Organisationseinheit der BAM
Ti:sapphire laser pulses of 130 fs and 800 nm were focused on 3.2-7m-thick TiN films by a 60-mm focal length lens in air. The morphology of the ablated areas generated by laser pulses at a fluence slightly above the ablation threshold was characterized in dependence on the pulse number by scanning electron microscopy (SEM) and atomic force microscopy (AFM). The cavity profiles, depths, diameters, and volumes were quantitatively evaluated by AFM. The polarization state of the laser light is discussed as a further parameter, in addition to fluence and pulse number, that influences and controls the ablation precision of these materials. It was observed that circularly polarized radiation enhances the average ablation rates and reduces the roughness in the cavities by a factor of 2-3 as compared to linearly polarized radiation of the same incident laser fluence. Special attention was paid to the interfacial region between the coating and substrate. Ultrashort-pulse laser drilling into the Si substrate revealed the generation of columnar features which even may surmount the original coating under laser conditions.
Chemical, morphological and accumulation phenomena in ultrashort-pulse laser ablation of TiN in air
(2000)
Ultrashort-pulse laser ablation (F=130 fs, 5=800 nm, repetition rate 2-20 Hz) of titanium nitride was investigated for laser fluences between 0.3 and 4.5 J/cm2 using the direct focusing technique in air. The influence of the laser pulse number and the peak fluence was investigated by means of several surface analytical techniques (optical microscopy, dynamic friction atomic force microscopy, scanning Auger electron microscopy and small-spot electron spectroscopy for chemical analysis). The correlation of the results about optical, physical and chemical properties of the irradiated areas allows us to propose a simple oxidation model, which explains different observed phenomena associated with surface damage such as mound formation and crater widening and clarifies the incubation behavior reported earlier for this material.
Femtosecond time-resolved microscopy has been used to analyze the structural transformation dynamics (melting, ablation, and solidification phenomena) induced by single intense 130 fs laser pulses in single-crystalline (100)-indium phosphide wafers in air on a time scale from ~100 fs up to 8 ns. In the ablative regime close to the ablation threshold, transient surface reflectivity patterns are observed by fs microscopy on a ps to ns time scale as a consequence of the complex spatial density structure of the ablating material (dynamic Newton fringes). At higher fluences, exceeding six times the ablation threshold, optical breakdown causes another, more violent ablation regime, which reduces the energy deposition depth along with the time of significant material removal. As a consequence, ablation lasts longer in a ring-shaped region around the region of optical breakdown. This leads to the formation of a crater profile with a central protrusion. In the melting regime below the ablation threshold, the melting dynamics of indium phosphide has been quantified and subsequent superficial amorphization has been observed upon solidification on the ns time scale leading to amorphous layer thicknesses of the order of a few tens of nanometers.
Laser ablation of single-crystalline indium phosphide (InP) was performed in air by means of linearly polarized Ti : sapphire femtosecond pulses (800 nm, 130 fs, 10 Hz). As a result of the irradiation with a variable number of laser pulses per spot (N /spl les/ 5), several morphological changes (crater formation, rim formation, ripple structures, and cones) were observed. These effects were explored using force modulation microscopy (FMM), a technique based on scanning force microscopy, allowing the simultaneous imaging of both topography and local stiffness at a high lateral resolution. The first laser pulse induces the formation of a protruding rim (height < 20 nm, width /spl ap/ 300 nm) bordering the ablated crater. A Fourier analysis of the multipulse generated topographies reveals the formation of wavelength-sized periodic ripples (modulation depth < 100 nm) with an orientation perpendicular to that of the electric field vector of the laser radiation. Besides these morphological alterations, material modifications were also observed in the irradiated regions by means of the FMM technique. Within the ablated craters, local stiffness variations were found revealing an inhomogeneous material composition/structure as a consequence of the femtosecond pulse laser treatment.
Structure formation on the surface of indium phosphide irradiated by femtosecond laser pulses
(2005)
Laser-induced periodic surface structures (LIPSS; ripples) with different spatial characteristics have been observed after irradiation of single-crystalline indium phosphide (c-InP) with multiple linearly polarized femtosecond pulses (130 fs, 800 nm) in air. With an increasing number of pulses per spot, N, up to 100, a characteristic evolution of two different types of ripples has been observed, i.e., (i) the growth of a grating perpendicular to the polarization vector consisting of nearly wavelength-sized periodic lines and (ii), in a specific pulse number regime (N = 5-30), the additional formation of equally oriented ripples with a spatial period close to half of the laser wavelength. For pulse numbers higher than 50, the formation of micrometer-spaced grooves has been found, which are oriented perpendicular to the ripples. These topographical surface alterations are discussed in the frame of existing LIPSS theories.
Laser ablation of single-crystalline indium phosphide (InP) was performed in air by means of linearly polarized Ti:sapphire femtosecond-pulses (800 nm, 130 fs, 10 Hz). As a result of the first laser pulses, several morphological changes (crater formation, rim formation, ripple structures and cones) were observed. These effects were explored using force modulation microscopy (FMM), a technique based on scanning force microscopy (SFM), allowing the simultaneous imaging of both topography and local stiffness at a high lateral resolution. The first laser pulse induces the formation of a protruding rim (height <20 nm, width ~300 nm) bordering the ablated crater. A Fourier-analysis of the multi-pulse generated topographies reveals the formation of wavelength-sized periodic ripples (modulation depth <100 nm) with an orientation perpendicular to that of the electric field vector of the laser radiation. Besides these morphological alterations, also material modifications were observed in the irradiated regions by means of the FFM technique. Within the ablated craters, local stiffness variations were found revealing an inhomogeneous material composition/structure as a consequence of the femtosecond pulse laser treatment.
The chemical characteristics of two different types of laser-induced periodic surface structures (LIPSS), so-called high and low spatial frequency LIPSS (HSFL and LSFL), formed upon irradiation of titanium surfaces by multiple femtosecond laser pulses in air (30 fs, 790 nm, 1 kHz), are analyzed by various optical and electron beam based surface analytical techniques, including micro-Raman spectroscopy, energy dispersive X-ray analysis, X-ray photoelectron spectroscopy, and Auger electron spectroscopy. The latter method was employed in a high-resolution mode being capable of spatially resolving even the smallest HSFL structures featuring spatial periods below 100 nm. In combination with an ion sputtering technique, depths-resolved chemical information of superficial oxidation processes was obtained, revealing characteristic differences between the two different types of LIPSS. Our results indicate that a few tens of nanometer shallow HSFL are formed on top of a ∼150 nm thick graded superficial oxide layer without sharp interfaces, consisting of amorphous TiO2 and partially crystallized Ti2O3. The larger LSFL structures with periods close to the irradiation wavelength originate from the laser-interaction with metallic titanium. They are covered by a ∼200 nm thick amorphous oxide layer, which consists mainly of TiO2 (at the surface) and other titanium oxide species of lower oxidation states underneath.
Commercial grade-1 titanium samples (Ti, 99.6%) were treated using three alternative methods, (i) femtosecond laser processing, (ii) thermal heat treatment, and (iii) electrochemical anodization, respectively, resulting in the formation of differently conditioned superficial titanium oxide layers. The laser processing (i) was carried out by a Ti:sapphire laser (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz) in a regime of generating laser-induced periodic surface structures (LIPSS). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning setup for the processing of several square-millimeters large surface areas covered homogeneously by these nanostructures. The differently oxidized titanium surfaces were characterized by optical microscopy, micro Raman spectroscopy, variable angle spectroscopic ellipsometry, and instrumented indentation testing. The tribological performance was characterized in the regime of mixed friction by reciprocating sliding tests against a sphere of hardened steel in fully formulated engine oil as lubricant. The specific tribological performance of the differently treated surfaces is discussed with respect to possible physical and chemical mechanisms.
The irradiation of single-crystalline indium phosphide (c-InP) by Ti:sapphire femtosecond laser pulses (130 fs, 800 nm) in air is studied by means of in-situ time resolved reflectivity measurements [fs-time-resolved microscopy (100 fs-10 ns) and point probing analysis (ns - µs)] and by complementary ex-situ surface analytical methods (Micro Raman Spectroscopy, Scanning Force, and Optical Microscopy). The dynamics of melting, ablation, and optical breakdown as well as structural changes resulting from rapid solidification are investigated in detail. Different laser-induced surface morphologies are characterized and discussed on the basis of recent ablation and optical breakdown models.