Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (17)
- Beitrag zu einem Tagungsband (4)
- Vortrag (1)
Sprache
- Englisch (20)
- Deutsch (1)
- Französisch (1)
Schlagworte
- Mechanical properties (4)
- Carbon fibres (3)
- Interface (3)
- Ionic liquid (3)
- A. Carbon fibres (2)
- Adhesion (2)
- Contact angle (2)
- Elastic properties (2)
- Epoxy (2)
- Fractography (2)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (1)
For the concept of using structural materials such as carbon fibre reinforced plastics as
energy storage devices, new matrix polymers are required. These polymers must provide ionic
conductivity as well as adequate mechanical strength. In the EU-Project StorAGE this
requirements are fulfilled by adding ionic liquid to commercial polymers. The mechanical
properties of these mixtures materials were characterized by using a 3-point-bending device.
In addition, single fibre pull test were performed in order to get information on the interfacial
shear strength. Adding of ionic liquid has an impact on the mechanical performance of the
materials. A decrease of the flexural strength and modulus of less than 10% of the value of the
reference materials took part. The interfacial shear strength decreased to a value of around
one third compare to the reference material.
The quality of interfacial interaction is dictated by the surface chemistry of the carbon fibres and the composition of the matrix. The composition of poly(vinylidene fluoride) (PVDF) was modified by the addition of maleic anhydride grafted PVDF. The surface properties of the various matrix formulations were characterised by contact angle and electrokinetic measurements. Carbon fibres were modified by industrial electrochemical oxidation and oxidation in nitric acid, or the use of a traditional epoxy-sizing of industrially oxidised fibres. The surface composition, morphology and wetting behaviour of the carbon fibres was characterised. The interaction between modified PVDF and the carbon fibres was studied by direct contact angle measurements between PVDF melt on single carbon fibres and by single fibre pull-out tests. The best wetting and adhesion behaviour was achieved between PVDF containing 5 ppm grafted maleic anhydride (MAH) and epoxy-sized carbon fibres. The addition of MAH-grafted PVDF to the unmodified PVDF caused the apparent interfacial shear strength to increase by 184%. The apparent interfacial shear strength of this fibrematrix combination allowed for the utilisation of 100% of the yield tensile strength of PVDF.
Structural electrolytes were prepared using a fully formulated commercially available high performance epoxy resin (MTM57) and an ionic liquid based electrolyte: lithium bis(trifluoromethylsulfonyl)imide (LiTFSI) dissolved in 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide (EMIM-TFSI). Through a systematic study, the composition of the formulations was found to have a greater effect than the curing temperature on the morphology and properties of the resulting structural electrolytes. The presence of lithium salt is essential to form a structurally homogeneous electrolyte. Bicontinuous morphologies containing continuous (coarse) epoxy networks surrounded by connected spherical epoxy nodules were obtained with different length scales upon varying the lithium salt concentration. Increasing the LiTFSI concentration improved the miscibility of MTM57 with the electrolyte and decreased the characteristic length scale of the resulting bicontinuous microstructure. The properties of the structural electrolytes correlated with the morphology, showing increased Youngs modulus and decreased ionic conductivity with increasing lithium salt concentration. The miscibility of the epoxy system with the electrolyte was also improved by substitution of EMIM-TFSI with an equal weight of an aprotic organic solvent, propylene carbonate (PC); however, the window of PC concentrations which resulted in structural electrolytes with bicontinuous microstructures was very narrow; at PC concentrations above 1 wt %, gel-like polymers with no permanent mesoporosity were obtained.
Electrolyte systems that can carry mechanical load while allowing for high levels of ionic conductivity are an important prerequisite for structural power storage devices. Introduction of structural power storage into the variety of consumer products will allow saving in weight and volume. Moreover, using a supercapacitor/battery system in hybrid electric vehicles (HEV), the supercapacitor part will extend the battery lifetime by protecting it from the high peak currents. To successfully produce structural power storage requires the development
of multifunctional electrolytes where one has to simultaneously maximize mechanical properties and ionic conductivity.
Structural supercapacitor electrolytes based on bicontinuous ionic liquid-epoxy resin systems
(2013)
'Structural electrolytes' retain the desirable mechanical characteristics of structural (epoxy) resins whilst introducing sufficient ionic conductivity to operate as electrolytes in electrochemical devices. Here, a series of ionic liquid–epoxy resin composites were prepared to identify the optimum system microstructure required to achieve a high level of multifunctionality. The ionic conductivity, mechanical properties, thermal stability and morphology of the cured epoxy based structural electrolytes were studied as a function of phase composition for three fully formulated high performance structural epoxy systems. At only 30 wt% of structural resin and 70 wt% of ionic liquid based electrolyte, stiff monolithic plaques with thicknesses of 2–3 mm were obtained with a room temperature ionic conductivity of 0.8 mS cm-1 and a Young's modulus of 0.2 GPa. This promising performance can be attributed to a long characteristic length scale spinodal microstructure, suggesting routes to further optimisation in the future.
A novel low-pressure radio-frequency plasma treatment protocol was developed to achieve the effective through-thickness surface modification of large porous poly (d,l-lactide) (PDLLA) polymer scaffolds using air or water: ammonia plasma treatments. Polymer films were modified as controls. Scanning electron micrographs and maximum bubble point measurements demonstrated that the PDLLA foams have the high porosity, void fraction and interconnected pores required for use as tissue engineering scaffolds. The polymer surface of the virgin polymer does contain acidic functional groups but is hydrophobic.
Following exposure to air or water: ammonia plasma, an increased number of polar functional groups and improved wetting behaviour, i.e. hydrophilicity, of wet surfaces was detected. The number of polar surface functional groups increased (hence the decrease in water contact angles) with increasing exposure time to plasma. The change in surface composition and wettablility of wet polymer constructs was characterised by zeta potential and contact angle measurements. The hydrophobic recovery of the treated PDLLA polymer surfaces was also studied. Storage of the treated polymer constructs in ambient air caused an appreciable hydrophobic recovery, whereas in water only partial hydrophobic recovery occurred. However, in both cases the initial surface characteristics decay as function of time.
The feasibility of reinforcing conventional carbon fiber composites by grafting carbon nanotubes (CNTs) onto the fiber surface has been investigated. Carbon nanotubes were grown on carbon fibers using the chemical vapor deposition (CVD) method. Iron was selected as the catalyst and predeposited using the incipient wetness technique before the growth reaction. The morphology of the products was characterized using scanning electron microscopy (SEM), which showed evidence of a uniform coating of CNTs on the fiber surface. Contact angle measurements on individual fibers, before and after the CNT growth, demonstrated a change in wettability that can be linked to a change of the polarity of the modified surface. Model composites based on CNT-grafted carbon fibers/epoxy were fabricated in order to examine apparent interfacial shear strength (IFSS). A dramatic improvement in IFSS over carbon fiber/epoxy composites was observed in the single fiber pull-out tests, but no significant change was shown in the push-out tests. The different IFSS results were provisionally attributed to a change of failure mechanism between the two types of tests, supported by fractographic analysis.
The introduction of carbon nanotubes (CNTs) modifies bulk polymer properties, depending on intrinsic quality, dispersion, alignment, interfacial chemistry and mechanical properties of the nanofiller. These effects can be exploited to enhance the matrices of conventional microscale fibre-reinforced polymer composites, by using primary reinforcing fibres grafted with CNTs. This paper presents a methodology that combines atomic force microscopy, polarised Raman spectroscopy, and nanoindentation techniques, to study the distribution, alignment and orientation of CNTs in the vicinity of epoxy-embedded micrometre-scale silica fibres, as well as, the resulting local mechanical properties of the matrix. Raman maps of key features in the CNT spectra clearly show the CNT distribution and orientation, including a parted morphology associated with long grafted CNTs. The hardness and indentation modulus of the epoxy matrix were improved locally by 28% and 24%, respectively, due to the reinforcing effects of CNTs. Moreover, a slower stress relaxation was observed in the epoxy region containing CNTs, which may be due to restricted molecular mobility of the matrix. The proposed methodology is likely to be relevant to further studies of nanocomposites and hierarchical composites.
Triggered biodegradable composites made entirely from renewable resources are urgently sought after to improve material recyclability or be able to divert materials from waste streams. Many biobased polymers and natural fibers usually display poor interfacial adhesion when combined in a composite material. Here we propose a way to modify the surfaces of natural fibers by utilizing bacteria (Acetobacter xylinum) to deposit nanosized bacterial cellulose around natural fibers, which enhances their adhesion to renewable polymers. This paper describes the process of modifying large quantities of natural fibers with bacterial cellulose through their use as substrates for bacteria during fermentation. The modified fibers were characterized by scanning electron microscopy, single fiber tensile tests, X-ray photoelectron spectroscopy, and inverse gas chromatography to determine their surface and mechanical properties. The practical adhesion between the modified fibers and the renewable polymers cellulose acetate butyrate and poly(l-lactic acid) was quantified using the single fiber pullout test.
Poly (ether ether ketone) (PEEK) has a high continuous service temperature, excellent mechanical properties, and good solvent and abrasion resistance, which can be further improved through the addition of carbon nanotubes (CNTs). CNT-PEEK nanocomposites are promising matrices for continuous carbon fibre composites; powder processing can mitigate the high melt viscosities in these systems. In this study, model single fibre (hierarchical) composites were produced by embedding sized and desized carbon fibres in nanocomposite CNTPEEK powders followed by single fibre pull-out tests to assess interfacial characteristics. Carbon fibre-PEEK interfacial shear strength is typically 40–45 MPa. Increasing CNT loadings increased fibre-matrix interfacial shear strength linearly up to ~70 MPa at 5.0 wt%, which was attributed to the CNT-based mechanical modification of the PEEK matrix. Apparent interfacial shear strength was inversely correlated with the embedded fibre length irrespective of carbon fibre sizing or CNT loading, indicating brittle fracture of the fibre-matrix interface.
Pulled out carbon fibres were still coated with the matrix, which indicated strong adhesion at the interface in all samples, likely related to a transcrystalline region. Adhesion was, however, negatively affected by the presence of epoxy sizings. Frictional shear strength was independent of embedded fibre length and CNT content for all samples.