XUV- and X-ray free-electron-lasers (FEL) combine short wavelength, ultrashort pulse duration, spatial coherence and high intensity. This unique combination of properties opens up new possibilities to study the dynamics of non-reversible phenomena with ultrafast temporal and nano- to atomic-scale spatial resolution. In this contribution we wish to present results of time-resolved experiments performed at the XUV-FEL FLASH (HASYLAB/Hamburg) aimed to investigate the nano-scale structural dynamics of laser-irradiated materials. Thin films and fabricated nano-structures, deposited on Si3N4-membranes, have been excited with ultrashort optical laser pulses. The dynamics of the non-reversible structural evolution of the irradiated samples during laser-induced melting and ablation has been studied in an optical pump - XUV-probe configuration by means of single-shot coherent scattering techniques (i.e. diffraction imaging [1]). In a first set of experiments we investigated the formation of laser induced periodic surface structures (LIPSS) on the surface of thin Si-films (thickness 100 nm). In a simplified view LIPPS are generated as a result of interference between the incident laser pulse and surface scattered waves which leads to a periodically modulated energy deposition. Time-resolved scattering using femtosecond XUV-pulses (with a wavelength of 13.5 nm and 7 nm) allowed us to directly follow LIPSS evolution on an ultrafast time-scale and with better than 40 nm spatial resolution. The observed scattering patterns show almost quantitative agreement with theoretical predictions [2] and reveal that the LIPSS start to form already during the 12 ps pump pulse. In the second set of measurements we studied picosecond and femtosecond laser induced ablation and disintegration of fabricated nano-structures. Correlations of coherent diffraction patterns measured at various time delays to the pattern of the undisturbed object show that order in the structure is progressively lost starting from short length scales. This structural rearrangement progresses at close to the speed of sound in the material. Under certain circumstances (e.g. adequate sampling) it became also possible to reconstruct real-space images of the object as it evolves over time [3]. The possibility of femtosecond single-shot imaging of ultrafast dynamic processes with nanoscale resolution provides yet more details of the physical processes involved. [1] H. N. Chapman et al. Nature Phys. 2, 839 (2006). [2] J. F. Young et al., Phys. Rev. B 27, 1155 (1983). [3] A. Barty et al. Nature Phot. 2, 415 (2008).
Ablation of indium phosphide wafers in air was performed with 130 fs laser pulses at a wavelength of 800 nm at a low repetition rate of 10 Hz. In order to evaluate the role of the incubation effects, the relationship between the number of laser pulses used for the ablation and the threshold fluence was studied. Particular attention was paid to the chemical composition, surface morphology and structural variations of the ablated area.
In this contribution the mechanisms of formation and current applications of LIPSS are reviewed, including the colorization of technical surfaces, the control of surface wetting properties, the mimicry of the natural texture of animal integuments, the tailoring of surface colonization by bacterial biofilms, and the improvement of the tribological performance of nanostructured metal surfaces.
Laser-induced periodic surface structures (LIPSS, ripples) are a universal phenomenon that can be observed on almost any material after the irradiation by linearly polarized laser beams, particularly when using ultrashort laser pulses with durations in the femtosecond to picosecond range.
During the past few years significantly increasing research activities have been reported in the field of LIPSS, since their generation in a single-step process provides a simple way of nanostructuring and surface functionalization towards the control of optical, mechanical, biological, or chemical surface properties. In this contribution the mechanisms of formation and current applications of LIPSS are reviewed, including the colorization of technical surfaces, the control of surface wetting properties, the mimicry of the natural texture of animal integuments, the tailoring of surface colonization by bacterial biofilms, the advancement of medical pacemakers, and the improvement of the tribological performance of nanostructured metal surfaces.
Laser-induced periodic surface structures (LIPSS, ripples) were generated on steel and titanium surfaces upon irradiation with multiple linear polarized femtosecond laser pulses (pulse duration 30 fs, central wavelength 790 nm). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning geometry for the processing of large surface areas covered homogeneously by the nanostructures. The irradiated surface regions were subjected to optical microscopy (OM), white light interference microscopy (WLIM) and scanning electron microscopy (SEM) revealing sub-wavelength spatial periods. The nanostructured surfaces were tribologically tested under reciprocal sliding conditions against a sphere of hardened 100Cr6 steel at 1 Hz using paraffin oil and engine oil as lubricants. After 1000 sliding cycles at a load of 1.0 N, the corresponding wear tracks were characterized by OM and SEM. For specific conditions the laser-generated nanostructures endured the tribological treatment. Simultaneously, a significant reduction of the friction coefficient was observed in the laser-irradiated (LIPSS-covered) areas when compared to the non-irradiated surface, indicating the potential benefit of laser surface structuring for tribological applications.
The wetting behavior of material surfaces can be controlled by surface structures. We functionalized inorganic material surfaces, such as steel, titanium alloy and silicon, to modify the wetting behavior using ultrashort laser pulses (fs- to ps-range). The laser processing was performed by scanning the laser beam across the surface of initially polished flat sample material. A combined experimental and theoretical study of the laser processing parameters (peak fluence, scan velocity, line overlap) allowed the identification of different regimes associated with characteristic surface morphologies (laser-induced periodic surface structures, grooves, micro cones, dimples, etc.). Analyses of the surface using optical as well as scanning electron microscopy allowed the identification of morphologies providing the optimum similarity to the natural skin of lizards. For mimicking skin structures of moisture-harvesting lizards towards an optimization of the surface wetting behavior, additionally, a two-step laser processing strategy was established for realizing hierarchical micro- and nanostructures. In this approach, a laser-generated regular array of small dimples was superimposed (step 2) to the micron-scaled capillaries processed before (step 1). Optical focus variation imaging measurements finally revealed the three dimensional topography of the laser processed surfaces derived from lizard skin structures. The functionality of these surfaces was analyzed in view of wetting properties.
Near-IR femtosecond (fs) (pulse duration = 150 fs, wavelength = 775 um, Repetition rate 1 kHz) and VUV nanosecond (ns) (pulse duration = 20 ns, wavelength = 157 nm, repetition rate 1 to 5 Hz) laser pulse ablation of single-crystalline TeO? (c-Te02) surfaces was performed in air using the direct focusing technique. A multi-method characterization using optical microscopy, atomic force microscopy and scanning electron microscopy revealed the surface morphology of the ablated craters. This allowed us at each irradiation site to characterize precisely the lateral and vertical dimensions of the laser-ablated craters for different laser pulse energies and number of laser pulses per spot. Based on the obtained information, we quantitatively determined the Ablation threshold fluence for the fs laser irradiation when different pulse numbers were applied to the same spot using two independent extrapolation techniques. We found that in the case of NIR fs laser pulse irradiation, the ablation threshold significantly depends on the number of laser pulses applied to the same spot indicating that incubation effects play an important role in this material. In the case of VUV ns laser pulses, the ablation rate is significantly higher due to the high photon energy and the predominantly linear absorption in the material. These results are discussed on the basis of recent models of the interaction of laser pulses with dielectrics. In the second part of this chapter, we use timeof-flight mass spectrometry (TOFMS) to analyze the elemental composltion of the ablation products generated upon laser irradiation of c-Te02 with single fs- (pulse duration ~ 200 fs, wavelength 398 nm) and ns-pulses (pulse duration 4 ns, wavelength 355 nm). Due to the three Order of magnitude different peak intensities of the ns- and fs laser pulses, significant differences were observed regarding the laser-induced species in the plasma plume. Positive singly, doubly and triply charged Te ions (Te+, Te2+, Te3+) in the form of many different isotopes were observed in case of both irradiations. In the case of the ns-laser ablation, the TeO+ formation was negligible compared to the fs case and there was no Te trimer (Te3+) formation observed. It was found that the amplitude of Te ion Signals strongly depends on the applied laser pulse energy. Singly charged Oxygen ions (0+) are always present as a byproduct in both kinds of laser ablation.
Near-IR femtosecond (fs) (pulse duration = 150 fs, wavelength = 775 nm, repetition
rate 1 kHz) and VUV nanosecond (ns) (pulse duration = 20 ns, wavelength = 157 nm,
repetition rate 1 to 5 Hz) laser pulse ablation of single-crystalline TeO2 (c-TeO2 ) surfaces
was performed in air using the direct focusing technique. A multi-method
characterization using optical microscopy, atomic force microscopy and scanning
electron microscopy revealed the surface morphology of the ablated craters. This allowed
us at each irradiation site to characterize precisely the lateral and vertical dimensions of
the laser-ablated craters for different laser pulse energies and number of laser pulses per
spot. Based on the obtained information, we quantitatively determined the ablation
threshold fluence for the fs laser irradiation when different pulse numbers were applied to
the same spot using two independent extrapolation techniques. We found that in the case
of NIR fs laser pulse irradiation, the ablation threshold significantly depends on the
number of laser pulses applied to the same spot indicating that incubation effects play an
important role in this material. In the case of VUV ns laser pulses, the ablation rate is
significantly higher due to the high photon energy and the predominantly linear
absorption in the material. These results are discussed on the basis of recent models of the
interaction of laser pulses with dielectrics. In the second part of this chapter, we use time-
of-flight mass spectrometry (TOFMS) to analyze the elemental composition of the
ablation products generated upon laser irradiation of c-TeO2 with single fs- (pulse
duration ~200 fs, wavelength 398 nm) and ns-pulses (pulse duration 4 ns, wavelength
355 nm). Due to the three order of magnitude different peak intensities of the ns- and fs
laser pulses, significant differences were observed regarding the laser-induced species in
the plasma plume. Positive singly, doubly and triply charged Te ions (Te+, Te2+, Te3+) in
the form of many different isotopes were observed in case of both irradiations. In the case
of the ns-laser ablation, the TeO+ formation was negligible compared to the fs case and
there was no Te trimer (Te3+) formation observed. It was found that the amplitude of Te
ion signals strongly depends on the applied laser pulse energy. Singly charged oxygen
ions (O+) are always present as a byproduct in both kinds of laser ablation.
The formation of laser-induced periodic surface structures (LIPSS) upon irradiation of semiconductors and dielectrics by linearly polarized high-intensity Ti:sapphire fs-laser pulses (τ ~100 fs, λ ~800 nm) is studied experimentally and theoretically. In the experiments, two different types of LIPSS exhibiting very different spatial periods are observed (socalled LSFL low spatial frequency LIPSS, and HSFL - high spatial frequency LIPSS), both having a different dependence on the incident laser fluence and pulse number per spot. The experimental results are analyzed by means of a new theoretical approach, which combines the generally accepted LIPSS theory of J. E. Sipe and co-workers [Phys. Rev. B 27, 1141-1154 (1983)] with a Drude model, in order to account for transient changes of the optical properties of the irradiated materials. The joint Sipe-Drude model is capable of explaining numerous aspects of fs-LIPSS formation, i.e., the orientation of the LIPSS, their fluence dependence as well as their spatial periods. The latter aspect is specifically demonstrated for silicon crystals, which show experimental LSFL periods Λ somewhat smaller than λ. This behaviour is caused by the excitation of surface plasmon polaritons, SPP, (once the initially semiconducting material turns to a metallic state upon formation of a dense free-electron-plasma in the material) and the subsequent interference between its electrical fields with that of the incident laser beam, resulting in a spatially modulated energy deposition at the surface.
Upon multi-pulse irradiation, a feedback mechanism, caused by the redshift of the resonance in a grating-assisted SPP excitation, is further reducing the LSFL spatial periods. The SPP-based mechanism of LSFL successfully explains the remarkably large range of LSFL periods between ~0.6 λ and λ.
The current state in the field of laser-induced periodic surface structures (LIPSS, ripples) is reviewed. Their formation mechanisms are analyzed in ultrafast experiments (time-resolved diffraction and polarization controlled double-pulse experiments) and technological applications are demonstrated.
This presentation reviews current and expected developments in the field of laser-induced periodic surface structures (LIPSS, ripples). These surface nanostructures are a universal phenomenon and can be generated on almost any material by irradiation with intense linearly polarized radiation. LIPSS are formed in a “self-ordered” way and are often accompanying laser material processing applications. The structures can be produced in a single-step process and enable surface functionalization through the adaption of optical, mechanical and chemical surface properties. Their spatial periods typically range from several micrometers down to less than 100 nanometers, exhibiting a clear correlation with the polarization direction of the laser radiation used. Various types of LIPSS have been classified, relevant control parameters were identified, and material specific formation mechanisms are analyzed for different types of inorganic solids, i.e., metals, semiconductors, and dielectrics, through time-resolved optical experiments and theoretical simulations. Special attention will be paid to a comparison of the currently available formation theories for LIPSS with a discussion of their respective strengths and weaknesses. Currrently explored applications featuring surface functionalization in the fields of optics, surface wetting, medicine, and tribology will be discussed.
Laser-induced periodic surface structures (LIPSS, ripples) are a universal phenomenon that can be observed on almost any material after the irradiation by linearly polarized laser beams, particularly when using ultrashort laser pulses with durations in the femtosecond to picosecond range. During the past years significantly increasing industrial and research activities have been reported in the field of LIPSS, since their generation in a single-step process provides a simple way of nanostructuring and surface functionalization towards the control of optical, mechanical or chemical surface properties. In this contribution the mechanisms of formation and current trends and applications of LIPSS are reviewed, including the colorization of technical surfaces, the control of surface wetting properties, the mimicry of the natural texture of animals, the tailoring of surface colonization by bacterial biofilms, the advancement of leadless medical pacemakers, and the improvement of the tribological performance of nanostructured metal surfaces.
Laser-induced periodic surface structures (LIPSS, ripples) are a universal phenomenon that can be observed on almost any material after the irradiation by linearly polarized laser beams, particularly when using ultrashort laser pulses with durations in the femtosecond to picosecond range. During the past years significantly increasing industrial and research activities have been reported in the field of LIPSS, since their generation in a single-step process provides a simple way of nanostructuring and surface functionalization towards the control of optical, mechanical, biological, or chemical surface properties. In this contribution the mechanisms of formation and current trends and applications of LIPSS are reviewed, including the colorization of technical surfaces, the control of surface wetting properties, the mimicry of the natural texture of animals, the tailoring of surface colonization by bacterial biofilms, the advancement of leadless medical pacemakers, and the improvement of the tribological performance of nanostructured metal surfaces.
This presentation reviews the current state in the field of Laser-induced Periodic Surface Structures (LIPSS). These surface nanostructures are a universal phenomenon and can be generated on almost any material by irradiation with intense linearly polarized laser radiation. LIPSS are formed in a “self-ordered” way and are often accompanying material processing applications. They can be produced following a single-step process and enable surface functionalization through the adaption of optical, mechanical and chemical surface properties. Their structural sizes typically range from several micrometers down to less than 100 nanometers exhibiting a clear correlation with the polarization direction of the laser radiation. Various types of surface structures are classified, relevant control parameters are identified, and their material specific formation mechanisms are analyzed for different types of inorganic solids, i.e., metals, semiconductors, and dielectrics, through time-resolved optical experiments and theoretical simulations. Finally, technological applications featuring surface functionalization in the fields of optics, fluidics, medicine, and tribology are discussed.