Materialschädigung und Referenzorganismen (7)
- 6.7 Materialsynthese und Design (4)
- 6.6 Physik und chemische Analytik der Polymere (3)
- 5 Werkstofftechnik (1)
Paper des Monats
- ja (3)
Near-IR femtosecond ( τ = 150 fs, λ = 775 nm, repetition rate 1 kHz) and VUV nanosecond (τ = 20 ns, λ = 157 nm, repetition rate 1 to 5 Hz) laser pulse ablation of single-crystalline TeO2 (c-TeO2, grown by the balance controlled Czochalski growth method) surfaces was performed in air using the direct focusing technique. The multi-method characterization using optical microscopy, atomic force microscopy and scanning electron microscopy revealed the surface morphology of the ablated craters. This allowed us to characterize precisely the lateral and vertical dimensions of the laser-ablated craters for different laser pulse energies and pulse numbers at each spot. Based on the obtained information, we quantitatively determined the ablation threshold fluence for the fs laser irradiation when different pulse numbers were applied to the same spot by using two independent extrapolation techniques. We found that in case of NIR femtosecond laser pulse irradiation, the ablation threshold significantly depends on the number of laser pulses applied to the same spot indicating that incubation effects play an important role in this material. In case of VUV ns laser pulses, the ablation rate is significantly higher due to the high photon energy and the predominantly linear absorption in the material. These results are discussed on the basis of recent models of the interaction of laser pulses with dielectrics.
We have studied plasma formation and relaxation dynamics along with the corresponding topography modifications in fused silica and sapphire induced by single femtosecond laser pulses (800 nm and 120 fs). These materials, representative of high bandgap amorphous and crystalline dielectrics, respectively, require nonlinear mechanisms to absorb the laser light. The study employed a femtosecond time-resolved microscopy technique that allows obtaining reflectivity and transmission images of the material surface at well-defined temporal delays after the arrival of the pump pulse which excites the dielectric material. The transient evolution of the free-electron plasma formed can be followed by combining the time-resolved optical data with a Drude model to estimate transient electron densities and skin depths. The temporal evolution of the optical properties is very similar in both materials within the first few hundred picoseconds, including the formation of a high reflectivity ring at about 7 ps. In contrast, at longer delays (100 ps20 ns) the behavior of both materials differs significantly, revealing a longer lasting ablation process in sapphire. Moreover, transient images of sapphire show a concentric ring pattern surrounding the ablation crater, which is not observed in fused silica. We attribute this phenomenon to optical diffraction at a transient elevation of the ejected molten material at the crater border. On the other hand, the final topography of the ablation crater is radically different for each material. While in fused silica a relatively smooth crater with two distinct regimes is observed, sapphire shows much steeper crater walls, surrounded by a weak depression along with cracks in the material surface. These differences are explained in terms of the most relevant thermal and mechanical properties of the material. Despite these differences the maximum crater depth is comparable in both material at the highest fluences used (16J/cm2). The evolution of the crater depth as a function of fluence can be described taking into account the individual bandgap of each material.
Serial interconnection of CIGSe thin film solar modules involves typically glass-side laser patterning of the molybdenum layer (P1 scribe). In this paper we present a working principle of P1 film side patterning. The investigated samples were sputter-deposited onto soda-lime glass substrates. For understanding the fundamental ablation behavior, two kinds of layer systems were studied: on the one hand monolayer systems which are compressively stressed and on the other hand bilayer systems, consisting of a tensile stressed layer on the substrate and a second layer on top. The film-side ablation process was studied using a nanosecond as well as a picosecond laser source. The influence of intrinsic stress was studied by XRD. Time resolved spectroscopy reveals the formation of plasma as important driving mechanism for ablation. It is shown that by proper adaption of the sputter conditions high-quality P1 film side patterning is achieved.
Near-IR femtosecond (fs) (pulse duration = 150 fs, wavelength = 775 um, Repetition rate 1 kHz) and VUV nanosecond (ns) (pulse duration = 20 ns, wavelength = 157 nm, repetition rate 1 to 5 Hz) laser pulse ablation of single-crystalline TeO? (c-Te02) surfaces was performed in air using the direct focusing technique. A multi-method characterization using optical microscopy, atomic force microscopy and scanning electron microscopy revealed the surface morphology of the ablated craters. This allowed us at each irradiation site to characterize precisely the lateral and vertical dimensions of the laser-ablated craters for different laser pulse energies and number of laser pulses per spot. Based on the obtained information, we quantitatively determined the Ablation threshold fluence for the fs laser irradiation when different pulse numbers were applied to the same spot using two independent extrapolation techniques. We found that in the case of NIR fs laser pulse irradiation, the ablation threshold significantly depends on the number of laser pulses applied to the same spot indicating that incubation effects play an important role in this material. In the case of VUV ns laser pulses, the ablation rate is significantly higher due to the high photon energy and the predominantly linear absorption in the material. These results are discussed on the basis of recent models of the interaction of laser pulses with dielectrics. In the second part of this chapter, we use timeof-flight mass spectrometry (TOFMS) to analyze the elemental composltion of the ablation products generated upon laser irradiation of c-Te02 with single fs- (pulse duration ~ 200 fs, wavelength 398 nm) and ns-pulses (pulse duration 4 ns, wavelength 355 nm). Due to the three Order of magnitude different peak intensities of the ns- and fs laser pulses, significant differences were observed regarding the laser-induced species in the plasma plume. Positive singly, doubly and triply charged Te ions (Te+, Te2+, Te3+) in the form of many different isotopes were observed in case of both irradiations. In the case of the ns-laser ablation, the TeO+ formation was negligible compared to the fs case and there was no Te trimer (Te3+) formation observed. It was found that the amplitude of Te ion Signals strongly depends on the applied laser pulse energy. Singly charged Oxygen ions (0+) are always present as a byproduct in both kinds of laser ablation.
The formation of laser-induced periodic surface structures (LIPSS) upon irradiation of fused silica with multiple irradiation sequences consisting of laser pulse pairs (50 fs single-pulse duration) of two different wavelengths (400 and 800 nm) is studied experimentally. Parallel polarized double-pulse sequences with a variable delay Δt between -10 and +10 ps and between the individual fs-laser pulses were used to investigate the LIPSS periods versus Δt. These two-color experiments reveal the importance of the ultrafast energy deposition to the silica surface by the first laser pulse for LIPSS formation. The second laser pulse subsequently reinforces the previously seeded spatial LIPSS frequencies.
The removal of a 75- to 90-nm-thick passivating silicon nitride antireflection coating from standard textured multicrystalline silicon photovoltaic wafers with a typical diffused 90-Ω/sq-emitter upon irradiation with near-infrared femtosecond laser pulses (790 nm central wavelength, 30 fs pulse duration) is studied experimentally. The laser irradiation areas are subsequently characterized by complementary optical microscopy, scanning electron microscopy and depth profiling chemical analyses using secondary ion mass spectrometry. The results clarify the thin-film femtosecond laser ablation scenario and outline the process windows for selective antireflection coating removal.
This 6 minute long MP4-video presents some key results of the European research project "BioCombs4Nanofibers" to the broader public. Inspired by nature, some concepts of certain types of spiders are transferred to technology in order to develop bacteria-repellent surfaces through laser surface nanostructuring.
Funding notice: This study was funded by the European Union's research and innovation program under the FET Open grant agreement No. 862016 (BioCombs4Nanofibers, http://biocombs4nanofibers.eu).
The processing of laser-induced periodic surface structures (LIPSS) represents a simple and robust way for the nanostructuring of solids that allows creating a wide range of surface functionalities featuring applications in optics, tribology, medicine, energy technologies, etc. While the currently available laser and scanner technology already allows surface processing rates at the m2/min level, industrial applications of LIPSS are sometimes hampered by the complex interplay between the nanoscale surface topography and the specific surface chemistry. This typically manifests in difficulties to control the processing of LIPSS and in limitations to ensure the long-term stability of the created surface functions. This presentation aims to identify some unsolved scientific problems related to LIPSS, discusses the pending technological limitations, and sketches the current state of theoretical modelling. Hereby, it is intended to stimulate further research and developments in the field of LIPSS for overcoming these limitations and for supporting the transfer of the LIPSS technology into industry.
Due to its large strength-to-weight ratio and excellent biocompatibility, titanium materials are of paramount importance for medical applications, e.g. as implant material for protheses. In this work, the evolution of various types of laser-induced micro- and nanostructures emerging on titanium or titanium alloys upon irradiation by near-infrared ultrashort laser pulses (925 fs, 1030 nm) in air environment is studied for various laser fluence levels, effective number of pulses and at different pulse repetition rates (1 – 400 kHz). The morphologies of the processed surfaces were systematically characterized by optical and scanning electron microscopy (OM, SEM). Complementary white-light interference microscopy (WLIM) revealed the corresponding surface topographies. Chemical and structural changes were analysed through depth-profiling time-of-flight secondary ion mass spectrometry (TOF-SIMS) and X-ray diffraction (XRD) analyses. The results point towards a remarkable influence of the laser processing parameters on the surface topography, while simultaneously altering the near-surface chemistry via laser-induced oxidation effects. Consequences for medical applications are outlined.
Nickel tungsten alloy tapes (Ni—5 at% W, 10 mm wide, 80 µm thick, biaxially textured) used in second-generation high temperature superconductor (2G-HTS) technology were laser-processed in air with ultraviolet ps-laser pulses (355 nm wavelength, 300 ps pulse duration, 250–800 kHz pulse repetition frequency). By employing optimized surface scan-processing strategies, various laser-generated periodic surface structures were generated on the tapes. Particularly, distinct surface microstructures and nanostructures were formed. These included sub-wavelength-sized highly-regular hexagonally-arranged nano-protrusions, wavelength-sized line-grating-like laser-induced periodic surface structures (LIPSS, ripples), and larger irregular pyramidal microstructures. The induced surface morphology was characterized in depth by electron-based techniques, including scanning electron microscopy (SEM), electron back scatter diffraction (EBSD), cross-sectional transmission electron microscopy (STEM/TEM) and energy dispersive X-ray spectrometry (EDS). The in-depth EBSD crystallographic analyses indicated a significant impact of the material initial grain orientation on the type of surface nanostructure and microstructure formed upon laser irradiation. Special emphasis was laid on high-resolution material analysis of the hexagonally-arranged nano-protrusions. Their formation mechanism is discussed on the basis of the interplay between electromagnetic scattering effects followed by hydrodynamic matter re-organization after the laser exposure. The temperature stability of the hexagonally-arranged nano-protrusion was explored in post-irradiation thermal annealing experiments, in order to qualify their suitability in 2G-HTS fabrication technology with initial steps deposition temperatures in the range of 773–873 K.