Filtern
Dokumenttyp
- Buchkapitel (10) (entfernen)
Sprache
- Englisch (10)
Referierte Publikation
- nein (10)
Schlagworte
- Laser ablation (4)
- Microstructures (4)
- Femtosecond laser (3)
- Laser-induced periodic surface structures (LIPSS) (3)
- Nanostructures (3)
- Femtosecond laser ablation (2)
- Laser-induced periodic surface structures, LIPSS (2)
- Atomic force microscopy (1)
- Capillary waves (1)
- Carrier excitation (1)
- Damage threshold (1)
- Dielectrics (1)
- Double-pulse (1)
- Femtosecond (1)
- Free electron laser (1)
- Incubation (1)
- Interferometer (1)
- Isotopes (1)
- Laser processing (1)
- Multiphoton absorption (1)
- Nanosecond laser ablation (1)
- Nanostrcutures (1)
- Optical properties (1)
- Pump-probe experiments (1)
- Scanning electron microscopy (1)
- Surface functionalization (1)
- TeO2 (1)
- Tellurium dioxide crystals (1)
- Time-of-flight mass spectrometry (TOF-MS) (1)
- Time-of-flight mass spectroscopy (1)
- Time-resolved scattering (1)
- VUV nanosecond laser ablation (1)
Organisationseinheit der BAM
Laser-induced periodic surface structures (LIPSS) were generated on two types of steel (100Cr6, X30CrMoN15-1) and two types of titanium (Ti, Ti6A14V) surfaces upon irradiation with multiple linear polarized femtosecond laser pulses in air environment (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz, Gaussian beam shape). Teh conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning geometry for the processing of large surface areas covered homogeneously by two different types of LIPSS - either near wavelength or sub-100 nm structures. The tribological performance of the nanostructured surfaces was characterized under reciprocating sliding at 1 Hz against a ball of hardened steel using different lubricants and normal forces. After 1000 cycles the corresponding wear tracks were characterized by optical and scanning electron microscopy. For specific conditions, the wear was strongly reduced and laser-generated nanostructures endured the tribological treatment. Simultaneously, a significant reduction of the friction coefficient was observed in the laser-irradiated LIPSS-covered areas, indicating the benefit of laser surface structuring for tribological applications. The spatially Gaussian shaped beam used for the laser processing was transformed via beam shaping into a top hat distribution at the surface of the samples for optimization. The tribological performance of the laser-induced nanostructures is discussed on the basis of different physical and chemical mechanisms.
The formation of laser-induced periodic surface structures (LIPSS) on different materials (silicon, fused silica, quartz) with linearly polarized fs-laser irradiation is studied experimentally. In dielectrics, the importance of transient excitation stages in the LIPSS formation is demonstrated by using (multiple) cross-polarized double-fs-laser-pulse irradiation sequences. A characteristic decrease of the spatial LIPSS periods is observed for double-pulse delays of less than 2 ps along with a characteristic 90°-rotation of the LIPSS orientation.
Given their unique properties, ultrashort laser pulses with durations in the femtosecond to picosecond range currently open new avenues in the field of laser materials processing, resulting in groundbreaking new applications based on laser-induced surface functionalization. This article reviews the usability of temporally distributed energy deposition via double-pulse irradiation in applications based on laser ablation. This includes simple new techniques for surface nanostructuring and improved sensitivities in spectroscopic material analyses.
Near-IR femtosecond (fs) (pulse duration = 150 fs, wavelength = 775 um, Repetition rate 1 kHz) and VUV nanosecond (ns) (pulse duration = 20 ns, wavelength = 157 nm, repetition rate 1 to 5 Hz) laser pulse ablation of single-crystalline TeO? (c-Te02) surfaces was performed in air using the direct focusing technique. A multi-method characterization using optical microscopy, atomic force microscopy and scanning electron microscopy revealed the surface morphology of the ablated craters. This allowed us at each irradiation site to characterize precisely the lateral and vertical dimensions of the laser-ablated craters for different laser pulse energies and number of laser pulses per spot. Based on the obtained information, we quantitatively determined the Ablation threshold fluence for the fs laser irradiation when different pulse numbers were applied to the same spot using two independent extrapolation techniques. We found that in the case of NIR fs laser pulse irradiation, the ablation threshold significantly depends on the number of laser pulses applied to the same spot indicating that incubation effects play an important role in this material. In the case of VUV ns laser pulses, the ablation rate is significantly higher due to the high photon energy and the predominantly linear absorption in the material. These results are discussed on the basis of recent models of the interaction of laser pulses with dielectrics. In the second part of this chapter, we use timeof-flight mass spectrometry (TOFMS) to analyze the elemental composltion of the ablation products generated upon laser irradiation of c-Te02 with single fs- (pulse duration ~ 200 fs, wavelength 398 nm) and ns-pulses (pulse duration 4 ns, wavelength 355 nm). Due to the three Order of magnitude different peak intensities of the ns- and fs laser pulses, significant differences were observed regarding the laser-induced species in the plasma plume. Positive singly, doubly and triply charged Te ions (Te+, Te2+, Te3+) in the form of many different isotopes were observed in case of both irradiations. In the case of the ns-laser ablation, the TeO+ formation was negligible compared to the fs case and there was no Te trimer (Te3+) formation observed. It was found that the amplitude of Te ion Signals strongly depends on the applied laser pulse energy. Singly charged Oxygen ions (0+) are always present as a byproduct in both kinds of laser ablation.
Near-IR femtosecond (fs) (pulse duration = 150 fs, wavelength = 775 nm, repetition
rate 1 kHz) and VUV nanosecond (ns) (pulse duration = 20 ns, wavelength = 157 nm,
repetition rate 1 to 5 Hz) laser pulse ablation of single-crystalline TeO2 (c-TeO2 ) surfaces
was performed in air using the direct focusing technique. A multi-method
characterization using optical microscopy, atomic force microscopy and scanning
electron microscopy revealed the surface morphology of the ablated craters. This allowed
us at each irradiation site to characterize precisely the lateral and vertical dimensions of
the laser-ablated craters for different laser pulse energies and number of laser pulses per
spot. Based on the obtained information, we quantitatively determined the ablation
threshold fluence for the fs laser irradiation when different pulse numbers were applied to
the same spot using two independent extrapolation techniques. We found that in the case
of NIR fs laser pulse irradiation, the ablation threshold significantly depends on the
number of laser pulses applied to the same spot indicating that incubation effects play an
important role in this material. In the case of VUV ns laser pulses, the ablation rate is
significantly higher due to the high photon energy and the predominantly linear
absorption in the material. These results are discussed on the basis of recent models of the
interaction of laser pulses with dielectrics. In the second part of this chapter, we use time-
of-flight mass spectrometry (TOFMS) to analyze the elemental composition of the
ablation products generated upon laser irradiation of c-TeO2 with single fs- (pulse
duration ~200 fs, wavelength 398 nm) and ns-pulses (pulse duration 4 ns, wavelength
355 nm). Due to the three order of magnitude different peak intensities of the ns- and fs
laser pulses, significant differences were observed regarding the laser-induced species in
the plasma plume. Positive singly, doubly and triply charged Te ions (Te+, Te2+, Te3+) in
the form of many different isotopes were observed in case of both irradiations. In the case
of the ns-laser ablation, the TeO+ formation was negligible compared to the fs case and
there was no Te trimer (Te3+) formation observed. It was found that the amplitude of Te
ion signals strongly depends on the applied laser pulse energy. Singly charged oxygen
ions (O+) are always present as a byproduct in both kinds of laser ablation.
Laser-induced periodic surface structures (LIPSS) are a universal phenomenon and can be generated on almost any material by irradiation with linearly polarized radiation. This chapter reviews the current state in the field of LIPSS, which are formed in a “self-ordered” way and are often accompanying materials processing applications. LIPSS can be produced in a single-stage process and enable surface nanostructuring and, in turn, adaption of optical, mechanical, and chemical surface properties. Typically, they feature a structural size ranging from several micrometers down to less than 100 nm and show a clear correlation with the polarization direction of the light used for their generation. Various types of LIPSS are classified, relevant control parameters are identified, and their material-specific formation mechanisms are analyzed for different types of inorganic solids, i.e., metals, semiconductors, and dielectrics. Finally, technological applications featuring surface functionalization in the fields of optics, fluidics, medicine, and tribology are discussed.
Laser-induced periodic surface structures (LIPSS) are a universal phenomenon and can be generated on almost any material by irradiation with linearly polarized radiation. This chapter reviews the current state in the field of LIPSS, which are formed in a “self-ordered” way and are often accompanying materials processing applications. LIPSS can be produced in a single-stage process and enable surface nanostructuring and, in turn, adaption of optical, mechanical, and chemical surface properties. Typically, they feature a structural size ranging from several micrometers down to less than 100 nm and show a clear correlation with the polarization direction of the light used for their generation. Various types of LIPSS are classified, relevant control parameters are identified, and their material-specific formation mechanisms are analyzed for different types of inorganic solids, i.e., metals, semiconductors, and dielectrics. Finally, technological applications featuring surface functionalization in the fields of optics, fluidics, medicine, and tribology are discussed.
Laser-induced periodic surface structures (LIPSS) are a universal phenomenon and can be generated on almost any material by irradiation with linearly polarized radiation. This chapter reviews the current state in the field of LIPSS, which are formed in a “self-ordered” way and are often accompanying materials processing applications. LIPSS can be produced in a single-stage process and enable surface nanostructuring and, in turn, adaption of optical, mechanical, and chemical surface properties. Typically, they feature a structural size ranging from several micrometers down to less than 100 nm and show a clear correlation with the polarization direction of the light used for their generation. Various types of LIPSS are classified, relevant control parameters are identified, and their material-specific formation mechanisms are analyzed for different types of inorganic solids, i.e., metals, semiconductors, and dielectrics. Finally, technological applications featuring surface functionalization in the fields of optics, fluidics, medicine, and tribology are discussed.
Surface nanostructures provide the possibility to create and tailor surface functionalities mainly via controlling their topography along with other chemical and physical material properties. One of the most appealing technologies for surface functionalization via micro- and nanostructuring is based on laser processing. This can be done either via direct contour-shaping of the irradiated material using a tightly focused laser beam or in a self-ordered way that allows employing larger laser beam diameters along with areal scanning to create a variety of laser-induced periodic surface structures (LIPSS). For the latter approach, particularly ultrashort pulsed lasers have recently pushed the borders across long-lasting limitations regarding the minimum achievable feature sizes and additionally boosted up the production times. This chapter reviews the plethora of recently investigated applications of LIPSS—for example, via imposing diffractive or plasmonic structural colors, the management of liquids and surface wetting properties, biomedical and bioinspired functionalities, beneficial effects in tribology for reducing friction and wear, the manipulation of optical scattering and absorption in photovoltaics, or the modification of magnetic or superconducting surface properties in other energy applications. The footprint of the LIPSS-based technology is explored in detail regarding the current state of industrialization, including an analysis of the market and associated LIPSS production costs.
Irradiation of solid surfaces with intense ultrashort laser pulses represents a unique way of depositing energy into materials. It allows to realize states of extreme electronic excitation and/or very high temperature and pressure and to drive materials close to and beyond fundamental stability limits. As a consequence, structural changes and phase transitions often occur along unusual pathways and under strongly nonequilibrium conditions. Due to the inherent multiscale nature—both temporally and spatially—of these irreversible processes, their direct experimental observation requires techniques that combine high temporal resolution with the appropriate spatial resolution and the capability to obtain good quality data on a single pulse/event basis. In this respect, fourth-generation light sources, namely, short wavelength and short pulse free electron lasers (FELs), are offering new and fascinating possibilities. As an example, this chapter will discuss the results of scattering experiments carried out at the FLASH free electron laser at DESY (Hamburg, Germany), which allowed us to resolve laser-induced structure formation at surfaces on the nanometer to submicron length scale and in temporal regimes ranging from picoseconds to several nanoseconds with sub-picosecond resolution.